Method and device for additive manufacturing by agglomeration of a granular material
A method for manufacturing a structure from a granular material, called sand, in particular a mold. A layer of sand is deposited. The layer of sand is selectively agglomerated by spraying, using a spray nozzle, an inorganic binder having an M2SiO3 type (meta)silicate dissolved in a solvent. Prior to the spraying, the inorganic binder is heated to a temperature to confer on it a viscosity less than 0.2 Pa·s. A device for implementing the method is provided.
1. A method for manufacturing a structure from a granular material, the manufacturing comprising an additive manufacturing phase, the method comprising: depositing a layer of sand, the granular material being sand; selectively agglomerating the layer of sand by spraying, by using a spray nozzle, an inorganic binder comprising a M 2 SiO 3 type (meta)silicate dissolved in a solvent, where M is selected from Na, K and Li individually or in combination, wherein the inorganic binder is heated prior to its spraying to a temperature between 30° C. and 100° C. so as to confer a viscosity less than 0.2 Pa·s to the inorganic binder; and wherein the inorganic binder comprises additives in form of nanoparticles in a colloidal suspension in the organic binder to modify a mechanical or thermal property of the structure.
2. The m of claim 1 , wherein the structure is a mold.
3. The method of claim 1 , wherein a quantity of the (meta)silicate in the inorganic binder is 5% and 90%.
4. The method of claim 3 , wherein the quantity of the (meta)silicate in the inorganic binder is between 10% and 40%.
5. The method of claim 1 , wherein M is Na and the proportion of the sodium silicate in the inorganic binder is equal to 30%.
6. The method of claim 1 , wherein the solvent is water.
7. The method of claim 1 , further comprising drying a zone affected by the spraying of the inorganic binder after selectively agglomerating the layer of sand.
8. The method of claim 7 , wherein the drying is performed by heating.
9. The method of claim 7 , wherein the drying is performed by putting the zone affected by the spraying of the inorganic binder in contact with CO 2 .
10. The method of claim 1 , wherein the layer of sand is deposited by a hopper moving at a constant speed; and further comprising depositing a layer of second granular material of a characteristic different from the layer of sand.
11. The method of claim 1 , further comprising extracting an agglomerated structure from a sand bed, comprising an injection of a gas under the sand bed in order to fluidify a non-agglomerated part of the sand bed after selectively agglomerating the layer of the sand.