High surface area coatings for solid-phase synthesis
High surface area coatings are applied to solid substrates to increase the surface area available for solid-phase synthesis of polymers. The high surface area coatings use three-dimensional space to provide more area for functional groups to bind polymers than an untreated solid substrate. The polymers may be oligonucleotides, polypeptides, or another type of polymer. The solid substrate is a rigid supportive layer made from a material such as glass, a silicon material, a metal material, and plastic. The coating may be thin films, hydrogels, microparticles. The coating may be made from a metal oxide, a high-κ dielectric, a low-κ dielectric, an etched metal, a carbon material, or an organic polymer. The functional groups may be hydroxyl groups, amine groups, thiolate groups, alkenes, n-alkenes, alkalines, N-Hydroxysuccinimide (NHS)-activated esters, polyaniline, aminosilane groups, silanized oxides, oligothiophenes, and diazonium compounds. Techniques for applying coatings to solid substrates and attaching functional groups are also disclosed.
1. A method of making a stack for solid-phase polymer synthesis comprising:
depositing a coating made up of nanoparticles that has a three-dimensional structure to a solid substrate wherein, depositing the coating comprises baking the nanoparticles for at least two hours to form the coating and the coating increases an available surface area relative to the solid substrate, wherein a yield of polymer synthesized on the stack is at least 10 times greater than a yield of solid-phase polymer synthesis on the solid substrate without the coating; and
attaching functional groups to the coating.
2. The method of claim 1 , wherein the nanoparticles comprise silicon dioxide nanoparticles.
3. The method of claim 1 , wherein the depositing comprises spin coating the solid substrate with the nanoparticles.
4. The method of claim 1 , wherein attaching the functional groups comprises silanization of the coating.
5. The method of claim 1 , wherein the solid substrate comprises a silicon material, a metal material, or a plastic.
6. The method of claim 1 , wherein depositing the coating comprises dip coating or spray coating.
7. The method of claim 3 , wherein the spin coating is performed at 2000 RPM for about 60 seconds.
8. The method of claim 1 , wherein the nanoparticles are particles with elongated shapes.
9. The method of claim 8 , wherein a narrow dimension of the nanoparticles is about 9-15 nm and a long dimension of the nanoparticles is about 40-100 nm.
10. The method of claim 1 , when the baking is performed at about 100 degrees Celsius.
11. The method of claim 1 , when the baking is performed overnight.
12. The method of claim 1 , wherein the coating forms a porous coating with pore sizes of about 20-50 nm.
13. The method of claim 1 , the coating is porous, about 1 μm thick, and baked for two hours at 100 degrees Celsius.
14. The method of claim 1 , wherein the solid substrate is a glass slide and the nanoparticles are colloidal silica nanoparticles.
15. The method of claim 1 , wherein the solid substrate is flat and provides a ridged surface that when coated with the nanoparticles has a textured surface.
16. The method of claim 1 , wherein the polymers are biological polymers.
17. The method of claim 16 , further comprising performing polymer synthesis on the coating, wherein the polymer is deoxyribonucleic acid (DNA) or a peptide.
18. The method of claim 1 , wherein the polymers are artificial organic polymers.