Compositions and methods for creating nanoscale surface geometries on metals of an implantable device
Compositions and methods for etching a nanoscale geometry on a metal or metal alloy surface are disclosed. Such surfaces, when included on an implantable medical device, enhance healing after surgery. When included on a bone contacting medical implant, the nanoscale geometry may enhance osseointegration. When included on a tissue contacting device, the nanoscale geometry may enhance endothelial cell attachment, proliferation, and restoration of a healthy endothelial surface.
1. A composition for etching a nanoscale geometry into a surface of a body implantable device formed of a metal or metal alloy, the composition comprising:
1.2N-3.0N hydrochloric acid (HCl), 2.0N-4.0N nitric acid (HNO 3 ), 0.1N-0.3N phosphoric acid (H 3 PO 4 ), 0.1N-0.3N hydrofluoric acid (HF), and
component metals of the body implantable device, wherein the metal or metal alloy of the body implantable device comprises stainless steel, and the composition comprises 3.75 g/l-90 g/l of each of chromium (Cr), molybdenum (Mo), and nickel (Ni), and up to 225 g/l iron (Fe),
wherein the body implantable device is a bone-contacting device and the nanoscale geometry enhances osseointegration when the bone-contacting device is implanted adjacent living bone, or
wherein the body implantable device is a tissue-contacting device and the nanoscale geometry enhances endothelial attachment and proliferation when the tissue-contacting device is implanted adjacent tissue.
2. The composition of claim 1 , comprising the component metals Cr, Mo, and Ni provided in a relative ratio that corresponds to a ratio of the metals in the stainless steel.
3. A composition for etching a nanoscale geometry into a surface of a body implantable device formed of a metal or metal alloy, the composition comprising:
0.5N-3.5N hydrofluoric acid (HF) and 0.1N-3.0N nitric acid (HNO 3 ), and
component metals of the body implantable device, device, wherein the metal or metal alloy of the body implantable device comprises a nickel-titanium alloy, and the composition comprises: 3.75 g/l-90 g/l of each of nickel (Ni) and titanium (Ti),
wherein the body implantable device is a bone-contacting device and the nanoscale geometry enhances osseointegration when the bone-contacting device is implanted adjacent living bone, or
wherein the body implantable device is a tissue-contacting device and the nanoscale geometry enhances endothelial attachment and proliferation when the tissue-contacting device is implanted adjacent tissue.
4. The composition of claim 3 , wherein the nickel (Ni) and titanium (Ti) are provided in a relative ratio that corresponds to a ratio of the metals in the nickel-titanium alloy.
5. The composition of claim 3 , wherein the composition further comprises: up to 225 g/l iron (Fe).
6. A composition for etching a nanoscale geometry into a surface of a body implantable device formed of a metal or metal alloy, the composition comprising:
0.5N-3.5N hydrofluoric acid (HF) and 0.1N-3.0N nitric acid (HNO 3 ), and
component metals of the body implantable device, wherein the metal or metal alloy of the body implantable device comprises a nickel-chromium-molybdenum alloy, and the composition comprises: 3.75 g/l-90 g/l of each of chromium (Cr), and molybdenum (Mo), and up to 225 g/l iron (Fe),
wherein the body implantable device is a bone-contacting device and the nanoscale geometry enhances osseointegration when the bone-contacting device is implanted adjacent living bone, or
wherein the body implantable device is a tissue-contacting device and the nanoscale geometry enhances endothelial attachment and proliferation when the tissue-contacting device is implanted adjacent tissue.
7. The composition of claim 6 , wherein the nickel (Ni), chromium (Cr), and molybdenum (Mo) are provided in a relative ratio that corresponds to a ratio of the metals in the nickel-chromium-molybdenum alloy.
8. A composition for etching a nanoscale geometry into a surface of a body implantable device formed of zirconia, the composition consisting of:
0.5N-3.5N hydrofluoric acid (HF) and 0.1N-3.0N nitric acid (HNO 3 ), and
soluble zirconia (ZnO 2 ) and up to 225 g/l iron (Fe),
wherein the body implantable device is a bone-contacting device and the nanoscale geometry enhances osseointegration when the bone-contacting device is implanted adjacent living bone, or
wherein the body implantable device is a tissue-contacting device and the nanoscale geometry enhances endothelial attachment and proliferation when the tissue-contacting device is implanted adjacent tissue.
9. The composition of claim 8 , comprising 3.75 g/l-90 g/l of the soluble zirconia (ZnO 2 ).
10. A method for etching a nanoscale surface geometry on at least a portion of a body implantable device, the method comprising:
preparing a chemical etching composition according to claim 1 ; and
contacting at least a portion of a surface of the implantable device with the chemical etching composition at a reaction temperature of from about 20° C. to about 100° C.,
wherein the surface of the body implantable device comprises stainless steel.
11. The method of claim 10 , further comprising, before the step of contacting with the chemical etching composition:
activating the surface to be etched with an activation solution comprising a 10% to 100% (v/v) aqueous solution of a mineral acid.
12. The method of claim 11 , wherein the activating step is carried out within 120 seconds before the contacting.
13. The method of claim 10 , wherein the body implantable device is an implantable bone-contacting device, and the nanoscale surface geometry enhances osseointegration when the bone-contacting device is implanted adjacent living bone, or wherein the body implantable device is an implantable tissue-contacting device and the nanoscale surface geometry enhances endothelial attachment and proliferation when the tissue-contacting device is implanted adjacent tissue.
14. A method for etching a nanoscale surface geometry on at least a portion of a body implantable device, the method comprising:
preparing a chemical etching composition according to claim 3 ; and
contacting at least a portion of a surface of the implantable device with the chemical etching composition at a reaction temperature of from about 20° C. to about 100° C.,
wherein the surface of the body implantable device comprises a nickel-titanium alloy.
15. The method of claim 14 , further comprising, before the step of contacting with the chemical etching composition:
activating the surface to be etched with an activation solution comprising a 10% to 100% (v/v) aqueous solution of a mineral acid.
16. A method for etching a nanoscale surface geometry on at least a portion of a body implantable device, the method comprising:
preparing a chemical etching composition according to claim 6 ; and
contacting at least a portion of a surface of the implantable device with the chemical etching composition at a reaction temperature of from about 20° C. to about 100° C.,
wherein the surface of the body implantable device comprises a nickel-chromium-molybdenum alloy.
17. The method of claim 16 , further comprising, before the step of contacting with the chemical etching composition:
activating the surface to be etched with an activation solution comprising a 10% to 100% (v/v) aqueous solution of a mineral acid.
18. A method for etching a nanoscale surface geometry on at least a portion of a body implantable device, the method comprising:
preparing a chemical etching composition according to claim 9 ; and
contacting at least a portion of a surface of the implantable device with the chemical etching composition at a reaction temperature of from about 20° C. to about 100° C.,
wherein the surface of the body implantable device comprises a nickel-chromium-molybdenum alloy.
19. The method of claim 16 , further comprising, before the step of contacting with the chemical etching composition:
activating the surface to be etched with an activation solution comprising a 10% to 100% (v/v) aqueous solution of a mineral acid.