Matting, exhaust gas purification device, and method for manufacturing matting
A mat material having a sufficiently high initial compression surface pressure is provided. The mat material of the present disclosure includes inorganic fibers; and an inorganic binder and an organic binder attached to the inorganic fibers, wherein the mat material has an initial compression surface pressure of 900 kPa or more as measured when compressed to a bulk density of 0.50 g/cm 3 .
1. A mat material comprising:
inorganic fibers; and
an inorganic binder and an organic binder attached to the inorganic fibers,
wherein the mat material has an initial compression surface pressure of 900 kPa or more as measured when compressed to a bulk density of 0.50 g/cm 3 ,
the mat material is a mat produced by papermaking, and
the mat material includes twisted strings of the inorganic fibers twisted together, and in a cross section parallel to a thickness direction of the mat material, a cross-sectional area percentage of the twisted strings is 0.5% or more and 10% or less relative to a cross-sectional area of the mat material.
2. The mat material according to claim 1 ,
wherein the mat material is produced by subjecting an inorganic fiber-binder mixture to papermaking, the inorganic fiber-binder mixture being a mixture of an inorganic fiber dispersion containing inorganic fibers having an underwater bulk specific gravity of 0.001 to 0.02 g/cm 3 , an inorganic binder, and an organic binder.
3. A method of producing a mat material, the method comprising:
a defibrating step of defibrating pre-defibration inorganic fibers by adding water to the pre-defibration inorganic fibers to produce an inorganic fiber dispersion;
an inorganic fiber-binder mixture producing step of mixing the inorganic fiber dispersion with an inorganic binder and an organic binder to obtain an inorganic fiber-binder mixture;
a papermaking step of subjecting the inorganic fiber-binder mixture to papermaking and dehydration to obtain a mat precursor; and
a heating and pressurizing step of heating and pressurizing the mat precursor to obtain a mat material,
wherein in the defibrating step, the pre-defibration inorganic fibers are defibrated such that the inorganic fibers after defibration have an underwater bulk specific gravity of 0.001 to 0.02 g/cm 3 .
4. A mat material comprising:
inorganic fibers; and
an inorganic binder and an organic binder attached to the inorganic fibers,
wherein the mat material has an initial compression surface pressure of 900 kPa or more as measured when compressed to a bulk density of 0.50 g/cm 3 ,
the mat material is a mat produced by papermaking, and
the mat material is produced by subjecting an inorganic fiber-binder mixture to papermaking, the inorganic fiber-binder mixture being a mixture of an inorganic fiber dispersion containing inorganic fibers having an underwater bulk specific gravity of 0.001 to 0.02 g/cm 3 , an inorganic binder, and an organic binder.