Microchannel heat sink and method of manufacturing the same

1. A method of manufacturing a microchannel heat sink, comprising:

processing preset inlet and outlet flow channels and a microchannel structure on each of plates constituting the microchannel heat sink;

preparing an upper cover plate and a lower cover plate, and processing corresponding patterns on the upper cover plate and the lower cover plate according to the microchannel structures of an uppermost plate and a lowermost plate of the microchannel heat sink to be manufactured, respectively;

aligning and stacking the upper cover plate, the each of the plates, and the lower cover plate in sequence;

placing the upper cover plate, the each of the plates, and the lower cover plate that are aligned and stacked in a reducing atmosphere for heating and heat preservation, and applying a pressure on the upper cover plate and/or the lower cover plate; and

after applying the pressure for a preset time, stopping the heat preservation and stopping the applying the pressure, and removing the upper cover plate and the lower cover plate.

2. The method of manufacturing the microchannel heat sink according to claim 1 , further comprising respectively processing positioning holes at corresponding positions of the upper cover plate, the each of the plates, and the lower cover plate,

wherein when being aligned and stacked, the upper cover plate, the each of the plates, and the lower cover plate are aligned via the positioning holes.

3. The method of manufacturing the microchannel heat sink according to claim 2 , wherein the positioning holes are distributed at portions of each of the plates near corners thereof, and located in areas other than the preset inlet and outlet flow channels and the microchannel structure on each plate.

4. The method of manufacturing the microchannel heat sink according to claim 1 , wherein the inlet and outlet flow channels and the microchannel structure on the each of the plates are processed by any one of chemical etching, laser cutting, plasma cutting, flame cutting, abrasive cutting, water jet cutting, wire cutting, computer numerical control (CNC) machine tool processing, and punching.

5. The method of manufacturing the microchannel heat sink according to claim 1 , wherein the upper cover plate and the lower cover plate are made of a metal or an alloy.

6. The method of manufacturing the microchannel heat sink according to claim 1 , wherein a thickness of the upper cover plate and a thickness of the lower cover plate are not less than a depression depth of the corresponding cover plate when receiving the pressure.

7. The method of manufacturing the microchannel heat sink according to claim 1 , further comprising providing an easily separable isolation layer between the upper cover plate and a plate adjacent to the upper cover plate and/or between the lower cover plate and a plate adjacent to the lower cover plate.

8. The method of manufacturing the microchannel heat sink according to claim 7 , wherein the easily separable isolation layer is a graphite paper or a graphite liquid.

9. The method of manufacturing the microchannel heat sink according to claim 1 , wherein applying the pressure is realized by placing an upper pressing block and a lower pressing block on opposite sides of the upper cover plate and the lower cover plate away from the stacked plates, respectively, and the upper pressing block and the lower pressing block respectively applying the pressure to the stacked plates through pressing the cover plates, or realized by directly pressing the upper cover plate and the lower cover plate to apply the pressure to the stacked plates.

10. The method of manufacturing the microchannel heat sink according to claim 1 , wherein the applied pressure is in a range of 1 MPa to 20 MPa.

11. The method of manufacturing the microchannel heat sink according to claim 1 , wherein the heating is performed by increasing a temperature to 300° C. to 950° C. at a rate of 30° C./min to 8000° C./min, and a time for the heat preservation is in a range of 120 s to 3600 s.