Hot stamped steel
A hot stamped steel includes a base material, a plated layer that is formed on a surface of the base material, and an oxide film that is formed on a surface of the plated layer; chemical composition of the plated layer contains 20.00 to 45.00 mass % of Al, 10.00 to 45.00 mass % of Fe, 4.50 to 15.00 mass % of Mg, 0.10 to 3.00 mass % of Si, 0.05 to 3.00 mass % of Ca, 0 to 0.50 mass % of Sb, 0 to 0.50 mass % of Pb, 0 to 1.00 mass % of Cu, 0 to 1.00 mass % of Sn, 0 to 1.00 mass % of Ti, 0 to 0.50 mass % of Sr, 0 to 1.00 mass % of Cr, 0 to 1.00 mass % of Ni, and 0 to 1.00 mass % of Mn with a remainder of Zn and impurities; and chemical composition of the oxide film contains 20.0 to 55.0 at % of Mg, 0.5 to 15.0 at % of Ca, 0 to 15.0 at % of Zn, and 0 at % or more and less than 10.0 at % of Al with a remainder of O and a total of 5.0 at % or less of impurities, and the adhesion amount of the oxide film per one surface is in a range of 0.01 to 10 g/m 2 .
1. A hot stamped steel comprising:
a base material that is formed of steel;
a plated layer that is formed on a surface of the base material; and
an oxide film that is formed on a surface of the plated layer,
wherein a chemical composition of the plated layer contains 20.00 to 45.00 mass % of Al, 10.00 to 45.00 mass % of Fe, 4.50 to 15.00 mass % of Mg, 0.10 to 3.00 mass % of Si, 0.05 to 3.00 mass % of Ca, 0 to 0.50 mass % of Sb, 0 to 0.50 mass % of Pb, 0 to 1.00 mass % of Cu, 0 to 1.00 mass % of Sn, 0 to 1.00 mass % of Ti, 0 to 0.50 mass % of Sr, 0 to 1.00 mass % of Cr, 0 to 1.00 mass % of Ni, and 0 to 1.00 mass % of Mn with a remainder of Zn and impurities,
a chemical composition of the oxide film contains 20.0 to 55.0 at % of Mg, 0.5 to 15.0 at % of Ca, 0 to 15.0 at % of Zn, and 0 at % or more and less than 10.0 at % of Al with a remainder of O and a total of 5.0 at % or less of impurities, and
an adhesion amount of the oxide film per surface area of the plated layer is in a range of 0.01 to 10 g/m 2 .
2. The hot stamped steel according to claim 1 ,
wherein the chemical composition of the plated layer contains one or both of 25.00 to 35.00 mass % of Al and 6.00 to 10.00 mass % of Mg.
3. The hot stamped steel according to claim 1 ,
wherein the chemical composition of the oxide film contains 35.0 to 55.0 at % of Mg.
4. The hot stamped steel according to claim 2 ,
wherein the chemical composition of the oxide film contains 35.0 to 55.0 at % of Mg.