Fiber-reinforced resin molding material and method for manufacturing same, and fiber-reinforced resin molded article
A fiber-reinforced resin molding material may include a reinforcement fiber sheet of basis weight 200 to 3,000 g/m 2 is impregnated with a resin composition to a resin composition of 25 to 55 vol. % of 100% total fiber-reinforced resin molding material mass. A thickness from a first surface to a position of 10 mass % resin composition being d1 (μm), and a thickness from an opposite surface to a position occupied by 10 mass % resin composition being d2 (μm) giving an absolute value, |d1−d2|, of 50 μm or less. A method for manufacturing such a material may include: impregnating a reinforcement fiber sheet including (i) a unidirectional sheet with plural continuous parallel fibers, (ii) a woven fabric of woven continuous fibers, and/or (iii) a non-crimp fabric containing continuous fibers of resin composition having an initial viscosity of ≤1 Pa·s and a viscosity of 5,000 to 150,000 Pa·s after 7 days at 25° C.
1. A method for manufacturing a fiber-reinforced resin molding material, the method comprising:
coating a resin composition on one surface of each of a first carrier film and a second carrier film; and
impregnating a reinforced fiber sheet with the resin composition after the coating by overlaying the first and second carrier films so that the surfaces coated by the resin composition face each other and in a state that the reinforced fiber sheet is put between the first and second carrier films, and conveying while pressing with a plurality of pressing rolls,
wherein the reinforced fiber sheet is one selected from the group consisting of (i) a woven fabric in which continuous fibers are woven and (ii) a non-crimp fabric comprising continuous fibers,
wherein the reinforcement fiber sheet has a basis weight in a range of from 200 to 3,000 g/m 2 ,
wherein the reinforced fiber sheet is impregnated so that an amount of the resin composition in the fiber-reinforced resin molding material is in a range of from 25 to 55 vol. %, and
wherein, when a total amount of the resin composition contained in the fiber-reinforced resin molding material is 100 mass %, a thickness from a first surface in a thickness direction of the fiber-reinforced resin molding material to a position occupied by 10 mass % of the resin composition is represented by d1 (μm), and a thickness from a second surface opposite to the first surface to a position occupied by 10 mass % of the resin composition is represented by d2 (μm), an absolute value (|d1−d2|) of a difference between d1 and d2 is 50 μm or less.
2. The method of claim 1 , wherein the resin composition has an initial viscosity of 1 Pa·s or less and a viscosity in a range of from 5,000 to 150,000 Pas after leaving for 7 days at 25° C.
3. The method of claim 1 , wherein the resin composition comprises at least one thermosetting resin selected from the group consisting of an epoxy resin, a vinyl ester resin, an unsaturated polyester resin, a polyimide resin, a maleimide resin, and a phenol resin.
4. The method of claim 3 , wherein the resin composition comprises a vinyl ester resin.
5. The method of claim 1 , wherein the continuous fibers are continuous fibers selected from the group consisting of carbon fibers, glass fibers, and aramid fibers.
6. The method of claim 1 , wherein the reinforced fiber sheet is a non-crimp fabric comprising continuous fibers.
7. The method of claim 1 , wherein R, representing a ratio of a sum of d1 and d2 to the basis weight of the reinforcement fiber sheet, is in a range of from 0.2 to 0.5.
8. The method of claim 1 , wherein d1 and/or d2 is in a range of from 5 to 750 μm.
9. The method of claim 1 , wherein the resin composition has an initial viscosity of 1 Pa·s or less and a viscosity in a range of from 5,000 to 150,000 Pas after leaving for 7 days at 25° C., and
wherein the resin composition comprises at least one thermosetting resin selected from the group consisting of an epoxy resin, a vinyl ester resin, an unsaturated polyester resin, a polyimide resin, a maleimide resin, and a phenol resin.
10. The method of claim 1 , wherein the resin composition has an initial viscosity of 1 Pa·s or less and a viscosity in a range of from 5,000 to 150,000 Pa·s after leaving for 7 days at 25° C., and
wherein the resin composition comprises a vinyl ester resin.
11. The method of claim 1 , wherein the resin composition has an initial viscosity of 1 Pa·s or less and a viscosity in a range of from 5,000 to 150,000 Pas after leaving for 7 days at 25° C., and
wherein the reinforced fiber sheet is a non-crimp fabric comprising continuous fibers.
12. The method of claim 1 , wherein the resin composition has an initial viscosity of 1 Pa·s or less and a viscosity in a range of from 5,000 to 150,000 Pas after leaving for 7 days at 25° C.,
wherein the reinforced fiber sheet is a non-crimp fabric comprising continuous fibers, and
wherein the resin composition comprises a vinyl ester resin.