The present invention relates to preceramic polymer grafted nanoparticles and as well as methods of making and using same. Advantages of such preceramic polymer grafted nanoparticles include, reduced out gassing, desired morphology control and desirable, distinct rheological properties that are not found in simple mixtures. As a result, Applicants' preceramic polymer grafted nanoparticles can be used to provide significantly improved, items including but not limited to hypersonic vehicles, jets, rockets, mirrors, signal apertures, furnaces, glow plugs, brakes, and armor.
1. A process of making a preceramic polymer grafted nanoparticle comprising: combining a carbosilane monomer comprising at least one silane moiety and at least one vinyl moiety and/or a cyclic carbosilane monomer, with a core comprising a material selected from the group consisting of Hydrogen, Lithium, Beryllium, Boron, Carbon, Nitrogen, Oxygen, Fluorine, Sodium, Magnesium, Aluminum, Silicon, Phosphorus, Sulfur, Chlorine, Potassium, Calcium, Scandium, Titanium, Vanadium, Chromium, Manganese, Iron, Cobalt, Nickel, Copper, Zinc, Gallium, Germanium, Arsenic, Selenium, Bromine, Strontium, Yttrium, Zirconium, Niobium, Molybdenum, Technetium, Ruthenium, Rhodium, Palladium, Silver, Cadmium, Indium, Tin, Antimony, Tellurium, Iodine, Cesium, Barium, Lanthanum, Cerium, Praseodymium, Neodymium, Promethium, Samarium, Europium, Gadolinium, Terbium, Dysprosium, Holmium, Erbium, Thulium, Ytterbium, Lutetium, Hafnium, Tantalum, Tungsten, Rhenium, Osmium, Iridium, Platinum, Gold, Mercury, Thallium, Lead, Bismuth, Polonium, Radium, Actinium, Thorium, Protactinium, Uranium, Neptunium, Plutonium, Americium, and mixtures thereof, said core having an outer surface, said outer surface being functionalized and allowing said core and said monomer to react for 24 hours to 72 hours at a temperature of from about 20° C. to 80° C., and at a pressure of from about 0.1 atm to about 100 atm.
2. The process of making a preceramic polymer grafted nanoparticle according to claim 1 , wherein:
a) said carbosilane monomer is selected from the group consisting of allyldimethylsilane, vinyldimethylsilane, allyldichlorosilane, vinyldichlorosilane, 1,1,-dimethylsilylcyclobutane, 1,1-dichlorosilylcyclobutane, 1,1-dimethyldisilylcyclobutane, 1,1-dichlorodisilylcyclobutane and mixtures thereof; and
b) said core comprises a ceramic and said core's functionalization comprises a silane moiety comprising a catalyst and/or a vinyl moiety comprising a catalyst.
3. The process of making a preceramic polymer grafted nanoparticle according to claim 2 , wherein said core comprises a nonoxide ceramic and said catalyst is platinum and/or a carbanion.
4. The process of making a preceramic polymer grafted nanoparticle according to claim 3 , wherein said core comprises SiC, ZrC, HfC, Si 3 N 4 , ZrN, HfN, ZrB 2 , HfB 2 , and mixtures thereof.
5. The process according to claim 1 , wherein said core and said monomer are combined and allowed to react at a temperature of from about 55° C. to 70° C. and at a from about 0.5 atm to about 10 atm.
6. A process of making a preceramic polymer grafted nanoparticle comprising: combining a carbosilane monomer comprising at least one silane moiety and at least one vinyl moiety and/or a cyclic carbosilane monomer, with a core comprising a material selected from the group consisting of Hydrogen, Lithium, Beryllium, Boron, Carbon, Nitrogen, Oxygen, Fluorine, Sodium, Magnesium, Aluminum, Silicon, Phosphorus, Sulfur, Chlorine, Potassium, Calcium, Scandium, Titanium, Vanadium, Chromium, Manganese, Iron, Cobalt, Nickel, Copper, Zinc, Gallium, Germanium, Arsenic, Selenium, Bromine, Strontium, Yttrium, Zirconium, Niobium, Molybdenum, Technetium, Ruthenium, Rhodium, Palladium, Silver, Cadmium, Indium, Tin, Antimony, Tellurium, Iodine, Cesium, Barium, Lanthanum, Cerium, Praseodymium, Neodymium, Promethium, Samarium, Europium, Gadolinium, Terbium, Dysprosium, Holmium, Erbium, Thulium, Ytterbium, Lutetium, Hafnium, Tantalum, Tungsten, Rhenium, Osmium, Iridium, Platinum, Gold, Mercury, Thallium, Lead, Bismuth, Polonium, Radium, Actinium, Thorium, Protactinium, Uranium, Neptunium, Plutonium, Americium, and mixtures thereof, said core having an outer surface, said outer surface being functionalized by a process selected from silanization, phosphination; and/or sulfonization followed by oxidative addition of platinum to said silane moiety and/or reacting an alkyllithium with said vinyl moiety.
7. The process of making a preceramic polymer grafted nanoparticle according to claim 6 , wherein:
a) said carbosilane monomer is selected from the group consisting of allyldimethylsilane, vinyldimethylsilane, allyldichlorosilane, vinyldichlorosilane, 1,1,-dimethylsilylcyclobutane, 1,1-dichlorosilylcyclobutane, 1,1-dimethyldisilylcyclobutane, 1,1-dichlorodisilylcyclobutane and mixtures thereof; and
b) said core comprises a ceramic and said core's functionalization comprises a silane moiety comprising a catalyst and/or a vinyl moiety comprising a catalyst.
8. The process of making a preceramic polymer grafted nanoparticle according to claim 7 , wherein said core comprises a nonoxide ceramic and said catalyst is platinum and/or a carbanion.
9. The process of making a preceramic polymer grafted nanoparticle according to claim 8 , wherein said core comprises SiC, ZrC, HfC, Si 3 N 4 , ZrN, HfN, ZrB 2 , HfB 2 , and mixtures thereof.
10. The process of making a preceramic polymer grafted nanoparticle according to claim 6 , wherein said core and said monomer are combined and allowed to react for 1 hour to 168 hours.
11. The process of making a preceramic polymer grafted nanoparticle according to claim 10 , wherein said core and said monomer are combined and allowed to react for 24 hours to 72 hours at a temperature of from about 20° C. to 80° C., and at a pressure of from about 0.1 atm to about 100 atm.
12. The process of making a preceramic polymer grafted nanoparticle according to claim 11 , wherein said core and said monomer are combined and allowed to react at a temperature of from about 55° C. to 70° C. and at a from about 0.5 atm to about 10 atm.