Resin powder for solid freeform fabrication, device for solid freeform fabrication object, and method of manufacturing solid freeform fabrication object
A resin powder for solid freeform fabrication includes a particle having a pillar-like form, wherein the ratio of the height of the particle to the diameter or the long side of the bottom of the particle is 0.5 to 2.0, the particle has a 50 percent cumulative volume particle diameter of from 5 to 200 μm, and the ratio (Mv/Mn) of the volume average particle diameter (Mv) to the number average particle diameter (Mn) of the particle is 2.00 or less.
1. A resin powder, comprising particles,
wherein the particle have a 50 percent cumulative volume particle diameter of from 5 to 200 μm,
a ratio (Mv/Mn) of a volume average particle diameter (Mv) to a number average particle diameter (Mn) of the particles is 2.00 or less, and
the resin powder has an average circularity of 083 to 0.98 in a range in which the resin powder has a particle diameter of from 0.5 to 200 μm, and
said resin powder comprises particles having a pillar-like form having no points at ends.
2. The resin powder according to claim 1 , which is suitable for solid freeform fabrication.
3. The resin powder according to claim 1 , satisfying at least one of the following relations (1) to (3):
Tmf 1> Tmf 2 and ( Tmf 1− Tmf 2)≥3 degrees C., (1):
where Tmf1 represents a melting starting temperature of an endothermic peak as the resin powder is heated to a temperature 30 degrees C. higher than a melting point of the resin powder at a temperature rising speed of 10 degrees C. per minute for a first time and Tmf2 represents a melting starting temperature of an endothermic peak as the resin powder is heated for the first time, cooled down to −30 degrees C. or lower at a temperature falling speed of 10 degrees C. per minute, and heated to the temperature 30 degrees C. higher than the melting point at a temperature rising speed of 10 degrees C. per minute for a second time, and both Tmf1 and Tmf2 are measured in differential scanning calorimetry measuring according to ISO 3146, wherein the melting starting temperature of the endothermic peak represents a temperature at a point −15 mW lower from a straight line parallel to X axis drawn from a site where quantity of heat becomes constant after endotherm at the melting point is finished to a lower temperature side,
Cd 1> Cd 2 and ( Cd 1− Cd 2)≥3 percent, (2):
where Cd1 represents a crystallinity obtained from an energy amount of the endothermic peak when the resin powder is heated to a temperature 30 degrees C. higher than the melting point of the resin powder at a temperature rising speed of 10 degrees C. per minute for a first time and Cd2 represents a crystallinity obtained from an energy amount of the endothermic peak as the resin powder is heated for the first time, cooled down to −30 degrees C. or lower at a temperature falling speed of 10 degrees C. per minute, and heated to the temperature 30 degrees C. higher than the melting point at a temperature rising speed of 10 degrees C. per minute for a second time, and both Cd1 and Cd2 are measured in differential scanning calorimetry measuring according to ISO 3146, and
C× 1> C× 2 and ( C× 1− C× 2)≥3 percent, (3):
where C×1 represents a crystallinity of the resin powder obtained by X-ray diffraction measuring and C×2 represents a crystallinity obtained by X-ray diffraction measuring as the resin powder is heated to the temperature 30 degrees C. higher than the melting point thereof at a temperature rising speed of 10 degrees C. per minute, cooled down to −30 degrees C. or lower at a temperature falling speed of 10 degrees C. per minute, and thereafter heated to the temperature 30 degrees C. higher than the melting point at a temperature rising speed of 10 degrees C. per minute in nitrogen atmosphere.
4. The resin powder according to claim 1 , and wherein a ratio of a height of the particle to a diameter or a long side of a bottom of the particle is 0.5 to 2.0.
5. The resin powder according to claim 1 , wherein the resin powder has a specific gravity of 0.8 g/mL or greater.
6. The resin powder according to claim 1 , wherein the resin powder has a specific gravity of 0.8 to 3.0 g/mL.
7. The resin powder according to claim 1 , wherein the resin powder has a melting point of 100 degrees C. or higher as measured according to ISO 3146.
8. The resin powder according to claim 1 , wherein the particle have a 50 percent cumulative volume particle diameter of from 20 to 70 μm.
9. The resin powder according to claim 1 , wherein the particle have a 50 percent cumulative volume particle diameter of from 20 to 50 μm.
10. The resin powder according to claim 1 , wherein Mv/Mn of the particles is 1.20 to 2.00.
11. The resin powder according to claim 1 , wherein particles having a pillar-like form accounts for 30 percent by mass or more of the resin powder.
12. The resin powder according to claim 1 , wherein said particles are solid particles.
13. The resin powder according to claim 1 , further comprising a toughening agent.
14. The resin powder according to claim 1 , further comprising a flame retardant.
15. The resin powder according to claim 1 , further comprising at least one member selected from the group consisting of polyolefin, polyamide, polyester, polyarylketone, polyphenylene sulfide, a liquid crystal polymer, polyacetal, polyimide, and a fluorochemical resin.
16. The resin powder according to claim 15 , wherein polyamide includes at least one member selected from the group including aromatic polyamide consisting of polyamide 410, polyamide 4T, polyamide 6, polyamide 66, polyamide MXD6, polyamide 610, polyamide 6T, polyamide 11, polyamide 12, polyamide 9T, polyamide 10T, and aramid.
17. The resin powder according to claim 15 , wherein polyester includes at least one member selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate, and polylactate.
18. The resin powder according to claim 15 , wherein polyaryl ketone includes at least one member selected from the group consisting of polyether ether ketone, polyether ketone, and polyether ketone ketone.
19. A method of manufacturing a solid freeform fabrication object, comprising:
forming a layer including a resin powder;
irradiating the layer with electromagnetic wave to melt the layer;
cooling down the layer;
curing the layer; and
repeating the forming, the irradiating, the cooling down, and the curing the layer,
wherein the resin powder comprises particles:
wherein the particles have a 50 percent cumulative volume particle diameter of from 5 to 200 μm,
a ratio (Mv/Mn) of a volume average particle diameter (Mv) to a number average particle diameter (Mn) of the particles is 2.00 or less,
the resin powder has an average circularity of 083 to 0.98 in a range in which the resin powder has a particle diameter of from 0.5 to 200 μm, and
said resin powder comprises particles having a pillar-like form having no points at ends.