Quality control method for diisononyl phthalate, producing method for resin composition, resin composition, and cable or tube
A quality control method for a diisononyl phthalate includes a measuring step of irradiating the diisononyl phthalate with a laser to measure a Raman spectrum; and an acceptance or rejection decision step of determining an acceptance or a rejection of a quality of the diisononyl phthalate on the basis of a high and low intensity relationship between an intensity of a first spectral peak, which is ascribed to a vibration of molecular chains in a straight chain hydrocarbon, and an intensity of a second spectral peak, which is ascribed to a vibration of isopropyl groups, in the measured Raman spectrum.
1. A quality control method for a plurality of diisononyl phthalates, comprising:
a measuring step of irradiating each of the plurality of diisononyl phthalates produced under different conditions with a laser to measure a Raman spectrum; and
an acceptance or rejection decision step of determining an acceptance or a rejection of a quality of each of the plurality of diisononyl phthalates on the basis of a high and low intensity relationship between an intensity of a first spectral peak, which is ascribed to a vibration of molecular chains in a straight chain hydrocarbon, and an intensity of a second spectral peak, which is ascribed to a vibration of isopropyl groups, in the measured Raman spectrum,
wherein the acceptance or rejection decision step of determining the acceptance or the rejection of the quality is according to a proportion of a straight chain type alkyl chain structures included in each of the plurality of diisononyl phthalates.
2. The quality control method for the plurality of diisononyl phthalates according to claim 1 , wherein the first spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 880 cm −1 and not larger than 900 cm −1 in the measured Raman spectrum, while the second spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 840 cm −1 and not larger than 860 cm −1 in the measured Raman spectrum.
3. The quality control method for the plurality of diisononyl phthalates according to claim 1 , wherein, in the acceptance or rejection decision step, when a value of a ratio of an integral intensity of the first spectral peak to an integral intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.3, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
4. The quality control method for the plurality of diisononyl phthalates according to claim 1 , wherein, in the acceptance or rejection decision step, when a value of a ratio of a peak height intensity of the first spectral peak to a peak height intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.67, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
5. A method for producing a resin composition, comprising:
a step of adding the plurality of diisononyl phthalates regarded as accepted by the quality control method for the plurality of diisononyl phthalates according to claim 1 to a polyvinyl chloride.
6. A quality control method for a plurality of diisononyl phthalates, comprising:
a measuring step of irradiating each of the plurality of diisononyl phthalates produced under different conditions with a laser to measure a Raman spectrum; and
an acceptance or rejection decision step of determining an acceptance or a rejection of a quality of each of the plurality of diisononyl phthalates on the basis of a high and low intensity relationship between an intensity of a first spectral peak, which is ascribed to a vibration of molecular chains in a straight chain hydrocarbon, and an intensity of a second spectral peak, which is ascribed to a vibration of isopropyl groups, in the measured Raman spectrum,
wherein the determining the acceptance or the rejection of the quality of each of the plurality of diisononyl phthalates is on the basis of a ratio of the first spectral peak and the second spectral peak.
7. The quality control method for the plurality of diisononyl phthalates according to claim 6 , wherein the first spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 880 cm −1 and not larger than 900 cm −1 in the measured Raman spectrum, while the second spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 840 cm −1 and not larger than 860 cm −1 in the measured Raman spectrum.
8. The quality control method for the plurality of diisononyl phthalates according to claim 6 , wherein, in the acceptance or rejection decision step, when a value of a ratio of an integral intensity of the first spectral peak to an integral intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.3, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
9. The quality control method for the plurality of diisononyl phthalates according to claim 6 , wherein, in the acceptance or rejection decision step, when a value of a ratio of a peak height intensity of the first spectral peak to a peak height intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.67, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
10. A method for producing a resin composition, comprising:
a step of adding the plurality of diisononyl phthalates regarded as accepted by the quality control method for the plurality of diisononyl phthalates according to claim 6 to a polyvinyl chloride.
11. A quality control method for a plurality of diisononyl phthalates, comprising:
a measuring step of irradiating each of the plurality of diisononyl phthalates produced under different conditions with a laser to measure a Raman spectrum; and
an acceptance or rejection decision step of determining an acceptance or a rejection of a quality of each of the plurality of diisononyl phthalates on the basis of a high and low intensity relationship between an intensity of a first spectral peak, which is ascribed to a vibration of molecular chains in a straight chain hydrocarbon, and an intensity of a second spectral peak, which is ascribed to a vibration of isopropyl groups, in the measured Raman spectrum,
wherein each of the plurality of diisononyl phthalates includes a straight chain type alkyl chain structure that is used to measure the first spectral peak and the second spectral peak.
12. The quality control method for the plurality of diisononyl phthalates according to claim 11 , wherein the first spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 880 cm −1 and not larger than 900 cm −1 in the measured Raman spectrum, while the second spectral peak is a peak of which the intensity is a maximum within a wave number range of not smaller than 840 cm −1 and not larger than 860 cm −1 in the measured Raman spectrum.
13. The quality control method for the plurality of diisononyl phthalates according to claim 11 , wherein, in the acceptance or rejection decision step, when a value of a ratio of an integral intensity of the first spectral peak to an integral intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.3, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
14. The quality control method for the plurality of diisononyl phthalates according to claim 11 , wherein, in the acceptance or rejection decision step, when a value of a ratio of a peak height intensity of the first spectral peak to a peak height intensity of the second spectral peak measured under a condition of a measurement temperature of 26 degrees Celsius is not less than 0.67, a quality of each of the plurality of diisononyl phthalates is regarded as accepted.
15. A method for producing a resin composition, comprising:
a step of adding the plurality of diisononyl phthalates regarded as accepted by the quality control method for the plurality of diisononyl phthalates according to claim 11 to a polyvinyl chloride.