Phosphor particles, composite, wavelength conversion member, and projector
Phosphor particles for producing a wavelength conversion member of a projector, including CASN, and/or SCASN. A cured sheet having a film thickness of 50±5 μm produced by using the particle satisfies the following optical characteristics: when an intensity at a peak wavelength of blue light emitted from a blue LED having a peak wavelength between 450 to 460 nm is defined as Ii [W/nm], and where the blue light is emitted to one surface side of the cured sheet, when an intensity of light emitted from the other surface side of the cured sheet at a peak wavelength between 450 to 460 nm is defined as It [W/nm] and an intensity thereof at a peak wavelength between 600 to 650 nm is defined as Ip [W/nm], It/Ii is equal to or less than 0.2 and Ip/Ii is equal to or more than 0.05.
1. Phosphor particles for producing a wavelength conversion member of a projector, the phosphor particles comprising:
CASN, wherein CASN is a phosphor in which a main crystal phase has a same crystal structure as that of CaAlSiN 3 and a general formula represented by MAlSiN 3 :Eu in which M is one or more elements selected from Sr, Mg, Ca, and Ba; and/or
SCASN, wherein SCASN is an Sr-containing phosphor in which a main crystal phase has a same crystal structure as that of CaAlSiN 3 and a general formula represented by (Sr, Ca) AlSiN 3 :Eu,
wherein a cured sheet produced by the following sheet producing procedure:
(1) 40 parts by mass of the phosphor particle and 60 parts by mass of a silicone resin OE-6630 manufactured by Dow Corning Toray Co., Ltd. are subjected to a stirring treatment and a defoaming treatment using a rotation and revolution mixer to obtain a uniform mixture,
(2) the mixture obtained in the section (1) is added dropwise to a transparent first fluororesin film, a transparent second fluororesin film is further laminated on the dropped material to obtain a sheet-like material, and this sheet-like material is molded into an uncured sheet using a roller having a gap in which 50 μm is added to a total thickness of the first fluororesin film and the second fluororesin film,
(3) the uncured sheet obtained in the section (2) is heated under conditions of 150° C. and 60 minutes, and the first fluororesin film and the second fluororesin film are peeled off to obtain a cured sheet having a film thickness of 50±5 μm,
satisfies the following optical characteristics:
when an intensity at a peak wavelength of blue light emitted from a blue LED having a peak wavelength in a range of 450 nm to 460 nm is defined as Ii [W/nm], and in a case where the blue light is irradiated on one surface side of the cured sheet, an intensity of light emitted from the other surface side of the cured sheet at a peak wavelength in the range of 450 nm to 460 nm is defined as It [W/nm], and an intensity of the light emitted from the other surface side of the cured sheet at a peak wavelength in a range of 600 nm to 650 nm is defined as Ip [W/nm], It/Ii is equal to or less than 0.2 and Ip/Ii is equal to or more than 0.05.
2. The phosphor particle according to claim 1 ,
wherein, in a case where a volume-based cumulative 50% diameter and a volume-based cumulative 90% diameter measured by a laser diffraction and scattering method are each defined as D 50 and D 90 , D 50 is equal to or less than 10 μm, and D 90 is equal to or less than 17 μm,
here, D 50 and D 90 are values measured by using a liquid obtained by putting 0.5 g of the phosphor particle into 100 mL of an ion exchange aqueous solution containing 0.05% by mass of sodium hexametaphosphate, and performing a dispersion treatment for 3 minutes by placing a chip in a center portion of the liquid using an ultrasonic homogenizer having a transmission frequency of 19.5±1 kHz and an amplitude of 31±5 μm.
3. The phosphor particle according to claim 1 ,
wherein an oxygen content is equal to or more than 1% by mass.
4. The phosphor particle according to claim 1 ,
wherein a light absorption rate with respect to light at a wavelength of 700 nm is equal to or less than 20%.
5. A composite comprising:
the phosphor particle according to claim 1 ; and
a sealing material that seals the phosphor particle.
6. A wavelength conversion member comprising the composite according to claim 5 .
7. A projector comprising the wavelength conversion member according to claim 6 .