Method for fabricating an environmental barrier coating on a ceramic matrix composite
A method of fabricating a coating includes providing a ceramic matrix composite that includes SiC fibers disposed in a SiC matrix, depositing a base slurry on the ceramic matrix composite, wherein the base slurry contains powders of a metal oxide, at least one of silicon carbide, silicon nitride, or free silicon, and barium-magnesium-aluminosilicate in a first carrier fluid, drying the deposited base slurry to produce a base green layer, depositing a transition slurry on the base green layer, wherein the transition slurry contains powders of a metal oxide, at least one of silicon carbide, silicon nitride, or free silicon, at least one of zirconium carbide, zirconium nitride, or zirconium oxide, and barium-magnesium-aluminosilicate in a second carrier fluid, drying the deposited transition slurry to produce a transition green layer, and forming a consolidated coating on the ceramic matrix composite by heating the base green layer and the at least one transition green layer to cause chemical reactions that convert the powders to metal-silicon-oxygen rich phase and metal-zirconium-oxygen rich phase.
1. A method of fabricating a coating, the method comprising:
providing a ceramic matrix composite that includes SiC fibers disposed in a SiC matrix;
depositing a base slurry on the ceramic matrix composite, wherein the base slurry contains, in parts by weight, 35-60 of a metal oxide powder, 5-20 of at least one of silicon carbide powder, silicon nitride powder, or free silicon powder, and 0.2-10 of barium-magnesium-aluminosilicate powder in a first carrier fluid;
drying the deposited base slurry to produce a base green layer;
depositing a transition slurry on the base green layer, wherein
the transition slurry contains, in parts by weight, 35-60 of a metal oxide powder, an amount X 1 of at least one of silicon carbide powder, silicon nitride powder, or free silicon powder, an amount X 2 of at least one of zirconium carbide powder, zirconium nitride powder, or zirconium oxide powder, and 0.2-10 of barium-magnesium-aluminosilicate powder in a second carrier fluid,
the total amount of X 1 +X 2 is 5-20, and
the amount X 1 is decreased and the amount of X 2 is increased through the deposition of the transition slurry;
drying the deposited transition slurry to produce a transition green layer; and
forming a consolidated coating on the ceramic matrix composite by heating the base green layer and the transition green layer.
2. The method as recited in claim 1 , wherein through the deposition of the transition slurry the amount X 1 is decreased to, and then held at, a non-zero amount, followed by decreasing the non-zero amount to zero.
3. The method as recited in claim 1 , wherein the amount X 1 is decreased and the amount of X 2 is increased cooperatively such that through the deposition of the transition slurry X 1 +X 2 is constant.
4. The method as recited in claim 1 , wherein the amount X 1 is linearly decreased and the amount of X 2 is linearly increased.
5. The method as recited in claim 1 , wherein the metal oxide of the base slurry and the transition slurry is selected from the group consisting of HfO 2 , Y 2 O 3 , Yb 2 O 3 , Lu 2 O 3 , oxides of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and combinations thereof.
6. The method as recited in claim 5 , further comprising applying a topcoat on the consolidated coating, the topcoat being selected from the group consisting of HfO 2 , Gd 2 Zr 2 O 7 , and combinations thereof.
7. The method as recited in claim 1 , wherein the metal oxide of at least one of the base slurry or the transition slurry is HfO 2 .
8. The method as recited in claim 1 , wherein the metal oxide of the base slurry and the transition slurry is HfO 2 .