Silicon oxide-coated iron powder, method for producing the same, molded body for inductor using the same, and inductor
A silicon oxide-coated iron powder has a small particle diameter, can achieve high in a high frequency band, and has high insulating property. In a method for producing the powder, a silicon alkoxide is added to a slurry containing iron powder having an average particle diameter of 0.25 μm or more and 0.80 μm or less and an average axial ratio of 1.5 or less dispersed in a mixed solvent of water and an organic material containing water in an amount of 1% by mass or more and 40% by mass or less. Then, a hydrolysis catalyst for the silicon alkoxide is added to perform silicon oxide coating, the method resulting in a silicon oxide-coated iron powder having the high μ′ in a high frequency band and the high insulating property.
1. A silicon oxide-coated iron powder comprising iron particles having an average particle diameter of 0.25 μm or more and 0.80 μm or less and an average axial ratio of 1.5 or less, having coated on a surface thereof a silicon oxide, the silicon oxide-coated iron powder having a volume resistivity of 1.0×10 5 Ω·cm or more measured in a state of applying a voltage of 10 V to a powder compact made of the silicon oxide-coated iron powder by vertical compression molding of the silicon oxide-coated iron powder at 64 MPa, wherein the iron particles comprise less than 0.1 mass % of Si and the silicon oxide-coated iron powder has a Si content of 1.0% by mass or more and 10% by mass or less.
2. The silicon oxide-coated iron powder according to claim 1 , wherein the silicon oxide-coated iron powder has a P content of the iron particles of 0.1% by mass or more and 1.0% by mass or less based on the mass of the iron particles.
3. A molded body for an inductor, comprising the silicon oxide-coated iron powder according to claim 1 .
4. An inductor comprising the silicon oxide-coated iron powder according to claim 1 .