Granted Patent B2
US 12,351,893 · App. 18/601,913 · Granted Jul 8, 2025

3D printers and feedstocks for 3D printers

Inventors: Satyabrata Raychaudhuri (Thousand Oaks, CA); Yongan Yan (Thousand Oaks, CA); Leonid Grigorian (Camarillo, CA)
Assignee: Yazaki Corporation
C22C1/1084B22F1/16B22F10/00B29C64/153B29C64/165B29C64/268B29C64/314B29C71/04B33Y10/00B33Y40/10B33Y70/00C22C26/00C22C32/0084B22F10/12B22F10/18B22F10/25B22F10/28Y02P10/25
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,351,893
App. No.
18/601,913
Granted
Jul 8, 2025
Kind
B2
Abstract

This disclosure relates in general to three dimensional (“3D”) printers having a configuration that prepares a three-dimensional object by using a feedstock comprising a metal or a polymer compound and a carbon coating formed on a surface of the compound. This disclosure also relates to such feedstocks and their preparation methods. This disclosure further relates to 3D composite objects prepared by using such printers and feedstocks. This disclosure also relates to carbon containing photocurable formulations and methods for their preparation. This disclosure further relates to electrically conducting 3D polymer composites prepared by using such carbon containing photocurable formulations.

Claims (58)

1. A method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer comprising:

dispensing a feedstock;

depositing a layer of the feedstock on a surface;

delivering an electromagnetic radiation to selected areas of the feedstock layer; and

preparing a three-dimensional composite object;

wherein the feedstock comprises a metal compound and a coating formed on a surface of the metal compound;

wherein the coating comprises nanocarbons including carbon nanotubes;

wherein the G/D ratio of the nanocarbons in the coating is approximately the same or higher than the G/D ratio of the nanocarbons in their initial state;

wherein the coating has a thickness; and

wherein the coating absorbs the delivered electromagnetic radiation at the selected areas of the feedstock layer, converts the absorbed electromagnetic radiation to heat, and transfers the heat to the metal compound, thereby heating the selected areas of the feedstock layer and causing the feedstock to bond to each other and the surface on which it is deposited, and thereby forming a bonded feedstock layer.

2. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , further comprising:

depositing a second layer of the feedstock on a surface of the bonded feedstock layer formed before; and

forming another bonded feedstock layer according to claim 1 .

3. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating further comprises a pyrolytic carbon, a graphite, an activated carbon, an amorphous carbon, a carbon fiber, or a combination thereof.

4. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating further comprises a non-agglomerated nanocarbon.

5. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the nanocarbons further comprise a graphene, a fullerene, or a combination thereof.

6. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the carbon nanotubes comprise a single-wall carbon nanotube, a double-wall carbon nanotube, a multi-wall carbon nanotube, or a combination thereof.

7. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein:

the nanocarbons further comprise a graphene; and

the graphene comprises a single layer graphene, a double layer graphene, a multilayer graphene, a graphene strip, or a combination thereof.

8. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein:

the coating further comprises a fullerene; and

the fullerene comprises a C 60 , a C 70 , a C 76 , a C 78 , a C 84 , or a combination thereof.

9. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the metal compound comprises titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, ruthenium, rhodium, palladium, aluminum, indium, gallium, tin, silver, gold, platinum, lead, bismuth, steel, bronze, brass, or a combination thereof.

10. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the metal compound comprises a metal particle, a metal wire, a metal tube, a metal sheet, or a combination thereof.

11. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein absorbance of the coating is higher than absorbance of the metal compound.

12. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein absorbance of the coating is at least 50 percent higher than the absorbance of the metal compound.

13. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein absorbance of the coating is at least 100 percent higher than the absorbance of the metal compound.

14. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein absorbance of the coating is at least 500 percent higher than the absorbance of the metal compound.

15. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein absorbance of the coating is at least 800 percent higher than the absorbance of the metal compound.

16. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein a heating rate of the feedstock comprising the metal compound and the coating is higher than a heating rate of a feedstock comprising the metal compound with no coating.

17. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein a heating rate of the feedstock comprising the metal compound and the coating is at least 50 percent higher than a heating rate of a feedstock comprising the metal compound with no coating.

18. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein a heating rate of the feedstock comprising the metal compound and the coating is at least 100 percent higher than a heating rate of a feedstock comprising the metal compound with no coating.

19. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein a heating rate of the feedstock comprising the metal compound and the coating is at least 500 percent higher than a heating rate of a feedstock comprising the metal compound with no coating.

20. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein a heating rate of the feedstock comprising the metal compound and the coating is 800 percent higher than a heating rate of a feedstock comprising the metal compound with no coating.

21. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the thickness of the coating is configured to substantially absorb the electromagnetic radiation, but not to cause defects in the composite object and thereby negatively impact properties of the composite object.

22. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating thickness is in the range of 10 nanometers to 100 micrometers.

23. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating thickness is in the range of 100 nanometers to 10 micrometers.

24. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating thickness is in the range of 1 micrometer to 5 micrometers.

25. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the electromagnetic radiation is delivered at a power of less than or equivalent to 5,000 watts.

26. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the electromagnetic radiation is delivered at a power of less than or equivalent to 1,000 watts.

27. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the electromagnetic radiation is delivered at a power of less than or equivalent to 500 watts.

28. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the electromagnetic radiation is delivered at a power of less than or equivalent to 100 watts.

29. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 1 , wherein the coating is substantially free of any dispersion solvent.

30. A method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer comprising:

dispensing a feedstock;

depositing a layer of the feedstock on a surface;

delivering an electromagnetic radiation to selected areas of the feedstock layer; and

preparing a three-dimensional composite object;

wherein the feedstock comprises a metal compound and a coating formed on a surface of the metal compound;

wherein the coating comprises a dried-slurry dispersion comprising nanocarbons including carbon nanotubes;

wherein the coating is substantially free of surfactants, functional groups, and dispersing agents;

wherein the coating has a thickness in the range of 10 nanometers to 100 micrometers when dry; and

wherein the coating absorbs the delivered electromagnetic radiation at the selected areas of the feedstock layer, converts the absorbed electromagnetic radiation to heat, and transfers the heat to the metal compound, thereby heating the selected areas of the feedstock layer and causing the feedstock to bond to each other and the surface on which it is deposited, and thereby forming a bonded feedstock layer.

31. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 30 , wherein the thickness of the coating is in the range of 100 nanometers to 10 micrometers when dry.

32. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 30 , wherein the thickness of the coating is in the range of 1 micrometer to 5 micrometers when dry.

33. The method of preparing a three-dimensional composite object using a three dimensional (“3D”) printer of claim 30 , wherein:

the metal compound comprises titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, ruthenium, rhodium, palladium, aluminum, indium, gallium, tin, silver, gold, platinum, lead, bismuth, steel, bronze, brass, or a combination thereof, in the form of metal granules.

Continuity (5)
Continuation 17169169 · Feb 5, 2021
Division 15515955
Provisional Application 62184867 · Jun 26, 2015
Provisional Application 62059947 · Oct 5, 2014
Related Publication 20240209477A1 · Jun 27, 2024
References Cited (57)
US 4612208A · Reichenecker · 1986 [cited by applicant]
US 5204055A · Sachs et al. · 1993 [cited by applicant]
US 5597589A · Deckard · 1997 [cited by applicant]
US 6780368B2 · Liu et al. · 2004 [cited by applicant]
US 7329379B2 · Boyd et al. · 2008 [cited by applicant]
US 7431965B2 · Grigorian et al. · 2008 [cited by applicant]
US 7879282B2 · Hopkinson et al. · 2011 [cited by applicant]
US 8574485B2 · Kramer et al. · 2013 [cited by applicant]
US 9136536B2 · Grigorian et al. · 2015 [cited by applicant]
US 9617158B2 · Raychaudhuri et al. · 2017 [cited by applicant]
US 10781512B2 · Konyashin · 2020 [cited by examiner]
US 20020145213A1 · Liu et al. · 2002 [cited by applicant]
US 20030122111A1 · Glatkowski · 2003 [cited by examiner]
US 20050012247A1 · Kramer et al. · 2005 [cited by applicant]
US 20050093208A1 · Boyd et al. · 2005 [cited by applicant]
US 20070238056A1 · Baumann et al. · 2007 [cited by applicant]
US 20070241482A1 · Giller et al. · 2007 [cited by applicant]
US 20080193634A1 · Yaniv et al. · 2008 [cited by applicant]
US 20090092747A1 · Zhamu et al. · 2009 [cited by applicant]
US 20100108950A1 · Plee · 2010 [cited by applicant]
US 20100258111A1 · Shah et al. · 2010 [cited by applicant]
US 20110117485A1 · Hermann et al. · 2011 [cited by applicant]
US 20140106257A1 · Raychaudhuri et al. · 2014 [cited by applicant]
US 20140134334A1 · Pridoehl et al. · 2014 [cited by applicant]
US 20140272172A1 · Zhamu · 2014 [cited by examiner]
US 20160168391A1 · Costa et al. · 2016 [cited by applicant]
US 20160271700A1 · Akimoto et al. · 2016 [cited by applicant]
US 20160289468A1 · Turner · 2016 [cited by examiner]
US 20160303779A1 · Kunc · 2016 [cited by examiner]
US 20170190579A1 · Cola et al. · 2017 [cited by applicant]
US 20180122570A1 · Li · 2018 [cited by examiner]
US 20180215854A1 · Paranthaman · 2018 [cited by examiner]
US 20200248014A1 · Bougher · 2020 [cited by examiner]
CA 3121870A1 · 2014 [cited by examiner]
CA 2893945A · 2015 [cited by applicant]
CN 1976799A · 2007 [cited by applicant]
CN 1979929A · 2007 [cited by applicant]
CN 102648088A · 2012 [cited by applicant]
CN 103553030A · 2014 [cited by applicant]
CN 103819656A · 2014 [cited by applicant]
CN 107107494A · 2017 [cited by applicant]
EP 2244268B1 · 2016 [cited by applicant]
EP 3312141A1 · 2018 [cited by applicant]
WO WO0156736A2 · 2001 [cited by examiner]
Santos et al., “Nanocomposite of photocurable epoxy-acrylate resin and carbon nanotubes: dynamic-mechanical, thermal and tribological properties”, Materials Research, vol. 16, No. 2, 2013, pp. 367-374. [cited by applicant]
Sangermano et al., “Use of single-walled carbon nanotubes as reinforcing fillers in UV-curable epoxy systems”, Macromolecular Materials and Engineering, vol. 293, No. 8, 2008, pp. 708-713. [cited by applicant]
Zhu et al., Alignment of multiwalled carbon nanotubes in bulk epoxy composites via electric field. Journal of Applied Physics, vol. 105, No. 5, 2009, pp. 1-6. [cited by applicant]
Martin-Gallego et al., Cationic photocured epoxy nanocomposites filled with different carbon fillers. Polymer, vol. 53, No. 9, 2012, pp. 1831-1838. [cited by applicant]
Santos et al., “Thermal and mechanical properties of a nanocomposite of a photocurable epoxy-acrylate resin and multiwalled carbon nanotubes”, Materials Science and Engineering A: Structural Materials Properties Microst… [cited by applicant]
Gojny et al., “Carbon nanotube-reinforced epoxy-compo sites: enhanced stiffness and fracture toughness at low nanotube content, Composites Science and Technology”, vol. 64, No. 15, 2004, pp. 2363-2371. [cited by applicant]
Dong et al., Study on tribological properties of multi-walled carbon nanotubes/epoxy resin nanocomposites, Tribology Letters, vol. 20, No. 3-4, 2005, pp. 251-254. [cited by applicant]
Ushiba et al., “3D microfabrication of single-wall carbon nanotube/polymer composites by two-photon polymerization lithography”, Carbon, vol. 59, 2013, pp. 283-288. [cited by applicant]
Kumar et al., “Chemical Vapor Deposition of Carbon Nanotubes: A Review on Growth Mechanism and Mass Production”, Journal of Nanoscience and Nanotechnology, vol. 10, 2010, pp. 3739-3758. [cited by applicant]
Hornyak et al., “Temperature Window for Chemical Vapor Decomposition Growth of Single-Wall Carbon Nanotubes”, Journal of Physical Chemistry B, vol. 106, 2002, pp. 2821-2825. [cited by applicant]
Deutsch et al., “Mix or Match: Choose the Best Mixers Every Time: The choice is wide—from a variety of agitators, to devices that homogenize, emulsify, or disintegrate solids”, Chemical Engineering, vol. 105, No. 8, Aug… [cited by applicant]
Dresselhaus et al., “Defect characterization in graphene and carbon nanotubes using Raman spectroscopy”, Phil. Trans. Royal Society A, vol. 368, 2010, pp. 5355-5377. [cited by applicant]
Ferrari, “Raman spectroscopy of graphene and graphite: Disorder, electron-phonon coupling, doping and nonadiabatic effects”, Solid State Communications, vol. 143, 2007, pp. 47-57. [cited by applicant]