IP Library › Granted Patent US 12,220,689
Granted Patent B2
US 12,220,689 · App. 17/625,819 · Granted Feb 11, 2025

Process for producing catalysts for ammonia synthesis by reducing iron oxides

Inventors: Rene Eckert (Bad Aibling, DE); Stephan J. Reitmeier (Kirchseeon, DE); Stefan Maier (Grafing, DE)
Assignee: CLARIANT INTERNATIONAL LTD
B01J37/18B01J23/745B01J37/08C01C1/0411G01N21/75
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,220,689
App. No.
17/625,819
Granted
Feb 11, 2025
Kind
B2
Abstract

Disclosed is a process whereby completed catalysts can be produced from the iron oxides, and these catalysts can be activated and employed directly after activation for ammonia synthesis from synthesis gas, comprising for example a mixture of nitrogen and hydrogen. A process is also disclosed to produce pre-reduced catalyst precursors, which are first reduced under controlled conditions and subsequently passivated in an oxidizing atmosphere, before they are used in ammonia synthesis as catalysts. These pre-reduced catalysts can be activated significantly more quickly and under milder conditions than the iron oxides.

Claims (26)

1. A process for activating catalysts and catalyst precursors for ammonia synthesis, comprising the process steps of:

(A) performing a reduction of iron oxides using at least one reducing gas and by means of heating,

(B) measuring a concentration of water formed in a gas phase during the reduction by means of non-dispersive infrared spectroscopy (NDIR), and

(C) setting a flow rate of the at least one reducing gas and/or a heating rate as a function of the concentration of water formed.

2. The process as claimed in claim 1 , wherein in process step (C) the concentration of water determined in process step (B) is compared with a mandated limiting value for water.

3. The process as claimed in claim 2 , wherein in process step (C) at least one of the following substeps is carried out:

(C1) the heating rate is increased if the concentration of water determined in process step (B) is below a range around the mandated limiting value, or

(C2) the flow rate is increased and/or the heating rate is lowered if the concentration of water determined in process step (B) is above the range around the mandated limiting value, or

(C3) the flow rate and/or the heating rate are retained if the concentration of water determined in process step (B) is within the range around the mandated limiting value.

4. The process as claimed in claim 3 , wherein the range around the mandated limiting value is selected from the group of ranges consisting of: ±1000 ppmv.

5. The process as claimed in claim 3 , wherein the range around the mandated limiting value is selected from the group of ranges consisting of: ±600 ppmv.

6. The process as claimed in claim 2 , wherein the mandated limiting value is selected from a range between 3000 ppmv to 4000 ppmv.

7. The process as claimed in claim 1 , wherein process steps (A), (B) and (C) are carried out continuously.

8. The process as claimed in claim 1 , wherein the measurement of water formed during the reduction in process step (B) takes place in real time.

9. The process as claimed in claim 1 , wherein in process step (B) the concentration of water formed during the reduction is measured in a wavelength range from 2.6 to 3 μm.

10. The process as claimed in claim 1 , wherein in process step (A) the at least one reducing gas is a mixture comprising hydrogen and nitrogen and ammonia is formed during the reduction.

11. The process as claimed in claim 1 , wherein in process step (B) an NDIR device is used to measure the concentration of water formed and wherein absorption bands of ammonia in a wavelength range from 2.6 μm to 3 μm are subtracted out by means of calibration.

12. The process as claimed in claim 1 , wherein in process step (B) a concentration of ammonia formed in the course of the reduction is ascertained by means of NDIR.

13. The process as claimed in claim 1 , wherein ammonia and/or water formed in the course of the reduction are condensed by means of a condenser.

14. The process as claimed in claim 13 , wherein in process step (C) ammonia and water are present and are condensed as an aqueous ammonia solution, and the condenser is set to a temperature of at least 10 K over a freezing point of the aqueous ammonia solution.

