Flexible optical-fiber ribbon

1. An optical-fiber ribbon, comprising:

(i) a plurality of respectively adjacent optical fibers extending in a longitudinal direction and arranged in parallel to form an optical-fiber assembly, wherein each optical fiber includes, from its center to its periphery, a glass core, a glass cladding, a primary coating, and an outermost secondary coating comprising a cured first curable resin; and

(ii) a plurality of successive elongated rectilinear beads comprising a cured second curable resin arranged along the optical-fiber assembly, wherein the beads are configured to form elongated bonds between adjacent optical fibers in the optical-fiber assembly;

wherein, as measured by a T-peel test, the force required to separate one optical fiber from the optical-fiber ribbon is between 0.01 N and 0.2 N; and

wherein, along at least a portion of the optical-fiber ribbon that includes one or more elongated rectilinear beads, each bead is configured so that when removing an optical fiber during optical-fiber breakout the corresponding point of failure occurs (i) within the bead without damaging the optical fiber's primary coating and/or the optical fiber's outermost secondary coating, and/or (ii) at the interface between the bead and the outermost secondary coating without damaging the optical fiber's primary coating and/or the optical fiber's outermost secondary coating.

2. The optical-fiber ribbon according to claim 1 , wherein, as measured by a T-peel test, the force required to separate one 250-micron optical fiber from the optical-fiber ribbon is between 0.02 N and 0.15 N.

3. The optical-fiber ribbon according to claim 1 , wherein, as measured by a T-peel test, the force required to separate one 200-micron optical fiber from the optical-fiber ribbon is between 0.015 N and 0.1 N.

4. The optical-fiber ribbon according to claim 1 , wherein, as measured by a T-peel test, the energy to break the bonds between each adjacent optical fiber's outermost secondary coating comprising the cured first curable resin and the corresponding bead comprising the cured second curable resin is 0.4 millijoule or less.

5. The optical-fiber ribbon according to claim 1 , wherein, after 30 days of immersion in 60° C. water, the optical-fiber ribbon maintains at least 70 percent of its original bonding strength as measured by a T-peel test.

6. The optical-fiber ribbon according to claim 1 , wherein the cured second curable resin forming the beads has elongation at break of at least 150 percent as measured via ASTM D638-14.

7. The optical-fiber ribbon according to claim 1 , wherein the cured second curable resin forming the beads has Young's modulus of between 1 MPa and 50 MPa as measured via ASTM D638-14.

8. The optical-fiber ribbon according to claim 1 , wherein each elongated bond between adjacent optical fibers in the optical-fiber assembly chemically couples each adjacent optical fiber's cured first curable resin and the corresponding bead's cured second curable resin.

9. The optical-fiber ribbon according to claim 1 , wherein:

a first elongated rectilinear bead comprising a cured second curable resin is configured to form a first elongated bond connecting a first pair of adjacent optical fibers; and

a second elongated rectilinear bead comprising a cured second curable resin is configured to form a second elongated bond connecting a second pair of adjacent optical fibers, wherein at least one optical fiber of the second pair of adjacent optical fibers differs from the optical fibers of the first pair of adjacent optical fibers.

10. An optical-fiber-cable unit comprising one or more optical-fiber ribbons according to claim 1 .

11. An optical-fiber ribbon, comprising:

(i) a plurality of respectively adjacent optical fibers extending in a longitudinal direction and arranged in parallel to form an optical-fiber assembly, wherein each optical fiber includes, from its center to its periphery, a glass core, a glass cladding, a primary coating, a secondary coating, and an outermost ink layer comprising a cured first curable resin; and

(ii) a plurality of successive elongated rectilinear beads comprising a cured second curable resin arranged along the optical-fiber assembly, wherein the beads are configured to form elongated bonds between adjacent optical fibers in the optical-fiber assembly;

wherein, as measured by a T-peel test, the force required to separate one optical fiber from the optical-fiber ribbon is between 0.01 N and 0.2 N; and

wherein, along at least a portion of the optical-fiber ribbon that includes one or more elongated rectilinear beads, each bead is configured so that when removing an optical fiber during optical-fiber breakout the corresponding point of failure occurs (i) within the bead without damaging the optical fiber's primary coating, the optical fiber's secondary coating, and/or the optical fiber's outermost ink layer, and/or (ii) at the interface between the bead and the outermost ink layer without damaging the optical fiber's primary coating, the optical fiber's secondary coating, and/or the optical fiber's outermost ink layer.

12. The optical-fiber ribbon according to claim 11 , wherein, as measured by a T-peel test, the force required to separate one 250-micron optical fiber from the optical-fiber ribbon is between 0.02 N and 0.15 N.

13. The optical-fiber ribbon according to claim 11 , wherein, as measured by a T-peel test, the force required to separate one 200-micron optical fiber from the optical-fiber ribbon is between 0.015 N and 0.1 N.

14. The optical-fiber ribbon according to claim 11 , wherein, as measured by a T-peel test, the energy to break the bonds between each adjacent optical fiber's outermost ink layer comprising the cured first curable resin and the corresponding bead comprising the cured second curable resin is 0.4 millijoule or less.

15. The optical-fiber ribbon according to claim 11 , wherein, after 30 days of immersion in 60° C. water, the optical-fiber ribbon maintains at least 70 percent of its original bonding strength as measured by a T-peel test.

16. The optical-fiber ribbon according to claim 11 , wherein the cured second curable resin forming the beads has elongation at break of at least 150 percent as measured via ASTM D638-14.

17. The optical-fiber ribbon according to claim 11 , wherein the cured second curable resin forming the beads has Young's modulus of between 1 MPa and 50 MPa as measured via ASTM D638-14.

18. The optical-fiber ribbon according to claim 11 , wherein each elongated bond between adjacent optical fibers in the optical-fiber assembly chemically couples each adjacent optical fiber's cured first curable resin and the corresponding bead's cured second curable resin.

19. The optical-fiber ribbon according to claim 11 , wherein:

a first elongated rectilinear bead comprising a cured second curable resin is configured to form a first elongated bond connecting a first pair of adjacent optical fibers; and

a second elongated rectilinear bead comprising a cured second curable resin is configured to form a second elongated bond connecting a second pair of adjacent optical fibers, wherein at least one optical fiber of the second pair of adjacent optical fibers differs from the optical fibers of the first pair of adjacent optical fibers.

20. An optical-fiber-cable unit comprising one or more optical-fiber ribbons according to claim 11 .