Beverage container body, can end, and material therefor
In a method of forming a beverage container, a can body is formed from a metal alloy. A can end is formed from a substantially compositionally identical metal alloy. The metal alloy is a heat treatable aluminum alloy. The heat treatable aluminum alloy is produced from up to 100% recycled aluminum material.
1. A method of forming a beverage container comprising the steps of:
forming a can body from a metal alloy;
forming a can end from a substantially compositionally identical metal alloy; and
heat treating the metal alloy after the step of forming the can body,
wherein the metal alloy and the substantially compositionally identical metal alloy are selected from the group consisting of a 4XXX, a 6XXX, a 2XXX, and a 7XXX aluminum alloy.
2. The method of claim 1 further comprising the step of heat treating the substantially compositionally identical metal alloy.
3. The method of claim 2 wherein the heat treating step the substantially compositionally identical metal alloy is performed prior to the the forming the can end step.
4. The method of claim 1 wherein the step of heat treating the metal alloy is an age hardening performed between 225° F. and 350° F.
5. The method of claim 4 further comprising the steps of:
casting the metal alloy in a liquid state into one of a solid slab, plate, or sheet;
cold rolling a thin metal sheet to reduce a thickness of the thin metal sheet into a cold rolled metal alloy sheet;
coiling the cold rolled metal alloy sheet;
performing a solid solution heat treatment on the metal alloy prior to forming the can body.
6. The method of claim 5 wherein the performing the solid solution heat treatment step is performed one of before the cold rolling, during the cold rolling, or after the cold rolling step.
7. The method of claim 6 further comprising the steps of:
reheating the slab, plate or sheet into a reheated slab, plate of sheet; and
hot rolling the reheated slab, plate or sheet to reduce a thickness of the reheated slab, plate, or sheet into the thin metal sheet.
8. A method of forming a beverage container can body comprising the steps of:
forming a shallow cup from a sheet of a metal alloy;
reforming the shallow cup into a pre-body having an open end, an elongated cylindrical sidewall, and an integral bottom;
reforming the pre-body into a can body comprising a circumferential shoulder of reducing diameter, a neck, and a radially outwardly curled flange;
aging the can body at an aging temperature greater than an ambient temperature for a duration of time,
wherein the metal alloy is selected from the group consisting of a 4XXX, a 6XXX, a 2XXX, and a 7XXX aluminum alloy.
9. The method of claim 8 wherein the aging temperature is between 100° F. and 600° F.
10. The method of claim 9 wherein the aging temperature is between 150° F. and 500° F.