Method for manufacturing glass plate, method for manufacturing magnetic-disk glass substrate, and method for manufacturing magnetic disk
Chamfering processing for chamfering an edge face of a disk-shaped glass plate includes a step of disposing the glass plate such that a portion of the glass plate is disposed in a heating space for heating the glass plate and the remaining portion is disposed outside the heating space; and a step of softening a portion of the edge face of the glass plate by irradiating a circumferential portion of the edge face with a laser beam outside the heating space while rotating the glass plate in one direction around the center of the glass plate, and heating the softened portion of the edge face that has reached the heating space through the rotation.
1. A method for manufacturing a glass plate, the method comprising:
chamfering processing for chamfering an edge face of a disk-shaped glass plate,
the chamfering processing including,
disposing the glass plate such that a portion of the glass plate is disposed in a heating space for heating the glass plate and the remaining portion is disposed outside the heating space, and
softening a portion of the edge face of the glass plate by irradiating a circumferential portion of the edge face with a laser beam outside the heating space while rotating the glass plate in one direction around a center of the glass plate, and heating the softened portion of the edge face that has reached the heating space through the rotation,
wherein a region of a main surface of the glass plate that is disposed in the heating space is more than or equal to half the area of the main surface of the glass plate.
2. The method for manufacturing a glass plate according to claim 1 ,
wherein the rotational speed of the glass plate around the center is lower than a rotational speed set value that is set according to a heating area of the main surface of the glass plate that is defined as a result of the main surface being disposed in the heating space.
3. The method for manufacturing a glass plate according to claim 2 ,
wherein V< 1/50·A is satisfied where the rotational speed of the glass plate is V [mm/s] and the heating area is A [mm 2 ].
4. The method for manufacturing a glass plate according to claim 1 ,
wherein the glass plate has an average coefficient of linear thermal expansion of 100×10 −7 /° C. or less in a temperature range of 100° C. to 300° C.
5. The method for manufacturing a glass plate according to claim 1 ,
wherein an irradiation position where the edge face is irradiated with the laser beam is defined such that the softened portion of the edge face irradiated with the laser beam starts to enter the heating space before the temperature of the softened portion falls below a temperature that is lower than a strain temperature of the glass plate by 50° C.
6. The method for manufacturing a glass plate according to claim 1 ,
wherein the softened portion of the edge face is heated in the heating space at a temperature that is lower than a glass transition temperature of the glass plate.
7. The method for manufacturing a glass plate according to claim 1 , further comprising
grinding or polishing the main surface of the glass plate without polishing the heated edge face.
8. The method for manufacturing a glass plate according to claim 1 ,
wherein the glass plate is a blank of a magnetic-disk glass plate.
9. A method for manufacturing a magnetic-disk glass substrate, comprising
grinding or polishing the main surface of the glass plate after the glass plate is manufactured using the method for manufacturing a glass plate according to claim 8 .
10. A method for manufacturing a magnetic disk,
wherein a magnetic film is formed on a main surface of a magnetic-disk glass substrate after the magnetic-disk glass substrate is manufactured using the method for manufacturing a magnetic-disk glass substrate according to claim 9 .