Composite member
The present invention provides an alloy, an alloy powder, an alloy member, and a composite member which are excellent in corrosion resistance and wear resistance, have crack resistance, and are suitable for an additive manufacturing method and the like. An alloy and an alloy powder include, by mass %, Cr: 18 to 22%, Mo: 18 to 28%, Ta: 1.5 to 57%, C: 1.0 to 2.5%, Nb: 0 to 42%, Ti: 0 to 15%, V: 0 to 27%, Zr: 0 to 29%, and a remainder consisting of Ni and unavoidable impurities, where a molar ratio of (Ta+0.7Nb+Ti+0.6V+Zr)/C=0.5 to 1.5 is satisfied. An alloy member is an additively manufactured product or a cast having such a solidification structure, and the solidification structure is a dendrite-like crystal structure having a metal phase having a face-centered cubic structure and carbides.
1. A composite member comprising:
a base material; and
an alloy layer laminated on a surface of the base material, wherein
the alloy layer which is a laminated model having a solidification structure, includes, by mass %,
Cr: 18 to 22%,
Mo: 18 to 28%,
Ta: 1.5 to 57%,
C: 1.0 to 2.5%
Nb: 0 to 42%,
Ti: 0 to 15%,
V: 0 to 27%,
Zr: 0 to 29%, and
a remainder consisting of Ni and unavoidable impurities, where a molar ratio of (Ta+0.7Nb+Ti+0.6V+Zr)/C=0.5 to 1.5 is satisfied, and wherein
the solidification structure is a dendrite crystal structure having a metal phase having a face-centered cubic structure and carbides including a carbide phase mainly containing any element of Ta, Nb, Ti, V, and Zr.
2. The composite member according to claim 1 , which is a screw for injection molding or a cylinder for injection molding.