Polyimide and method for manufacturing same

1. A method for manufacturing a polyimide, comprising:

defining a first substance by using a diamine compound comprising an amide bond;

mixing a second substance with a first organic solvent and the first substance to prepare a third substance, wherein a molecular structure of the second substance comprises an ether dianhydride; and

processing the third substance by a cross-linking and curing process to form the polyimide;

wherein a plurality of steps for manufacturing the first substance comprise:

mixing a p-phenylenediamine or a 9H-carbazole-2,7-diamine with a second organic solvent to prepare a first mixture;

mixing a 4-aminobenzoic acid with the first mixture to prepare a second mixture, wherein a molar ratio of the p-phenylenediamine or the 9H-carbazole-2,7-diamine to the 4-aminobenzoic acid is 1:1; and

processing the second mixture by vacuum distillation and vacuum drying to prepare the first substance.

2. The method for manufacturing the polyimide in claim 1 , wherein the second organic solvent comprises N, N-dimethylformamide, N-methyl pyrrolidone, and N, N-dimethylacetamide.

3. The method for manufacturing the polyimide in claim 1 , wherein a mass of the second organic solvent is 1 time to 5 times a total mass of the p-phenylenediamine and the 4-aminobenzoic acid, or the mass of the second organic solvent is 1 time to 5 times a total mass of 9H-carbazole-2,7-diamine and 4-aminobenzoic acid.

4. The method for manufacturing the polyimide in claim 1 , wherein the 4-aminobenzoic acid with the molar ratio of 1:1 to the p-phenylenediamine or the 9H-carbazole-2,7-diamine is added to the first mixture within a preset duration, and the preset duration ranges from 1 hour to 2 hours.

5. The method for manufacturing the polyimide in claim 1 , wherein a preparation of the second mixture is processed by stirring with a stirring rate ranging from 100 rpm to 250 rpm, and a reaction time of the preparation ranges from 2 hours to 7 hours.

6. The method for manufacturing the polyimide in claim 1 , wherein a plurality of steps for manufacturing the third substance comprise:

mixing the second substance with the first organic solvent to prepare a third mixture, wherein the molecular structure of the second substance comprises the ether dianhydride;

mixing another second substance with the third mixture to prepare a fourth mixture, wherein a molecular structure of the another second substance comprises an ether dianhydride, and a molar ratio of the another second substance and the first substance is 1:1; and

performing a bubble removing process for the fourth mixture to prepare the third substance.

7. The method for manufacturing the polyimide in claim 6 , wherein a preparation of the third mixture is processed by stirring with a stirring rate ranging from 100 rpm to 250 rpm.

8. The method for manufacturing the polyimide in claim 6 , wherein a plurality of steps of the bubble removing process comprise:

stopping stirring the fourth mixture and filtering the fourth mixture in vacuum to prepare a fifth mixture; and

pumping the fifth mixture with a vacuum pump and allowing the fifth mixture to stand to form the third substance.

9. The method for manufacturing the polyimide in claim 8 , wherein the fifth mixture is pumped with the vacuum pump for 0.8 hour to 1.2 hours and the fifth mixture is allowed to stand for 2 hours to 4 hours to prepare the third substance.

10. The method for manufacturing the polyimide in claim 6 , wherein during a preparation of the fourth mixture, a stirring rate ranges from 300 rpm to 500 rpm, a reaction time ranges from 5 hours to 12 hours, and a reaction temperature ranges from 50° C. to 100° C.

11. The method for manufacturing the polyimide in claim 6 , wherein the first organic solvent comprises N, N-dimethylformamide, N-methyl pyrrolidone, and N, N-dimethylacetamide.

12. The method for manufacturing the polyimide as claimed in claim 6 , wherein a mass of the first organic solvent is 1 time to 5 times a mass of the second substance.

13. The method for manufacturing the polyimide in claim 1 , wherein the cross-linking and curing process comprises:

removing a solvent of the third substance by a spin coating and a high-temperature vacuum drying process, wherein the solvent has a first volume, and the first volume accounts for 65% to 75% of a volume of the third substance.

14. The method for manufacturing the polyimide in claim 13 , wherein the solvent having been removed is the first organic solvent.

15. The method for manufacturing the polyimide in claim 13 , wherein after the third substance is processed by the spin coating and the high-temperature vacuum drying process to prepare a sixth mixture, the cross-linking and curing process further comprises:

maintaining the sixth mixture at a first temperature for 20 minutes to 40 minutes;

heating the sixth mixture from the first temperature to a second temperature and holding the second temperature for 50 minutes to 70 minutes; and

cooling the sixth mixture from the second temperature to the first temperature;

wherein the first temperature ranges from 110° C. to 130° C., the second temperature ranges from 420° C. to 500° C., a duration time of a preset post-drying process ranges from 3 hours to 5 hours.

16. The method for manufacturing the polyimide in claim 15 , wherein the sixth mixture is heated from the first temperature to the second temperature in a constant heating rate, and the constant heating rate ranges from 4° C./min to 10° C./min; and the sixth mixture is cooled from the second temperature to the first temperature in a constant cooling rate, and the constant cooling rate ranges from 4° C./min to 10° C./min.

17. The method for manufacturing the polyimide in claim 1 , wherein the first substance comprises:

18. The method for manufacturing the polyimide in claim 1 , wherein the second substance comprises:

19. A polyimide, structures of the polyimide comprise: