Wax as a melt flow modifier and processing aid for polymers
An improved method forms and employs a wax to modify throughputs and melt flow in polymers. The method includes: (a) selecting a solid polymeric material, (b) heating the solid polymeric material in an extruder to produce a molten polymeric material, (c) filtering the molten polymeric material, (d) placing the molten polymeric material through a chemical depolymerization process in a reactor to produce a depolymerized polymeric material, and (e) adding the depolymerized material to a pre-wax mixture to produce a modified polymer.
1. A modified polymer wherein said modified polymer is produced by mixing an amount of a wax with a polymer, wherein said modified polymer has an increased melt flow index when compared to said polymer,
wherein said wax is formed by catalytically depolymerizing a polyethylene, and wherein said polymer is polyethylene or polypropylene.
2. The modified polymer of claim 1 wherein at least an amount of said polyethylene is from a recycled post-consumer or post-industrial feed.
3. The modified polymer of claim 1 wherein said wax has a melting point between 106° C. and 135° C.
4. The modified polymer of claim 1 wherein said wax has a melting point between 86° C. and 105° C.
5. The modified polymer of claim 1 wherein said wax has a melting point between 65° C. and 85° C.
6. The modified polymer of claim 1 wherein said wax has a melting point between 40° C. and 65° C.
7. The modified polymer of claim 2 wherein said amount of said polyethylene includes inorganics.
8. The modified polymer of claim 1 wherein said polymer is polyethylene.
9. The modified polymer of claim 1 wherein said polyethylene is HDPE.
10. The modified polymer of claim 1 wherein said amount of said wax is between 1-8% of said modified polymer by weight.
11. The modified polymer of claim 1 wherein said amount of said wax is between 1-5% of said modified polymer by weight.
12. The modified polymer of claim 1 wherein said amount of said wax is between 2-4% of said modified polymer by weight.
13. A modified polymer wherein said modified polymer is produced by mixing an amount of a wax with a polymer, wherein said modified polymer has an increased melt flow index when compared to said polymer,
wherein said wax is formed by catalytically depolymerizing a polypropylene, and wherein said polymer is polyethylene or polypropylene.
14. The modified polymer of claim 13 wherein at least an amount of said polypropylene is from a recycled post-consumer or post-industrial feed.
15. The modified polymer of claim 13 wherein said amount of said polypropylene includes inorganics.
16. The modified polymer of claim 13 wherein said polymer is polypropylene.
17. The modified polymer of claim 13 wherein said amount of said wax is between 1-8% of said modified polymer by weight.
18. The modified polymer of claim 13 wherein said amount of said wax is between 1-5% of said modified polymer by weight.
19. The modified polymer of claim 13 wherein said amount of said wax is between 2-4% of said modified polymer by weight.