Hot-rolled steel sheet for non-oriented electrical steel sheet, non-oriented electrical steel sheet, and method for manufacturing same
A hot-rolled steel sheet for a non-oriented electrical steel sheet according to one aspect of the present invention contains, by mass %, C: 0.0050% or less, Si: 0.5% or more and 3.5% or less, Mn: 0.1% or more and 1.5% or less, Al: 0.1% or more and 1.5% or less, Cu: 0.01% or more and 0.10% or less, Sn: 0.01% or more and 0.20% or less, and a remainder including Fe and impurities, in which the hot-rolled steel sheet has a Cu concentration peak value of 0.12% or more in a range from a surface thereof to a depth of 10 μm.
1. A hot-rolled steel sheet for a non-oriented electrical steel sheet comprising, by mass %:
C: 0.0050% or less;
Si: 0.5% or more and 3.5% or less;
Mn: 0.1% or more and 1.5% or less;
Al: 0.1% or more and 1.5% or less;
Cu: 0.010% or more and 0.10% or less;
Sn: 0.010% or more and 0.20% or less; and
a remainder including Fe and impurities,
wherein the hot-rolled steel sheet has a Cu concentration peak value of 0.12% or more in a range from a surface thereof to a depth of 10 μm.
2. A non-oriented electrical steel sheet comprising, by mass %:
C: 0.0050% or less;
Si: 0.5% or more and 3.5% or less;
Mn: 0.1% or more and 1.5% or less;
Al: 0.1% or more and 1.5% or less;
Cu: 0.010% or more and 0.10% or less;
Sn: 0.010% or more and 0.20% or less; and
a remainder including Fe and impurities,
wherein the non-oriented electrical steel sheet has a Cu concentration peak value of 0.12% or more in a range from a surface thereof to a depth of 5 μm.
3. A manufacturing method of the hot-rolled steel sheet for a non-oriented electrical steel sheet according to claim 1 , the method comprising:
steelmaking; and
hot rolling,
wherein the hot rolling includes slab heating, rough rolling, finish rolling, and coiling,
an air ratio in the slab heating of the hot rolling is set to 1.0 or more and 1.2 or less,
a temperature of a rough-rolled steel sheet immediately before the finish rolling of the hot rolling is set to 1000° C. or higher and 1050° C. or lower,
a finish rolling temperature in the finish rolling of the hot rolling is set to 930° C. or higher and 970° C. or lower, and
a coiling temperature in the coiling of the hot rolling is set to 750° C. or higher and 800° C. or lower.
4. A manufacturing method of the non-oriented electrical steel sheet according to claim 2 , the method comprising:
pickling;
cold rolling; and
final annealing,
wherein, in the cold rolling, the hot-rolled steel sheet for a non-oriented electrical steel sheet comprising, by mass %:
C: 0.0050% or less;
Si: 0.5% or more and 3.5% or less;
Mn: 0.1% or more and 1.5% or less;
Al: 0.1% or more and 1.5% or less;
Cu: 0.010% or more and 0.10% or less;
Sn: 0.010% or more and 0.20% or less; and
a remainder including Fe and impurities,
wherein the hot-rolled steel sheet has a Cu concentration peak value of 0.12% or more in a range from a surface thereof to a depth of 10 μm,
is cold-rolled.
5. The manufacturing method of the non-oriented electrical steel sheet according to claim 4 ,
wherein a pickling solution used in the pickling contains thiosulfate.