Gallium oxide-based semiconductor and production method thereof
To provide a gallium oxide-based semiconductor with its bandgap being sufficiently reduced, and a manufacturing method thereof. A gallium oxide-based semiconductor containing a mixed crystal having a composition represented by (Ga (1-x) Fe x ) 2y O 3 , wherein 0.10≤x≤0.40 and 0.85≤y≤1.2, wherein the mixed crystal has a beta-gallia structure, is provided. Also, a method for manufacturing the gallium oxide-based semiconductor, including depositing a mixed crystal having a composition represented by (Ga (1-x) Fe x ) 2y O 3 , wherein 0.10≤x≤0.40 and 0.85≤y≤1.2 on a substrate surface by a pulsed laser deposition method, wherein denoting the temperature of the substrate as T° C., x and T satisfy the relationship represented by 500x+800≤T<1,000, is provided.
1. A method for producing the gallium oxide-based semiconductor comprising a mixed crystal having a composition represented by (Ga (1-x) Fe x ) 2y O 3 , wherein 0.10≤x≤0.30 and 0.8≤y≤1.2, and wherein the mixed crystal has a beta-gallia structure, the method comprising:
depositing a mixed crystal having a composition represented by (Ga (1-x) Fe x ) 2y O 3 , wherein 0.10≤x≤0.30 and 0.8≤y≤1.2, on a substrate surface by a pulsed laser deposition method, and
wherein denoting a temperature of the substrate as T in degrees C., x and T satisfy a relationship represented by 500x+800≤T≤950.
2. The method for producing the gallium oxide-based semiconductor according to claim 1 , wherein the laser used in the pulsed laser deposition method is a pulsed ultraviolet laser.
3. The method for producing the gallium oxide-based semiconductor according to claim 1 , wherein y is 1.0.