Coated steel sheet

Inventors: Tiago Machado Amorim (Longeville les Metz, FR); Christian Allely (Metz, FR); Raisa Grigorieva (Metz, FR); David Dussaussois (Homecourt, FR)
Assignee: ArcelorMittal
C21D9/46B21D22/022B32B15/012C21D1/673C21D6/004C21D6/005C21D6/008C21D8/005C22C21/02C22C21/10C23C2/12C23C2/26C23C2/261C23C2/28C23C2/29C23C2/40C21D2211/002C21D2211/005C21D2211/008
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,351,886
App. No.
17/463,142
Granted
Jul 8, 2025
Kind
B2
Abstract

A pre-coated steel sheet includes a steel sheet precoated with a metallic coating, the coating including: 2.0 to 24.0% by weight of zinc; 1.1 to 7.0% by weight of silicon; optionally from 0.5 to 3.0% by weight of magnesium when the amount of silicon is between 1.1 and 4.0%, and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight, a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath; a ratio Al/Zn by weight greater than 2.9, wherein the coating does not include In and the coating does not include Sn.

Claims (77)

1. A heat treatable coated steel sheet, comprising a steel sheet coated with a metallic coating, the coating including:

2.0 to 24.0% by weight of zinc;

1.1 to 2% by weight of silicon;

and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight,

a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath;

a ratio Al/Zn by weight greater than 2.9;

a ratio Zn/Si by weight between 2.9 and 8; and

wherein the coating is free from magnesium, does not include In and does not include Sn;

wherein the steel sheet has a base with a composition by weight percentage including 0.20%≤C≤0.25%; 0.15%≤Si≤0.35%; 1.10%≤Mn≤1.40%; 0%≤Cr≤0.30%; 0%≤Mo≤0.35%; 0%≤P≤0.025%; 0%≤S≤0.005%; 0.020%≤Ti≤0.060%; 0.020%≤Al≤0.060%; 0.002%≤B≤0.004%, a balance of the steel sheet base composition being iron and unavoidable impurities from the manufacture of steel;

wherein the coated steel sheet is heat treatable in a furnace under non protective atmosphere at an austenitization temperature between 84° and 950° C. and a dwell time between 1 and 12 minutes and is suitable for hot forming at a temperature between 60° and 830° C.

2. The coated steel sheet according to claim 1 , wherein the coating comprises at least one of the additional elements chosen from Pb, Ni, Zr, or Hf.

3. The coated steel sheet according to claim 1 , wherein the ratio Al/Zn is between 5 and 9.

4. The coated steel sheet according to claim 1 , wherein the coating comprises from 1.5 to 2% 3.5% by weight of silicon.

5. The coated steel sheet according to claim 4 , wherein the coating comprises from 5.0 to 10.0% by weight of zinc.

6. The coated steel sheet according to claim 1 , wherein the coating comprises from 5.0 to 19.0% by weight of zinc.

7. The coated steel sheet according to claim 1 , wherein the coating comprises from 5.0 to 15.0% by weight of zinc.

8. The coated steel sheet according to claim 1 , wherein the coating comprises from 5.0 to 10.0% by weight of zinc.

9. The coated steel sheet according to claim 1 , wherein the coating comprises greater than 71% by weight of aluminum.

10. The coated steel sheet according to claim 1 , wherein the coating comprises greater than 76% by weight of aluminum.

11. The coated steel sheet according to claim 1 , wherein a thickness of the coating is between 5 and 50 μm.

12. The coated steel sheet according to claim 11 , wherein the thickness is between 10 and 35 μm.

13. The coated steel sheet according to claim 11 , wherein the thickness is between 12 and 18 μm.

14. The coated steel sheet according to claim 11 , wherein the thickness is between 26 and 31 μm.

15. The coated steel sheet according to claim 1 , wherein the coating does not comprise elements selected among Cr, Mn, Ti, Ce, La, Nd, Pr, Ca, Bi, In, Sn and Sb or combinations thereof.

