Method of preparing diisocyanate composition and optical lens
In the embodiments, an aqueous hydrochloric acid solution instead of hydrogen chloride gas and solid triphosgene instead of phosgene gas may be used in the process of preparing a diisocyanate from a diamine through a diamine hydrochloride. In addition, the embodiments provide processes for preparing a diisocyanate composition and an optical lens of higher quality by controlling the water content in the diamine hydrochloride composition for preparing a diisocyanate within a specific range.
1. A process for preparing a diisocyanate composition, which comprises:
(1) reacting a diamine composition with an aqueous hydrochloric acid solution to obtain a diamine hydrochloride composition;
(2) adding a first organic solvent to obtain the diamine hydrochloride composition in a solid phase; and
(3) reacting the diamine hydrochloride composition obtained in step 2 with triphosgene to obtain a diisocyanate composition,
wherein the diisocyanate composition has a b* value according to the CIE color coordinate of 0.1 to 2.0.
2. The process for preparing a diisocyanate composition of claim 1 , wherein the content of Fe ions in the aqueous hydrochloric acid solution is 0.5 ppm or less.
3. The process for preparing a diisocyanate composition of claim 1 , wherein the diamine hydrochloride composition has a b* value according to the CIE color coordinate of 1.5 or less when dissolved in water at a concentration of 8% by weight.
4. The process for preparing a diisocyanate composition of claim 3 , wherein the b* value according to the CIE color coordinate of the diamine hydrochloride composition is adjusted by washing it with a solvent having a polarity of 5.7 or less.
5. The process for preparing a diisocyanate composition of claim 1 , which further comprises measuring the b* value according to the CIE color coordinate of the diamine hydrochloride composition.
6. The process for preparing a diisocyanate composition of claim 1 , wherein the diisocyanate composition is obtained by distillation after the reaction of the diamine hydrochloride composition and triphosgene, and the distillation comprises distillation of diisocyanate at a temperature of 100° C. to 130° C. and a pressure of 2.0 torr or less.
7. A process for preparing an optical lens, which comprises:
(1) reacting a diamine composition with an aqueous hydrochloric acid solution to obtain a diamine hydrochloride composition;
(2) adding a first organic solvent to obtain the diamine hydrochloride composition in a solid phase;
(3) reacting the diamine hydrochloride composition obtained in step 2 with triphosgene to obtain a diisocyanate composition; and
(4) mixing the diisocyanate composition with a thiol or an episulfide and polymerizing and curing the resultant in a mold,
wherein the diisocyanate composition has a b* value according to the CIE color coordinate of 0.1 to 2.0.
8. The process for preparing an optical lens of claim 7 , wherein the optical lens has a transmittance of 90% or more and a yellow index (Y.I.) of 20 or less.