Golf ball
In a golf ball for professional golfers and skilled amateurs which has a single-layer core, a cover and at least one intermediate layer therebetween, the core is molded from a rubber composition that includes a base rubber, an unsaturated carboxylic acid and/or metal salt thereof, an organic peroxide and, in a specific weight ratio, water and sulfur, and has a hardness profile which satisfies certain specific conditions. The ball achieves an excellent distance on full shots with a driver (W #1) and a middle iron, and is designed for high controllability in the short game.
1. A golf ball comprising a single-layer core, a cover and at least one intermediate layer interposed between the core and the cover, wherein the core is a material molded under heat from a rubber composition which comprises:
(a) a base rubber,
(b) a co-crosslinking agent which is an α, β-unsaturated carboxylic acid or a metal salt thereof or both,
(c) an organic peroxide,
(d) water, and
(e) sulfur
and in which components (d) and (e) have a weight ratio (e)/(d) therebetween that is equal to or more than 0.010; and the core has a hardness profile which satisfies the following conditions:
HAV−H 70≥−4, and
H 100− H 70>10,
where H0 is the JIS-C hardness at a center of the core, H50 is the JIS-C hardness at a point 50% from the core center, H70 is the JIS-C hardness at a point 70% from the core center, H100 is the JIS-C hardness at a surface of the core, and HAV is an average cross-sectional hardness obtained as the average of H0, H50 and H100, and
wherein the cover comprises:
(I) polyurethane or polyurea,
(II) a thermoplastic polyester elastomer, and
(III) an aromatic vinyl elastomer,
components (II) and (III) each being included in respective amounts of 20 parts by weight or less per 100 parts by weight of component (I) in which the amount of component (II) is larger than the amount of component (III), and
wherein the thermoplastic polyester elastomer serving as component (II) has a rebound resilience of from 50 to 72% and a melt viscosity at 200° C. and a shear rate of 243 s −1 of 1.0×10 4 dPa·s or less.
2. The golf ball of claim 1 which satisfies the condition:
H 100− H 0≥20.
3. The golf ball of claim 1 , wherein the rubber composition of the core further comprises (f) an antioxidant which is a benzimidazole of the following general formula or a metal salt thereof or both
(wherein R is a hydrogen atom or a hydrocarbon group of 1 to 20 carbon atoms and m is an integer from 1 to 4, with the proviso that if m is 2 or more, each R may be like or unlike).
4. The golf ball of claim 3 , wherein component (f) is selected from the group consisting of 2-mercaptobenzimidazole, 2-mercaptomethylbenzimidazole and metal salts thereof.
5. The golf ball of claim 1 , wherein the thermoplastic polyester elastomer serving as component (II) has a Shore D hardness of 45 or less, a rebound resilience of 74% or less, and a melt viscosity at 200° C. and a shear rate of 243 s −1 of 1.5×10 4 dPa·s or less.
6. The golf ball of claim 1 , wherein the aromatic vinyl elastomer serving as component (III) has a Shore D hardness of 30 or less and a rebound resilience of 30% or less.
7. The golf ball of claim 1 , wherein the amount of component (II) included per 100 parts by weight of component (I) is from 5 to 20 parts by weight and the content of component (III) per 100 parts by weight of component (I) is from 0.1 to 5 parts by weight.