System and method for repairing high-temperature gas turbine components
A method of forming a component includes mixing a powdered base material and a binder to define a mixture, forming the mixture into a desired shape without melting the base material, removing the binder from the desired shape to define a skeleton, the volume of the skeleton being between 80 percent and 95 percent base material, and infiltrating the skeleton with a melting point depressant material to define a finished component, the finished component having less than one percent porosity by volume.
1. A method of forming a pre-sintered preform, the method comprising:
mixing a powdered base material and a binder to define a mixture;
forming the mixture into a shape without melting the base material;
removing the binder from the shape to define a skeleton, the skeleton having a volume that contains between 80 percent and 95 percent base material; and
infiltrating the skeleton with a melting point depressant material to define a finished pre-sintered preform, the finished pre-sintered preform having less than one percent porosity by volume,
wherein at least one of the mixture or the melting point depressant material includes at least one of powdered rhenium or ruthenium and the combined percentage of rhenium and ruthenium is 6% or less of the finished pre-sintered preform.
2. The method of claim 1 , wherein the shape is heated to burn out the binder without melting the base material.
3. The method of claim 1 , wherein the melting point depressant consists essentially of Ni, Cr, and at least one of Ti, Zr, and Hf.
4. The method of claim 1 , wherein the melting point depressant consists essentially of, by weight, 6.5% Cr, 11% Zr, 7.5% Ti, and the remainder Ni.
5. The method of claim 1 , wherein the melting point depressant consists essentially of, by weight, 5.0% Cr, 10% Hf, 10% Zr, and the remainder Ni.
6. The method of claim 1 , wherein the melting point depressant consists essentially of, by weight, 17% Cr, 22% Ti, and the remainder Ni.
7. The method of claim 1 , wherein the finished pre-sintered preform is a portion of a leading edge of a turbine vane.
8. The method of claim 1 , wherein the melting point depressant contains a quantity of Ti selected such that the pre-sintered preform has between 4% and 6% titanium, by weight.
9. The method of claim 1 , wherein the shape is selected to replace a damaged portion of a turbine blade leading edge.
10. The method of claim 1 , wherein the shape is selected to replace a damaged portion of a turbine blade tip.
11. The method of claim 1 , wherein the rhenium or ruthenium is uniformly distributed in the finished pre-sintered preform.
12. The method of claim 11 , wherein the rhenium or ruthenium powder has a diameter that is at least 50% or smaller than a diameter of the powdered base material or a melting point depressant powder.
13. The method of claim 1 , wherein the pre-sintered preform has an oxidation and rupture resistance equal to or greater than a material of a removed portion of a repairable gas turbine component replaced by the pre-sintered preform.