Polyphenylene sulfide resin composition and molded article
A polyphenylene sulfide resin composition includes a blend of the following: 100 parts by weight of a polyphenylene sulfide resin (A); 100 to 250 parts by weight of a modified cross-section glass fiber (B); and 25 to 150 parts by weight of a non-fibrous inorganic filler (C) satisfying the following (C-a) and (C-b): (C-a) having a Mohs hardness of more than 2 and less than 4, and (C-b) having a melting point or softening point of 380° C. or more; wherein the ratio X/Y of the mass X of the modified cross-section glass fiber (B) to the mass Y of the non-fibrous inorganic filler (C) is more than 1 and less than 7.
1. A polyphenylene sulfide resin composition comprising a blend of:
100 parts by weight of a polyphenylene sulfide resin (A) having a minimum melt flow rate of 1000 g/10 min;
100 to 250 parts by weight of a modified cross-section glass fiber (B) having a flattening ratio of 1.3 to 10; and
25 to 150 parts by weight of a non-fibrous inorganic filler (C);
wherein the non-fibrous inorganic filler (C): has a Mohs hardness of more than 2 and less than 4, has a melting point or softening point of 380° C. or more, and is selected from the group consisting of mica, carbonates, and sulfates;
wherein a ratio X/Y of a blending weight X of said modified cross-section glass fiber (B) to a blending weight Y of said non-fibrous inorganic filler (C) is more than 1 and less than 7, such that the polyphenylene sulfide resin composition has low linear expansion, low anisotropy, and low swelling properties;
wherein the low linear expansion corresponds to: a maximum coefficient of linear expansion in the machine direction (MD) of 1.9×10 −5 /K and a maximum coefficient of linear expansion in the traverse direction (TD) of 1.8×10 −5 /K;
wherein the low anisotropy corresponds to: a maximum difference between the coefficient of linear expansion in the MD and the coefficient of linear expansion in the TD of 0.1 ×10 −5 K, and a maximum creep ratio of 1.5; and
wherein the low swelling properties correspond to: a maximum swelling ratio in the MD of 0.06% and a maximum swelling ratio in the TD of 0.07%.
2. The polyphenylene sulfide resin composition according to claim 1 , wherein the flattening ratio is 1.5 to 7.
3. The polyphenylene sulfide resin composition according to claim 1 , wherein the ratio X/Y is more than 1 and less than 5.
4. The polyphenylene sulfide resin composition according to claim 1 , wherein said non-fibrous inorganic filler (C) is calcium carbonate.
5. The polyphenylene sulfide resin composition according to claim 1 , wherein
the carbonates are selected from calcium carbonate, magnesium carbonate, dolomite, and the sulfates are selected from calcium sulfate and barium sulfate.
6. A molded article composed of said polyphenylene sulfide resin composition according to claim 1 .
7. A housing part comprising the molded article according to claim 6 .