16. The coated steel sheet according to claim 1 wherein the steel sheet has a base made of 22MnB5 steel.

17. The coated sheet according to claim 1 , wherein the coated steel sheet, after said heat treatment and after a subsequent hot stamping, exhibits microcracks, and no microcrack has a depth greater than 50 μm.

18. The coated sheet according to claim 1 , wherein the coated steel sheet, after said heat treatment and after a subsequent hot stamping, exhibits microcracks having a depth between 0 and 50 μm.

19. The coated sheet according to claim 1 , wherein the ratio Al/Zn is 5.6 or less.

20. The coated sheet according to claim 1 , wherein the metallic coating has a ratio Al/Zn between 5.3 and 8.8%, and a ratio Zn/Si by weight between 3 and 7.5.

21. A heat treatable coated steel sheet, comprising a steel sheet coated with a metallic coating, the coating including:

2.0 to 24.0% by weight of zinc;

1.1 to 2% by weight of silicon;

and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight,

a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath;

a ratio Al/Zn by weight greater than 2.9;

a ratio Zn/Si by weight between 2.9 and 8; and

wherein the coating is free from magnesium, does not include In and does not include Sn;

wherein the steel sheet has a base with a composition by weight percentage including: 0.24%≤C≤0.38%; 0.40%≤Mn≤3%; 0.10%≤Si≤0.70%; 0.015%≤Al≤0.070%; 0%≤Cr≤2%; 0.25%≤Ni≤2%; 0.020%≤Ti≤0.10%; 0%≤Nb≤0.060%; 0.0005%≤B≤0.0040%; 0.003%≤N≤0.010%; 0.0001%≤S≤0.005%; 0.0001%≤P≤0.025%; it being understood that the contents of titanium and nitrogen satisfy Ti/N>3.42, and that the contents of carbon, manganese, chromium and silicon satisfy 2.6C+Mn/5.3+Cr/13+Si/15≥1.1%, the composition optionally comprising one or more of the following: 0.05%≤Mo≤0.65%; 0.001%≤W≤0.30%; 0.0005%≤Ca≤0.005%, a balance of the steel sheet base composition being iron and unavoidable impurities from manufacture;

wherein the coated steel sheet is heat treatable in a furnace under non protective atmosphere at an austenitization temperature between 84° and 950° C. and a dwell time between 5 and 10 minutes and is suitable for hot forming at a temperature between 60° and 830° C.

22. The coated sheet according to claim 21 , wherein the coating comprises greater than 71% by weight of aluminum.

23. The coated sheet according to claim 22 , wherein the coating comprises greater than 76% by weight of aluminum.

24. The coated sheet according to claim 21 , wherein the coated steel sheet, after said heat treatment and after a subsequent hot stamping, exhibits microcracks, and no microcrack has a depth greater than 50 μm.

25. The coated sheet according to claim 21 , wherein the ratio Al/Zn is 5.6 or less.

26. The coated sheet according to claim 21 , wherein the metallic coating has a ratio Al/Zn between 5.3 and 8.8%, and a ratio Zn/Si by weight between 3 and 7.5.

27. A heat treatable coated steel sheet, comprising a steel sheet coated with a metallic coating, the coating including:

2.0 to 24.0% by weight of zinc;

1.1 to 2% by weight of silicon;

and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight,

a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath;

a ratio Al/Zn by weight greater than 2.9;

a ratio Zn/Si by weight between 2.9 and 8; and

wherein the coating is free from magnesium, does not include In and does not include Sn;

wherein the steel sheet has a base with a composition by weight percentage including: 0.040%≤C≤0.100%; 0.80%≤Mn≤2.00%; 0%≤Si≤0.30%; 0%≤S≤0.005%; 0%≤P≤0.030%; 0.010%≤Al≤0.070%; 0.015%≤Nb≤0.100%; 0.030%≤Ti≤0.080%; 0%≤N≤0.009%; 0%≤Cu≤0.100%; 0%≤Ni≤0.100%; 0%≤Cr≤0.100%; 0%≤Mo≤0.100%; 0%≤Ca≤0.006%, a balance of the steel sheet base composition being iron and unavoidable impurities from manufacture;

wherein the coated steel sheet is heat treatable in a furnace under non protective atmosphere at an austenitization temperature between 84° and 950° C. and a dwell time between 5 and 10 minutes and is suitable for hot forming at a temperature between 60° and 830° C.

