Separation of fibers
There is provided a method for separation of fibers in for instance recycled textile, starting with a mixture comprising cellulose fibers and non-cellulose fibers and then reducing the cellulose chain length of the cellulose fibers so that the limiting viscosity number determined according to ISO 5351 is in the interval 200-900 ml/g, mechanically breaking agglomerates of fibers into smaller pieces, adjusting the concentration of fibers to 0.1-4 wt %, and subjecting the mixture to flotation to remove the non-cellulose fibers. Non-cellulosic fibers such as synthetic fibers can be removed very specifically without or essentially without removing cellulose fibers in the mixture. This gives a very high degree of removal and simultaneously the yield is kept high because no or only few cellulose fibers are removed.
1. A method for separation of fibers comprising the steps of:
a) providing a mixture of textile fibers comprising cellulose fibers and non-cellulose fibers,
b) reducing the cellulose chain length of the cellulose fibers so that the limiting viscosity number determined according to ISO 5351 is in the interval 200-900 ml/g,
c) subjecting the mixture of textile fibers to mechanical treatment to break agglomerates of textile fibers into smaller pieces,
d) adjusting the concentration of textile fibers in the mixture so that it is in the interval 0.1-4 wt % textile fibers calculated by weight, and
e) subjecting the mixture to flotation to remove the non-cellulose fibers.
2. The method according to claim 1 , wherein the chain length of the cellulose fibers is reduced by treatment with ozone under acid conditions below pH 6.
3. The method according to claim 1 , wherein the chain length of the cellulose fibers is reduced by treatment with oxygen under basic conditions above pH 10.
4. The method according to claim 1 , wherein step c) is performed before step b).
5. The method according to claim 1 , wherein step c) is performed by grinding.
6. The method according to claim 1 , wherein the concentration of textile fibers in the mixture is adjusted during step d) so that it is in the interval 0.2-1.5 wt % textile fibers calculated by weight.
7. The method according to claim 1 , wherein the flotation is performed by using more than one air diffuser nozzle, giving different bubble sizes.
8. The method according to claim 1 , wherein the mixture is filtered before the flotation in step e).
9. The method according to claim 8 , wherein the reject from a filter before the flotation is ground and filtered again.
10. The method according to claim 1 , wherein the mixture is made of textiles to be recycled.
11. The method according to claim 10 , wherein the mixture is treated in water under reducing conditions and a pH above 10 before step b).
12. The method according to claim 11 , wherein the reducing conditions are achieved by addition of dithionite anions.
13. The method according to claim 11 , wherein additional grinding is performed in wet state.
14. The method according to claim 1 , wherein the mixture after step e) is dewatered and dried.
15. The method according to claim 1 , wherein the mixture after step e) is used as a raw material in a Viscose manufacturing process.
16. The method according to claim 1 , wherein the mixture after step e) is used as a raw material in a Lyocell manufacturing process.
17. The method according to claim 1 , wherein at least one surfactant is added before the flotation in step e).
18. The method according to claim 1 , wherein an additional flotation step is performed before at least one of the steps c) and d).
19. The method according to claim 18 , wherein agglomerates separated in the flotation are subjected to mechanical treatment to disintegrate the agglomerates.
20. The method according to claim 1 , wherein the temperature during the flotation in step e) is in the interval 30-90° C. during at least a part of the flotation.