Silicide films through selective deposition
Methods for forming silicide films are disclosed. Methods of selectively depositing metal-containing films on silicon surfaces which are further processed to form silicide films are disclosed. Specific embodiments of the disclosure relate to the formation of silicide films on FinFET structures without the formation of a metal layer on the dielectric.
1. A selective deposition method comprising:
exposing a substrate comprising a first semiconductor surface and a second dielectric surface to a blocking compound to selectively form a blocking layer on the second dielectric surface, the blocking compound comprising a blocking agent of a general formula R 3 Si—X, where each R is independently C1-C4 alkyl and X is a leaving group;
selectively depositing a metal layer on the first surface over the second surface;
optionally depositing a germanium-containing layer on the first surface;
optionally depositing a silicon-containing layer on the first surface; and
annealing the substrate to form a modified first surface.
2. The method of claim 1 , wherein the blocking agent consists essentially of a compound of Formula I.
3. The method of claim 1 , wherein the metal layer comprises one or more of Ti, Zr, Hf or Ta.
4. The method of claim 3 , wherein the metal layer comprises a TiGe alloy.
5. The method of claim 1 , wherein selectively depositing a metal layer on the first surface over the second surface comprises exposing the substrate to a metal precursor.
6. The method of claim 4 , wherein the substrate is exposed to the metal precursor and a reagent.
7. The method of claim 6 , wherein the reagent comprises one or more of hydrogen, ammonia, hydrazine, hydrazine derivatives, silanes, halosilanes, polysilanes, boranes, or haloboranes.
8. The method of claim 7 , wherein the metal film comprises a pure metal film, a metal nitride, a metal silicide or a metal boride.
9. The method of claim 6 , wherein the reagent comprises one or more of oxygen, ozone, or water.
10. The method of claim 9 , wherein the metal film comprises a pure metal film or a metal oxide.
11. The method of claim 6 , wherein a plasma of the reagent is exposed to the substrate.
12. The method of claim 1 , wherein a germanium-containing layer is deposited on the first surface.
13. The method of claim 12 , wherein the germanium-containing layer is deposited before the metal layer.
14. The method of claim 12 , wherein the modified first surface comprises a germanide.
15. The method of claim 1 , wherein a silicon-containing layer is deposited on the first surface.
16. The method of claim 15 , wherein the silicon-containing layer is deposited before the metal layer.
17. The method of claim 15 , wherein the modified first surface comprises a silicide.
18. The method of claim 1 , wherein the substrate is annealed at a temperature in a range of about 500° C. to about 1200° C.