Insert and cutting tool including same
An insert includes a base of a cermet including hard particles and a binder phase. The base includes first and second surfaces, a cutting edge on at least a part of a ridge line of the first and second surfaces, a third surface opposite to the first surface, and a through hole from the first surface to the third surface. An inner wall constituting the through hole includes a binder-phase-riched layer having a higher content of the binder phase than an inside of the base, at least in a center part. A thickness of the binder-phase-ricked layer in the center part is larger than a thickness of the binder-phase-ricked layer in an end part of the inner wall. A cutting tool includes a holder which has a pocket located at an end, the insert located in the pocket, and a clamp inserted in the through hole of the insert.
1. An insert, comprising a base which is a cermet comprising hard particles and a binder phase, wherein
the base comprises
a first surface,
a second surface,
a cutting edge located on at least a part of a ridge line of the first surface and the second surface,
a third surface located opposite to the first surface, and
a through hole from the first surface to the third surface,
an inner wall constituting the through hole comprises a binder-phase-riched layer having a higher content of the binder phase than an inside of the base, at least in a center part,
a thickness T1 of the binder-phase-riched layer in the center part is larger than a thickness T2 of the binder-phase-riched layer in an end part of the inner wall, and
the thickness T1 is 1 μm or more, and 20 μm or less.
2. The insert according to claim 1 , wherein the thickness T2 is 0.2 μm or more, and 6 μm or less.
3. The insert according to claim 1 , wherein a diameter R1 in the center part is larger than a diameter R2 in the end part.
4. The insert according to claim 3 , wherein the diameter R1 is 5 μm or more, and 30 μm or less larger than the diameter R2.
5. The insert according to claim 1 , wherein a hardness of the binder-phase-riched layer in the center part is 10 GPa or more, and 20 GPa or less.
6. The insert according to claim 1 , wherein the binder-phase-riched layer in the center part comprises a metal layer having a higher content of the binder phase than the binder-phase-riched layer at a side of a through axis of the through hole.
7. The insert according to claim 1 , comprising a coating layer on the binder-phase-riched layer in the center part, wherein the coating layer comprises a part having a higher hardness than that of the binder-phase-riched layer.
8. A cutting tool, comprising:
a holder which has a length extending from a first end to a second end, and which comprises a pocket located at a side of the first end;
the insert according to claim 1 , the insert being located in the pocket; and
a clamp inserted in the through hole of the insert.
9. An insert, comprising a base which is a cermet comprising hard particles and a binder phase, wherein
the base comprises
a first surface,
a second surface,
a cutting edge located on at least a part of a ridge line of the first surface and the second surface,
a third surface located opposite to the first surface, and
a through hole from the first surface to the third surface,
an inner wall constituting the through hole comprises a binder-phase-riched layer having a higher content of the binder phase than an inside of the base, at least in a center part,
a thickness T1 of the binder-phase-riched layer in the center part is larger than a thickness T2 of the binder-phase-riched layer in an end part of the inner wall, and
the thickness T2 is 0.2 μm or more, and 6 μm or less.
10. The insert according to claim 9 , wherein a diameter R1 in the center part is larger than a diameter R2 in the end part.
11. The insert according to claim 10 , wherein the diameter R1 is 5 μm or more, and 30 μm or less larger than the diameter R2.
12. The insert according to claim 9 , wherein a hardness of the binder-phase-riched layer in the center part is 10 GPa or more, and 20 GPa or less.
13. The insert according to claim 9 , wherein the binder-phase-riched layer in the center part comprises a metal layer having a higher content of the binder phase than the binder-phase-riched layer at a side of a through axis of the through hole.
14. The insert according to claim 9 , comprising a coating layer on the binder-phase-riched layer in the center part, wherein the coating layer comprises a part having a higher hardness than that of the binder-phase-riched layer.
15. A cutting tool, comprising:
a holder which has a length extending from a first end to a second end, and which comprises a pocket located at a side of the first end;
the insert according to claim 10 , the insert being located in the pocket; and
a clamp inserted in the through hole of the insert.
16. An insert, comprising a base which is a cermet comprising hard particles and a binder phase, wherein
the base comprises
a first surface,
a second surface,
a cutting edge located on at least a part of a ridge line of the first surface and the second surface,
a third surface located opposite to the first surface, and
a through hole from the first surface to the third surface,
an inner wall constituting the through hole comprises a binder-phase-riched layer having a higher content of the binder phase than an inside of the base, at least in a center part,
a thickness T1 of the binder-phase-riched layer in the center part is larger than a thickness T2 of the binder-phase-riched layer in an end part of the inner wall, and
a diameter R1 in the center part is larger than a diameter R2 in the end part.
17. The insert according to claim 16 , wherein the diameter R1 is 5 μm or more, and 30 μm or less larger than the diameter R2.
18. The insert according to claim 16 , wherein a hardness of the binder-phase-riched layer in the center part is 10 GPa or more, and 20 GPa or less.
19. The insert according to claim 16 , wherein the binder-phase-riched layer in the center part comprises a metal layer having a higher content of the binder phase than the binder-phase-riched layer at a side of a through axis of the through hole.
20. The insert according to claim 16 , comprising a coating layer on the binder-phase-riched layer in the center part, wherein the coating layer comprises a part having a higher hardness than that of the binder-phase-riched layer.