28. The coated sheet according to claim 27 , wherein the coated steel sheet, after said heat treatment and after a subsequent hot stamping, exhibits microcracks, and no microcrack has a depth greater than 50 μm.

29. The coated sheet according to claim 27 , wherein the ratio Al/Zn is 5.6 or less.

30. The coated sheet according to claim 27 , wherein the metallic coating has a ratio Al/Zn between 5.3 and 8.8%, and a ratio Zn/Si by weight between 3 and 7.5.

31. A heat treatable coated steel sheet, comprising a steel sheet coated with a metallic coating, the coating including:

2.0 to 24.0% by weight of zinc;

1.1 to 7.0% by weight of silicon;

and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight,

a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath;

a ratio Al/Zn by weight between 8.6 and 9;

a ratio Zn/Si by weight between 2.9 and 8; and

wherein the coating is free from magnesium, does not include In and does not include Sn,

the thickness of the coating is between 10 and 35 μm, and

the coated steel sheet is heat treatable in a furnace under non protective atmosphere at an austenitization temperature between 84° and 950° C. and a dwell time between 1 and 12 minutes and is suitable for hot forming at a temperature between 60° and 830° C.

32. A heat treatable coated steel sheet, comprising a steel sheet coated with a metallic coating, the coating including:

15 to 24.0% by weight of zinc;

1.1 to 7.0% by weight of silicon;

and optionally additional elements chosen from Pb, Ni, Zr or Hf, a content by weight of each additional element being less than 0.3% by weight,

a balance being aluminum, unavoidable impurities and residual elements resulting from feeding ingots or from a passage of the steel sheet in a molten bath;

a ratio Al/Zn by weight greater than 2.9;

a ratio Zn/Si by weight between 5 and 8; and

wherein the coating is free from magnesium, does not include In and does not include Sn,

