Resin composition and article made therefrom
A resin composition includes a prepolymer which is prepared from a mixture subjected to a prepolymerization reaction, the mixture including 100 parts by weight of a first maleimide resin, 40 to 60 parts by weight of a siloxane compound and 10 to 30 parts by weight of a diamine compound, wherein: the first maleimide resin includes bisphenol A diphenyl ether bismaleimide; the siloxane compound includes a compound of Formula (I), having a molecular weight of 2200 to 2600 g/mol; and the diamine compound includes 4-aminophenyl-4-aminobenzoate. The resin composition may be used to make various articles, such as a varnish, a prepreg, a resin film, a laminate or a printed circuit board, and at least one of the following properties can be improved, including resin compatibility and X-axis coefficient of thermal expansion.
1. A resin composition comprising a prepolymer which is prepared from a mixture subjected to a prepolymerization reaction, the mixture comprising 100 parts by weight of a first maleimide resin, 40 to 60 parts by weight of a siloxane compound and 10 to 30 parts by weight of a diamine compound, wherein:
the first maleimide resin comprises bisphenol A diphenyl ether bismaleimide;
the siloxane compound comprises a compound of Formula (I), having a molecular weight of 2200 to 2600 g/mol,
wherein 26≤n≤32, and n is a positive integer; and
the diamine compound comprises 4-aminophenyl-4-aminobenzoate.
2. The resin composition of claim 1 , further comprising a second maleimide resin.
3. The resin composition of claim 2 , comprising 100 parts by weight of the prepolymer and 10 to 35 parts by weight of the second maleimide resin.
4. The resin composition of claim 2 , wherein the second maleimide resin comprises polyphenylmethane maleimide, biphenyl aralkyl maleimide, diallyl nadiimide or a combination thereof.
5. The resin composition of claim 1 , further comprising inorganic filler, flame retardant, curing accelerator, polymerization inhibitor, solvent, silane coupling agent, coloring agent, toughening agent or a combination thereof.
6. An article made from the resin composition of claim 1 , comprising a varnish, a prepreg, a resin film, a laminate or a printed circuit board.
7. The article of claim 6 , wherein no layer separation occurs after standing still the varnish at room temperature for 3 hours in a resin compatibility test.
8. The article of claim 6 , having an X-axis coefficient of thermal expansion as measured by reference to IPC-TM-650 2.4.24.5 of less than or equal to 4.21 ppm/° C.