Method for producing hollow resin particles
A method for producing hollow resin particles, the method comprising a mixture liquid preparation step, a suspension preparation step, a polymerization step, and a solvent removal step; wherein a content of a saturated hydrocarbon solvent is 50% by mass or more with respect to 100% by mass of a total amount of a hydrocarbon solvent; wherein a polymerization initiator is an oil-soluble polymerization initiator; and wherein, in the mixture liquid, a crosslinkable monomer contains a tri- or higher functional crosslinkable monomer, and with respect to 100 parts by mass of a total amount of the polymerizable monomer, a total content of the crosslinkable monomer is 80 to 98 parts by mass, a content of the tri- or higher functional crosslinkable monomer is from 10 parts by mass to 98 parts by mass, and a content of the hydrocarbon solvent is from 300 parts by mass to 1500 parts by mass.
1. A method for producing hollow resin particles, the method comprising:
a mixture liquid preparation step comprising preparing a mixture liquid which contains a polymerizable monomer containing a non-crosslinkable monomer and a crosslinkable monomer, a hydrocarbon solvent, a polymerization initiator and an aqueous medium,
a suspension preparation step comprising, by suspending the mixture liquid, preparing a suspension in which polymerizable monomer droplets including the hydrocarbon solvent are dispersed in the aqueous medium,
a polymerization step comprising, by a polymerization reaction of the suspension, preparing a precursor composition containing a precursor particle having a hollow portion in which the hydrocarbon solvent is included, and
a solvent removal step comprising removing the hydrocarbon solvent included in the precursor particle;
wherein a content of the saturated hydrocarbon solvent is 50% by mass or more, with respect to 100% by mass of a total amount of the hydrocarbon solvent;
wherein the polymerization initiator is an oil-soluble polymerization initiator; and
wherein the crosslinkable monomer contains a tri- or higher functional crosslinkable monomer having three or more polymerizable functional groups, and with respect to 100 parts by mass of a total amount of the polymerizable monomer in the mixture liquid, a total content of the crosslinkable monomer is from 80 parts by mass to 98 parts by mass, a content of the tri- or higher functional crosslinkable monomer is from 10 parts by mass to 98 parts by mass, and a content of the hydrocarbon solvent is from 300 parts by mass to 1500 parts by mass.
2. The method for producing hollow resin particles according to claim 1 , wherein a volume average particle diameter of the hollow resin particles is from 1 μm to 20 μm.
3. The method for producing hollow resin particles according to claim 1 , wherein the polymerizable monomer in the mixture liquid contains from 1 part by mass to 10 parts by mass of a carboxyl group-containing monomer, with respect to 100 parts by mass of a total amount of the polymerizable monomer.
4. The method for producing hollow resin particles according to claim 1 , wherein the hydrocarbon solvent has 4 to 7 carbon atoms.
5. The method for producing hollow resin particles according to claim 1 , wherein the solvent removal step is a step comprising removing the hydrocarbon solvent included in the precursor particle in the precursor composition by bubbling an inert gas into the precursor composition at a temperature higher than or equal to a temperature subtracted from the boiling point of the hydrocarbon solvent by 35° C.