the thickness of the coating is between 10 and 35 μm, and

the coated steel sheet is heat treatable in a furnace under non protective atmosphere at an austenitization temperature between 84° and 950° C. and a dwell time between 1 and 12 minutes and is suitable for hot forming at a temperature between 60° and 830° C.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Aug 31, 2021
From: ALLELY, CHRISTIAN; DUSSAUSSOIS, DAVID; GRIGORIEVA, RAISA; MACHADO AMORIM, TIAGO
To: ARCELORMITTAL
Reel/Frame 057346/0731 →
Priority Claims (1)
WO PCT/IB2015/001284 · Jul 30, 2015 · international
Continuity (2)
Continuation 15748395
Related Publication 20210395854A1 · Dec 23, 2021
References Cited (115)
US 6635359B1 · Kurosaki et al. · 2003 [cited by applicant]
US 7867344B2 · Kusumi et al. · 2011 [cited by applicant]
US 8453482B2 · Maki et al. · 2013 [cited by applicant]
US 8858735B2 · Kondo et al. · 2014 [cited by applicant]
US 9034480B2 · Yoshida et al. · 2015 [cited by applicant]
US 9074277B2 · Maki et al. · 2015 [cited by applicant]
US 9234267B2 · Yoshida et al. · 2016 [cited by applicant]
US 9296520B2 · Watakabi · 2016 [cited by applicant]
US 11162153B2 · Machado Amorim · 2021 [cited by examiner]
US 20050142294A1 · Marutian et al. · 2005 [cited by applicant]
US 20070163685A1 · Kusumi et al. · 2007 [cited by applicant]
US 20070271978A1 · Brandstatter et al. · 2007 [cited by applicant]
US 20100068412A1 · Chaleix · 2010 [cited by applicant]
US 20100221572A1 · Laurent et al. · 2010 [cited by applicant]
US 20100282373A1 · Van Tol et al. · 2010 [cited by applicant]
US 20100319426A1 · Pohl et al. · 2010 [cited by applicant]
US 20110274945A1 · Shimoda et al. · 2011 [cited by applicant]
US 20110303328A1 · Kondo et al. · 2011 [cited by applicant]
US 20120073351A1 · Maki et al. · 2012 [cited by applicant]
US 20120085466A1 · Lupp et al. · 2012 [cited by applicant]
US 20120085467A1 · Thirion · 2012 [cited by examiner]
US 20120088115A1 · Smith · 2012 [cited by examiner]
US 20120135263A1 · Kobayashi et al. · 2012 [cited by applicant]
US 20120186705A1 · Sikora et al. · 2012 [cited by applicant]
US 20120267012A1 · Sohn et al. · 2012 [cited by applicant]
US 20130206824A1 · Wakatabi · 2013 [cited by applicant]
US 20130236739A1 · Yoshida et al. · 2013 [cited by applicant]
US 20140027026A1 · Schwinghammer et al. · 2014 [cited by applicant]
US 20140216612A1 · Laurent · 2014 [cited by examiner]
US 20140377584A1 · Hasegawa et al. · 2014 [cited by applicant]
US 20150007911A1 · Murakami · 2015 [cited by examiner]
US 20150020562A1 · Yamanaka et al. · 2015 [cited by applicant]
US 20150147589A1 · Bouaziz et al. · 2015 [cited by applicant]
US 20150191813A1 · Maki et al. · 2015 [cited by applicant]
US 20160222484A1 · Koyer et al. · 2016 [cited by applicant]
US 20170073792A1 · Hikida et al. · 2017 [cited by applicant]
US 20180023177A1 · Rachiele et al. · 2018 [cited by applicant]
US 20180044774A1 · Allely et al. · 2018 [cited by applicant]
US 20180051366A1 · Ooi et al. · 2018 [cited by applicant]
US 20180195159A1 · Sohn et al. · 2018 [cited by applicant]
US 20180216218A1 · Allely et al. · 2018 [cited by applicant]
US 20180223386A1 · Allely et al. · 2018 [cited by applicant]
US 20180223409A1 · Allely et al. · 2018 [cited by applicant]
US 20190044774A1 · Crols · 2019 [cited by applicant]
US 20190218651A1 · Allely et al. · 2019 [cited by applicant]
US 20190271342A1 · Canourgues et al. · 2019 [cited by applicant]
CN 101617059A · 2009 [cited by applicant]
CN 102011082A · 2011 [cited by applicant]
CN 102301014A · 2011 [cited by applicant]
CN 102791901B · 2012 [cited by applicant]
CN 104388870A · 2015 [cited by applicant]
DE 10246164A1 · 2004 [cited by applicant]
DE 202012000616U1 · 2012 [cited by applicant]
