Nitridation-induced in situ coupling of Ni-CO
There is disclosed a process of producing a hybrid super-capacitor (HSC) electrode, the process comprising performing nitridation-induced in situ coupling of Ni—Co 4 N nanoparticles in an N-doped carbon matrix, wherein the resultant hybrid super-capacitor (HSC) electrode is a Ni—Co 4 N@NC electrode. The resultant hybrid super-capacitor (HSC) electrode is a self-supported metal nitride coordinated with N-doped carbon, wherein the nitridation-induced in situ coupling is performed via a facile pyrolysis of layered Ni—Co hydroxide decorated on polyaniline (PANI) nanotubes on the basis of a carbon cloth (CC). Also disclosed is a hybrid supercapacitor cell assembled by employing Ni—Co 4 N-2@NC as a positive electrode and AC as a negative electrode with a PVA (poly vinyl alcohol)/KOH as a gel electrolyte.
1. A process of producing a hybrid super-capacitor (HSC) electrode, the process comprising:
performing nitridation-induced in situ coupling of Ni—Co 4 N nanoparticles in an N-doped carbon matrix, wherein the resultant hybrid super-capacitor (HSC) electrode is a Ni—Co 4 N@NC electrode,
wherein the nitridation-induced in situ coupling is performed via a facile pyrolysis of layered Ni—Co hydroxide decorated on polyaniline (PANI) nanotubes on the basis of a carbon cloth (CC).
2. The process of claim 1 , wherein the resultant hybrid super-capacitor (HSC) electrode is a self-supported metal nitride coordinated with N-doped carbon.
3. The process of claim 1 , wherein nitrogenous gases released from the facile pyrolysis of polyaniline (PANI) nanotubes are used for the in-situ conversion of NiCo @PANI to Ni—Co 4 N@NC.
4. The process of claim 1 , wherein the produced hybrid super-capacitor (HSC) electrode is constructed with Ni—Co 4 N@NC and activated carbon (AC) as cathode and anode of the produced hybrid super-capacitor (HSC) electrode.
5. The process of claim 4 , wherein the cathode and anode demonstrate a specific energy of 57.2 Wh kg −1 at a specific power of 843.8 W kg −1 and capacity retention of 89.7% after 15,000 cycles.
6. The process of claim 1 , wherein synthesis of polyaniline (PANI) on carbon cloth (PANI/CC) is conducted through steps comprising:
using ammonium persulfate to polymerize aniline to form PANI on carbon cloth (CC);
immersing clean CC in a 50 mL of mixture solution of 1 M H 2 SO 4 and 0.55 mL aniline placed in an ice bath under magnetic stirring;
adding 50 mL of 1 M H 2 SO 4 containing 0.545 g ammonium persulfate dropwise to the mixture solution forming a reaction mixture; and
placing the reaction mixture in the ice bath.
7. The process of claim 6 , wherein the reaction mixture is placed in the ice bath for 5 hours, and a subsequently obtained green color PANI deposited CC is washed with de-ionized (DI) water and acetone and dried overnight at 60° prior to further use.
8. The process of claim 1 , wherein preparation of Ni—Co 4 N@NC nanoparticles arrays on CC comprises the steps of:
growing PANI nanowires on a carbon cloth (CC) substrate through polymerization of aniline in a chilled environment resulting in PANI coated CC;
growing NiCo precursor nanosheets on the PANI coated CC under a hydrothermal process, and calcinating the PANI coated CC in a tubular furnace under Ar/NH3 environment at 700° C.
9. The process of claim 8 , wherein formation of metal nitrides from the NiCo precursor nanosheets takes place inside the tubular furnace.
10. The process of claim 8 , wherein an SEM image of the prepared Ni—Co 4 N@NC nanoparticles arrays on CC reveals that the NiCo precursor nanosheets are assembled into uniformly oriented free-standing 1D nanorods and are perpendicularly anchored on the CC substrate, forming hierarchical arrays.