Fireproof water-resistant wood chip material and method of its production
A wood chip material, especially a fireproof water resistant wood chip material, especially a fireproof water resistant wood chip material to make oriented strand boards which consists of a mixture containing 30 to 43 weight percent of wood chips, 53 to 61.9 weight percent of an aqueous solution of silicate, 2 to 5 weight percent of aluminium hydroxide, 1 to 3 weight percent of water, 0.1 to 1 weight percent of a stabilizer of the aqueous solution of silicate, and a hardener of the aqueous solution of sodium silicate in the concentration of 0.5 to 5 weight percent to the pure aqueous solution of sodium silicate providing always that the density of the aqueous solution of sodium silicate ranges from 1370 to 1400 kg/m 3 and the SiO 2 to NA 2 O molar ratio in the aqueous solution of sodium silicate ranges from 3.2 to 3.4. A method of production of a wood chip material, especially method of production of a fireproof water resistant wood chip material, especially method of production of a fireproof water resistant wood chip material to make oriented strand boards according to which, as the first step, the aluminium hydroxide is mixed with water, then wood chips are added into the mixture and everything is stirred thoroughly in such a manner that a wood chip mixture is formed, then the stabilizer of the aqueous solution of sodium silicate is added in the aqueous solution of silicate and after that the hardener of the aqueous solution of sodium silicate is admixed in this solution. Then the solution is stirred for 1 to 10 minutes until a binding solution is formed. Then the wood chip mixture is poured, at continuous stirring, in the binding solution and everything is stirred thoroughly again. Then the resulting mixture is poured in the place of application.
1. A fireproof water-resistant wood chip material to make oriented strand boards, comprising a mixture comprising
30 to 43 weight percent of wood chips,
53 to 61.9 weight percent of an aqueous solution of sodium silicate,
2 to 5 weight percent of aluminum hydroxide,
1 to 3 weight percent of water,
0.1 to 1 weight percent of a stabilizer of the aqueous solution of silicate, and
a hardener of the aqueous solution of sodium silicate in the concentration of 0.5 to 5 weight percent to the pure aqueous solution of sodium silicate,
wherein the density of the aqueous solution of sodium silicate ranges from 1370 to 1400 kg/m 3 , and
wherein the Si0 2 to Na 2 O molar ratio in the aqueous solution of sodium silicate ranges from 3.2 to 3.4.
2. The wood chip material according to claim 1 , wherein the wood chips are spruce chips and/or pine chips.
3. The wood chip material according to claim 1 , wherein hydrophilic alkoxyle alkyl ammonia salts are used as the stabilizer of the aqueous solution of sodium silicate.
4. A method of production of a fireproof water resistant wood chip material to make oriented strand boards of claim 1 , wherein in a first step, the aluminum hydroxide is mixed with water, then wood chips are added into the mixture and the resulting mixture is stirred thoroughly in such a manner that a wood chip mixture is formed, then in a second step the stabilizer of the aqueous solution of sodium silicate is added to the aqueous solution of silicate, and after that the hardener of the aqueous solution of sodium silicate is admixed with the resulting solution, then the solution is stirred for 1 to 10 minutes until a binding solution is formed, then the wood chip mixture of the first step is poured, at continuous stirring, in the binding solution of the second step and the resulting mixture is stirred thoroughly before the resulting mixture is poured in the place of application.
5. The method of production of the wood chip material according to claim 4 , wherein the resulting mixture is, after being poured in the place of application, is left undisturbed until it becomes hardened.