EP 1134301A1 · 2001 [cited by applicant]
EP 2644736A1 · 2013 [cited by applicant]
EP 2695963A1 · 2014 [cited by applicant]
EP 2839049B1 · 2017 [cited by applicant]
JP S464045Y1 · 1971 [cited by applicant]
JP S60162763A · 1985 [cited by applicant]
JP H04293759A · 1992 [cited by applicant]
JP H10176238A · 1998 [cited by applicant]
JP 11279735A · 1999 [cited by examiner]
JP H11279735A · 1999 [cited by applicant]
JP 2000104153A · 2000 [cited by applicant]
JP 2000328216A · 2000 [cited by applicant]
JP 2001073108A · 2001 [cited by applicant]
JP 2001115247A · 2001 [cited by applicant]
JP 2001214280A · 2001 [cited by applicant]
JP 2002012959A · 2002 [cited by applicant]
JP 2002322527A · 2002 [cited by applicant]
JP 2003251272A · 2003 [cited by applicant]
JP 2004339530A · 2004 [cited by applicant]
JP 2005060728A · 2005 [cited by applicant]
JP 2005290418A1 · 2005 [cited by applicant]
JP 2006051543A · 2006 [cited by applicant]
JP 2006193776A · 2006 [cited by applicant]
JP 2009218518A · 2006 [cited by applicant]
JP 2006299377A · 2006 [cited by applicant]
JP 2007182608A · 2007 [cited by applicant]
JP 2007211276A · 2007 [cited by applicant]
JP 2008038168A · 2008 [cited by applicant]
JP 2008111189A · 2008 [cited by applicant]
JP 2010070784A · 2010 [cited by applicant]
JP 2010515830A · 2010 [cited by applicant]
JP 2010229483A · 2010 [cited by examiner]
JP 4733522B2 · 2011 [cited by applicant]
JP 2011152589A · 2011 [cited by applicant]
JP 2012112010A · 2012 [cited by applicant]
JP 2015094006A · 2015 [cited by applicant]
JP 2016539249A · 2016 [cited by applicant]
KR 0146986B1 · 1998 [cited by applicant]
KR 100317680A1 · 2001 [cited by applicant]
KR 20040007718A · 2004 [cited by examiner]
RU 2544977C2 · 2015 [cited by applicant]
UA 76547 · 2006 [cited by applicant]
WO WO02103073A2 · 2002 [cited by applicant]
WO WO2010085983A1 · 2010 [cited by applicant]
WO WO2010086186A1 · 2010 [cited by examiner]
WO WO2012137687 · 2012 [cited by applicant]
WO WO2013122004A1 · 2013 [cited by applicant]
WO WO2013156688A1 · 2013 [cited by applicant]
WO WO2014059475A1 · 2014 [cited by applicant]
U.S. Appl. No. 17/463,128, filed Aug. 31, 2021, Allely et al., enclosed. [cited by applicant]
U.S. Appl. No. 17/463,187, filed Aug. 31, 2021, Allely et al., enclosed. [cited by applicant]
U.S. Appl. No. 17/463,217, filed Aug. 31, 2021, Allely et al., enclosed. [cited by applicant]
U.S. Appl. No. 15/748,262, filed Jan. 29, 2018, published as US 2018-0216218 A1 on Aug. 2, 2018. [cited by applicant]
U.S. Appl. No. 15/748,395, filed Jan. 29, 2018, published as US 2018-0223386 A1 on Aug. 9, 2018. [cited by applicant]
U.S. Appl. No. 17/463,217, filed Aug. 31, 2021, submitted herewith, not yet published. [cited by applicant]
U.S. Appl. No. 17/463,187, filed Aug. 31, 2021, submitted herewith, not yet published. [cited by applicant]
U.S. Appl. No. 17/463,128, filed Aug. 31, 2021, submitted herewith, not yet published. [cited by applicant]
U.S. Appl. No. 15/748,033, filed Jan. 26, 2018, published as US 2018-0223409 A1 on Aug. 9, 2018. [cited by applicant]
U.S. Appl. No. 16/359,751, filed Mar. 20, 2019, published as US 2019-0218651 A1 on Jul. 18, 2019. [cited by applicant]
U.S. Appl. No. 17/463,142, filed Aug. 31, 2021, submitted herewith, not yet published. [cited by applicant]
Spiekermann P, “Legierungen—ein besonderes patentrechtliches Problem?”, Mitteilungen Der Deutschen Patentanwaelte, Heymann, Koln, DE, (Jan. 1, 1993), vol. 34, ISSN 0026-6884, pp. 178-190, XP002152326 [A] 1-26 * p. 4-p. … [cited by applicant]
Hauger A et al., “Flexibles Walzen Von Tailer Rolled Blanks//Flexible Rolling of Tailor Rolled Blanks”, Stahl und Eisen, Verlag Stahleisen, Jan. 1, 2006, pp. 21-23, vol. 126, No. 5, Dusseldorf, DE See English Abstract. [cited by applicant]