15. The process as claimed in claim 1 , wherein the iron oxides used are magnetite, wüstite, or a combination thereof.

16. The process as claimed in claim 15 , wherein in process step (A) the iron oxides are wüstite and heating takes place to a temperature in the range from 370° C. to 400° C.

17. The process as claimed in claim 1 , wherein process step (A) is set to a temperature in the range from 360° C. to 450° C.

18. The process as claimed in claim 1 , wherein in process step (B) the at least one reducing gas is a mixture comprising hydrogen and nitrogen and an aqueous ammonia solution is condensed out during the reduction.

19. The process as claimed in claim 1 , additionally comprising a process step (D), wherein the catalysts and/or catalyst precursors from process step (C) are exposed to an oxidizing gas to form a protective layer on the catalysts and/or catalyst precursors.

20. The process as claimed in claim 1 , wherein the iron oxides used is wüstite.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jan 10, 2022
From: ECKERT, RENE; REITMEIER, STEPHAN J.; MAIER, STEFAN
To: CLARIANT INTERNATIONAL LTD
Reel/Frame 058590/0139 →
Priority Claims (1)
DE 10 2019 120 012.1 · Jul 24, 2019 · national
Continuity (1)
Related Publication 20220250048A1 · Aug 11, 2022
References Cited (22)
US 4703030A · Khader · 1987 [cited by examiner]
US 5093303A · Tamaura · 1992 [cited by examiner]
US 7091043B2 · Itou · 2006 [cited by applicant]
US 10287173B2 · Malmali · 2019 [cited by applicant]
US 11054406B2 · Virtanen · 2021 [cited by applicant]
CH 681392 · 1993 [cited by applicant]
CN 1114239 · 1996 [cited by applicant]
CN 105435861 · 2016 [cited by applicant]
RU 2263538 · 2005 [cited by applicant]
SU 1077624 · 1985 [cited by applicant]
A, Baranski et al., “Kinetics of Reduction of an Iron Catalyst for Ammonia Synthesis.” Reaction Kinetics and Catalysis Letters, vol. 15, No. 2, pp. 285-291. (Year: 1980). [cited by examiner]
English translation of the Written Opinion for PCT/EP2020/069218. (Year: 2020). [cited by examiner]
600Kt/a Ammonia Synthesis Unit, Ammonia Synthesis Catalyst Reduction Summary, M-Sized Nitrogenous Fertilizer Process,, 2018, p. 46-49, 2018., No. 2. [cited by applicant]
Selection and Reduction of New Type of Ammonia Synthesis Catalyst, Fertilizer Industry,, 2007, No. 4, p. 7-11, 2007., 34. [cited by applicant]
Shu Jizhao, The Reduction Rate of A110-2 Ammonia Catalyst, Journal of Zhejiang Institute of Technology, 1989, p. 41-47, 03. [cited by applicant]
W.C. Lin et al, Determination of Water Vapor in a Small air sample by a Nondispersive Infrared Gas Analyzer, 1997, p. 278-281, 32, No. 2. [cited by applicant]
A. Baranski et al., Applied Catalysis 40 (1988), 67-72 “Simultaneous effect of phase composition and water vapour on the reduction of iron catalyst for ammonia synthesis”. [cited by applicant]
A. Baranski et al., Applied Catalysis 3 (1982) 201-206 “The effect of water on the reduction of an iron catalyst for ammonia synthesis”. [cited by applicant]
Chen, Z., Lu, C., Sensor Letters 3 (2005) 274-295 “Humidity Sensors: A Review of Materials and Mechanisms”. [cited by applicant]
Nakatani S, (2003) SAE Technical Papers, “Development of a gaseous compounds measurements system for fuel cell powertrain” SAE World Congress, Mar. 3-6, 2003 SAE International. [cited by applicant]
Stohlberg-Rohr, T. et al., NDIR humidity measurement, 2011, 1058-1061. [cited by applicant]
Turner, K., Schaffer, C., “Ammonia Synthesis Loop Water Exposure: Identification and Re-reduction of AmoMax®-10” Ammonia Technical Manual, 2016, 119-122. [cited by applicant]