Cemented carbide compositions and applications thereof
Sintered cemented carbides are described herein exhibiting enhanced high temperature properties without dramatic losses in bending strength. In some embodiments, a sintered cemented carbide composition comprises tungsten carbide, a metallic binder phase comprising at least one metal of the iron group, and at least one solid solution carbide phase comprising tantalum (Ta) and molybdenum (Mo), wherein a value of (Mo/Ta) in the sintered cemented carbide composition is from 0.3-100, and the sintered cemented carbide composition has a transverse rupture strength of at least 4000 MPa.
1. A sintered cemented carbide composition comprising:
tungsten carbide, a metallic binder phase comprising at least one metal of the iron group, and at least one solid solution carbide phase comprising tantalum (Ta) and molybdenum (Mo), wherein a value of (Mo/Ta) in the sintered cemented carbide composition is from 0.3-100 and the sintered cemented carbide composition has a transverse rupture strength of at least 4000 MPa, wherein the metallic binder phase is present in an amount of 1-20 wt. %, Ta is present in an amount of 0.05-1.5 wt. %, Mo is present in an amount of 0.5 to 5 wt. % with the tungsten carbide being a main constituent and providing a balance of the sintered cemented carbide composition, and wherein the sintered cemented carbide composition optionally includes vanadium in an amount of 0.05-0.15 wt. %.
2. The sintered cemented carbide composition of claim 1 , wherein Ta is present in an amount exceeding the solubility limit of Ta in the metallic binder phase.
3. The sintered cemented carbide composition of claim 2 , wherein the value of (Mo/Ta) is from 1 to 10.
4. The sintered cemented carbide composition of claim 2 , wherein the value of (Mo/Ta) is from 1 to 5.
5. The sintered cemented carbide composition of claim 1 , having hardness of at least 1500 HV30.
6. The sintered cemented carbide composition of claim 1 , having hardness of 1600-2000 HV30.
7. The sintered cemented carbide composition of claim 5 , wherein the transverse rupture strength is at least 4300 MPa.
8. The sintered cemented carbide composition of claim 1 , wherein the vanadium is present in the composition in an amount of 0.05-0.15 wt. %.
9. The sintered cemented carbide composition of claim 8 , wherein the vanadium is present in an amount less than the tantalum.
10. The sintered cemented carbide composition of claim 8 , wherein the vanadium is part of the solid solution carbide phase.
11. The sintered cemented carbide composition of claim 1 having a magnetic saturation of 75-85%.
12. The sintered cemented carbide composition of claim 11 , wherein the solid solution carbide phase precipitates as clusters.
13. A sintered cemented carbide composition comprising:
tungsten carbide, a metallic binder comprising at least one metal of the iron group, and at least one solid solution carbide phase comprising tantalum (Ta), molybdenum (Mo) and vanadium (V), wherein tantalum is present in an amount exceeding the solubility limit of tantalum in the metallic binder phase, the tungsten carbide is a main constituent of the sintered cemented carbide composition, Mo is present in an amount from 0.5 to 3 wt. % of the sintered cemented carbide composition, and the sintered cemented carbide composition has a transverse rupture strength of at least 4000 MPa.
14. The sintered cemented carbide composition of claim 13 , wherein a value of (V/Ta) is less than 1.
15. The sintered cemented carbide composition of claim 13 , wherein the solid solution carbide phase comprises chromium.
16. The sintered cemented carbide composition of claim 13 , wherein the composition comprises one or more of the following features:
the sintered cemented carbide composition has a magnetic saturation of 75-85%;
the sintered cemented carbide composition having hardness of at least 1600 HV30;
the solid solution carbide phase precipitates in clusters; and
the metallic binder phase is present in an amount of 3-15 wt. % of the sintered cemented carbide composition.
17. The sintered cemented carbide composition of claim 13 , wherein the solid solution carbide phase precipitates as clusters.