Wound dressing based on polymeric mixture of cellulose acetate and hyaluronic acid embedded with copper oxide and magnesium oxide nanoparticles
Wound dressings fabricated from a polymeric mixture of cellulose acetate and hyaluronic acid embedded with copper oxide and/or magnesium oxide nanoparticles and a method of making the wound dressing. The method includes combining hyaluronic acid and deionized water to form a first mixture, combining cellulose acetate and acetone to form a second mixture, combining the first and second mixtures to form a third mixture of hyaluronic acid, cellulose acetate, deionized water and acetone, separately adding at least one of a copper acetate solution and a magnesium chloride solution to the third mixture to form a fourth mixture, adding sodium hydride to the fourth mixture to form a final mixture, and drying the final mixture to form a film used for the wound dressing. Different weights of copper oxide and magnesium oxide can be chosen to achieve a certain morphological appearance. The wound dressing is a promising option for wound healing.
1. A method for making a wound dressing, the method comprising:
combining hyaluronic acid and deionized water to form a first mixture;
combining cellulose acetate and acetone to form a second mixture;
combining the first and second mixtures to form a third mixture of hyaluronic acid, cellulose acetate, deionized water, and acetone;
separately adding at least one of a copper acetate solution and a magnesium chloride solution to the third mixture to form a fourth mixture;
adding sodium hydride to the fourth mixture under an ultrasonic bath to form a final mixture; and
drying the final mixture to form a film used as the wound dressing;
wherein the ratio of hyaluronic acid to deionized water in the first mixture is about 1:10 (g/mL);
wherein the ratio of cellulose acetate to acetone in the second mixture is about 1:10 (g/mL).
2. The method of making a wound dressing according to claim 1 , wherein the ultrasonic bath lasts for a minimum of 30 minutes.
3. The method of making a wound dressing according to claim 1 , wherein the third mixture is stirred until a clear solution is obtained.
4. The method of making a wound dressing according to claim 1 , wherein both the copper acetate solution and the magnesium chloride solution are added to the third mixture to form the fourth mixture.