Dental zirconia blank having multilayer structure different in content of yttria
To provide a dental zirconia blank which has high permeability, can reproduce a color tone close to a natural tooth and a strength to be able to tolerate in oral cavity. Furthermore, to provide a dental zirconia blank from which a prosthesis device of 4 or more units having high strength can be prepared. To provide a dental zirconia blank having a plurality of layers, comprising; a first layer consisting of a high permeability ceramic containing 91.6 to 96.5 mol % of zirconium oxide and 3.5 to 8.4 mol % of yttrium oxide, and a second layer consisting of a low permeability ceramic containing 95.6 to 98.5 mol % of zirconium oxide and 1.5 to 4.4 mol % of yttrium oxide, wherein a content rate of yttrium oxide in the low permeability ceramic is lower than a content rate of yttrium oxide in the high permeability ceramic by 0.5 to 5.4 mol %, and the first layer is positioned at one end of the plurality of layers in a layering direction.
1. A dental zirconia blank consisting of;
a first layer consisting of a high permeability ceramic containing 91.6 to 96.5 mol % of zirconium oxide and 3.5 to 8.4 mol % of yttrium oxide, and
a second layer consisting of a low permeability ceramic containing 95.6 to 98.5 mol % of zirconium oxide and 1.5 to 4.4 mol % of yttrium oxide, wherein
a content rate of yttrium oxide in the low permeability ceramic is lower than a content rate of yttrium oxide in the high permeability ceramic by 0.5 to 5.4 mol %,
a ceramic powder constituting the high permeability ceramic and a ceramic powder constituting the low permeability ceramic have BET specific surface areas within a range of 5 to 20 m 2 /g, and
the ceramic powder constituting the high permeability ceramic and the ceramic powder constituting the low permeability ceramic have average primary particle diameters within a range of 10 to 1000nm.
2. The dental zirconia blank according to claim 1 , wherein
the first layer consists of a plurality of high permeability layered areas having different compositions with each other.
3. The dental zirconia blank according to claim 2 , wherein
the first layer consists of a plurality of high permeability layered areas having different content rates of zirconium oxide and/or different content rates of yttrium oxide in the high permeability ceramic with each other.
4. The dental zirconia blank according to claim 2 , wherein
at least one high permeability layered area includes 0.0001 to 0.30 mol % of erbium oxide.
5. The dental zirconia blank according to claim 1 , wherein
the second layer consists of a plurality of low permeability layered areas having different compositions with each other.
6. The dental zirconia blank according to claim 5 , wherein
the second layer consists of a plurality of low permeability layered areas having different content rates of zirconium oxide and/or different content rates of yttrium oxide in the low permeability ceramic with each other.
7. The dental zirconia blank according to claim 5 , wherein
at least one low permeability layered area includes 0.0001 to 0.30 mol % of erbium oxide.
8. The dental zirconia blank according to claim 1 , wherein
the high permeability ceramic is a temporary calcined body of a plurality of powders having different compositions with each other.
9. The dental zirconia blank according to claim 1 , wherein
the low permeability ceramic is a temporary calcined body of a plurality of powders having different compositions with each other.
10. The dental zirconia blank according to claim 1 , wherein
the first layer is positioned to a position spaced from a surface of a side of one end in a layering direction by a range of 5 to 40% of a dimension between the surface of the side of the one end and a surface of a side of the other end opposing to the surface of the side of the one end on a perpendicular line from the center of the gravity of the surface of the side of the one end at which the first layer is positioned in the layering direction of the dental zirconia blank.
11. The dental zirconia blank according to claim 1 , wherein
a difference of BET specific surface area between the ceramic powder constituting the high permeability ceramic and the ceramic powder constituting the low permeability ceramic is within a range of 2 m 2 /g and a difference of an average primary particle diameter between the ceramic powder constituting the high permeability ceramic and the ceramic powder constituting the low permeability ceramic is within a range of 20 nm.
12. The dental zirconia blank according to claim 2 , wherein
transparency of at least one high permeability layered area is higher than transparency of the second layer, and
the chromaticities LE, aE, bE of the at least one high permeability layered area based on the L*·a*·b* colorimetric system satisfy the following relations:
65.0≤ LE≤ 82.0
−4.0≤ aE≤ 2.0
0.0≤ bE≤ 20.0.
13. The dental zirconia blank according to claim 1 , wherein
transparency of the first layer is higher than transparency of the second layer, and
the chromaticities LE, aE, bE of the first layer based on the L*·a*·b* colorimetric system satisfy the following relations:
65.0≤ LE≤ 82.0
−4.0≤ aE≤ 2.0
0.0≤ bE≤ 20.0.
14. The dental zirconia blank according to claim 1 , wherein
the high permeability ceramic includes 0.0001 to 0.30 mol % of erbium oxide.
15. The dental zirconia blank according to claim 1 , wherein
the low permeability ceramic includes 0.0001 to 0.30 mol % of erbium oxide.
16. The dental zirconia blank according to claim 1 , wherein
the first layer consists of a plurality of high permeability layered areas having different compositions with each other, and
the second layer consists of a plurality of low permeability layered areas having different compositions with each other.
17. The dental zirconia blank according to claim 1 , wherein
the first layer consists of a plurality of high permeability layered areas having different content rates of zirconium oxide and/or different content rates of yttrium oxide in the high permeability ceramic with each other, and
the second layer consists of a plurality of low permeability layered areas having different content rates of zirconium oxide and/or different content rates of yttrium oxide in the low permeability ceramic with each other.