Process for producing superabsorbents
The invention relates to a process for producing long-term color stable superabsorbent polymer particles, comprising polymerization of a monomer solution, wherein the monomer solution comprises at least 0.01% by weight of 1-hydroxyethane-1,1-diphosphonic acid or a salt thereof and at least 0.01% by weight of 2-hydroxy-2-sulfonatoacetic acid or a salt thereof.
1. A process for producing long-term color stable superabsorbent polymer particles, comprising polymerizing a monomer solution comprising
a) partly neutralized acrylic acid,
b) at least one crosslinker,
c) at least one initiator,
d) 0.1 to 0.6% by weight of 1-hydroxyethane-1,1-diphosphonic acid or a salt thereof based on the acrylic acid prior to neutralization, and
e) 0.05 to 0.5% by weight of 2-hydroxy-2-sulfonatoacetic acid or a salt thereof based on the acrylic acid prior to neutralization,
drying the resulting polymer gel, optionally grinding and classifying the resulting dried polymer gel, and optionally thermally post-crosslinking and cooling the resulting polymer particles.
2. The process according to claim 1 , wherein a degree of neutralization of the partly neutralized acrylic acid is from 50 to 85 mol %.
3. The process according to claim 1 , wherein the superabsorbent polymer particles are thermally post-crosslinked.
4. The process according to claim 1 wherein the resulting polymer particles have a Hunter 60 value (HC60) after 28 days of aging at 60° C. and a relative humidity of 86% of at least 47.
5. The process according to claim 1 wherein the resulting polymer particles have a Hunter 60 value (HC60) after 28 days of aging at 60° C. and a relative humidity of 86% of at least 55.