Passive radiative cooling ceramic
A radiative cooling apparatus including a layer of a material. The layer defines an exterior face. The material has a composition such that the layer is configured to reflect, at the exterior face, at least partly of the incoming electromagnetic radiation of at least some wavelengths in the solar spectrum. The layer is further configured to emit thermally-generated electromagnetic emission of at least some mid-infrared wavelengths out from the exterior face. Ceramics provided by embodiments of the invention could produce extra cooling effect without any electricity consumption, creating a prominent benefit to the energy saving of air conditioning systems of buildings.
1. A radiative cooling apparatus comprising a layer of a ceramic material; the layer defining an exterior face; the ceramic material comprising a metal oxide having a composition such that the layer is configured to reflect, at the exterior face, at least part of an incoming electromagnetic radiation of at least some wavelengths in the solar spectrum; the layer further configured to emit thermally-generated electromagnetic emission of at least some mid-infrared wavelengths out from the exterior face, wherein the material comprises a porous structure and is homogenous along all directions; wherein the porous structure has a porosity of 60%-90% and a pore distribution of 50 nm-10 μm.
2. The radiative cooling apparatus of claim 1 , wherein the porous structure has a porosity of 70 %.
3. The radiative cooling apparatus of claim 1 , wherein the ceramic material has a substantially white color.
4. The radiative cooling apparatus of claim 1 , further comprises a color glaze attached to the exterior face of the ceramic material.
5. A method of preparing a radiative cooling material according to claim 1 , comprising the steps of:
a) providing an organic solution containing a polymer;
b) adding a metal oxide into the organic solution to form a suspension;
c) conducting a phase inversion process of the suspension to form a precursor; and
d) sintering the precursor to obtain the radiative cooling material.
6. The method of claim 5 , further comprises, after step a), the step of stirring the organic solution using a magnetic stirrer.
7. The method of claim 5 , further comprises, after step b), the step of degassing the suspension with stirring to remove air bubbles in the suspension.
8. The method of claim 5 , wherein step d) further comprising sintering the precursor in an environment in which a temperature steadily rising from room temperature to 1000° C. at rate of 5° C./minute, and then maintained at 1000° C. for 3 hours.
9. The method of claim 8 , wherein step d) further comprising supplying air to the environment at a rate of at 200 ml/min.
10. A method of glazing a radiative cooling material, comprising the steps of:
a) providing a radiative cooling material prepared according to claim 5 ;
b) applying a water-based glaze solution on an exterior face of the radiative cooling material; and
c) sintering the radiative cooling material to obtain a glazed material.