Granted Patent B2

US 12,415,910 · App. 17/945,317 · Granted Sep 16, 2025

Inventors: Ulf Schueller (Weiterstadt, DE); Sebastian Wilhelm (Mainz-Kastel, DE); Harald Schmitz (Weinheim, DE); Andreas Maus (Frankfurt, DE); Bernd Lothar Marczinke (Römerberg, DE); Elke Damm (Bad Vilbel, DE); Gerhardus Meier (Frankfurt, DE); Eric D. Day (Florence, KY); Sameer D. Mehta (Mason, OH); Harilaos Mavridis (Lebanon, OH)

Assignee: Basell Polyolefine GmbH

C08L23/06B65D1/0207B65D23/10C08F2/38C08F110/02B29C49/0005B29K2023/065

Abstract

Claims (44)

1. A polyethylene composition having the following features:

1) a ratio MIF/MIE from greater than 125 to 180, where MIF is the melt flow index measured at 190° C. with a load of 21.60 kg, and MIE is the melt flow index measured at 190° C. with a load of 2.16 kg, both determined according to ISO 1133-1 2012-03;

2 ) a MIF from 20 to 40 g/10 min.;

3 ) a density from 0.948 to 0.960 g/cm 3 , determined according to ISO 1183-1:2012 at 23° C.;

4 ) an ER value from 5 to 10;

wherein the ER is calculated according with an equation as follows ;

ER=(1.781*10 −3 )* G′

at a value of G″=5,000 dyn/cm 2 ;

wherein:

G′=storage-modulus;

G″=loss-modulus;

both G′ and G″ being measured with dynamic oscillatory shear in a plate-plate rotational rheometer at a temperature of 190° C.

2. The polyethylene composition of claim 1 , wherein the polyethylene composition is formed by contacting a precursor polyethylene composition (I) with a radical initiator, wherein the precursor polyethylene composition (I) has a ratio MIF/MIE 11 ) lower than MIF/MIE 1 ) and from 90 to 120 ;

wherein the ratio 1)/1 I ), which is between the MIF/MIE 1) of the final polyethylene composition (after contacting with the radical initiator) and the MIF/MIE 1 I ) of the precursor polyethylene composition (I), is equal to or greater than 1.05, preferably equal to or greater than 1.1, in particular from 1.05 or from 1.1 to 1.8, or from 1.05 or from 1.1 to 1.6.

3. The polyethylene composition of claim 2 , wherein the precursor polyethylene composition (I) has:

2 I ) a MIF from 30 to 50 g/10 min.;

3 I ) a density from 0.948 to 0.960 g/cm 3 ;

4 I )ER value from 2 to 5.

4. The polyethylene composition of claim 2 , wherein the precursor polyethylene composition (I) comprises:

A) 30-70% by weight, of an ethylene homopolymer or copolymer, wherein the ethylene homopolymer or copolymer has a density equal to or greater than 0.960 g/cm 3 and melt flow index MIE measured at 190° C. with a load of 2.16 kg, according to ISO 1133, of 40 g/10 min. or higher;

B) 30-70% by weight, of an ethylene copolymer having a MIE value lower than 0.5 g/10 min.

5. The polyethylene composition of claim 1 , obtained by using, in the polymerization stage, a Ziegler-Natta polymerization catalyst.

6. The polyethylene composition of claim 5 , wherein the Ziegler-Natta polymerization catalyst comprises the product of reaction of:

A) a solid catalyst component comprising Ti, Mg, chlorine and one internal electron donor ED selected from esters of aliphatic monocarboxylic acids (EAA) and another internal donor ED I selected from cyclic ethers (CE) in an amount such that the EAA/CE molar ratio ranges from 0.02 to less than 20;

B) an organo-Al compound; and optionally

C) an external electron donor compound.

7. The polyethylene composition of claim 1 , consisting of or comprising one or more ethylene copolymers.

8. The polyethylene composition of claim 1 , having at least one of the following additional features:

a swell ratio equal from 160% to 200%;

a FNCT 6 MPa/50° C. from 40 to 100 h;

a comonomer content equal to or less than 1.7% by weight, with respect to the total weight of the polyethylene composition;

a MIP of 0.3 g/10 min. to 4 g/10 min., wherein the MIP is the melt flow index measured at 190° C. with a load of 5 kg, determined according to ISO 1133-1 2012-03;

a ratio (MIF/MIE)/ER, which is between MIF/MIE and ER, and is from 15 to 26;

a long chain branching index LCBI from 0.55 to 0.95;

wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having the same molecular weight at a mol. weight of 1,000,000 g/mol;

a η 0.02 from 56,000 to 80,000 Pa·s;

wherein the η 0.02 is the complex viscosity of the melt, measured at a temperature of 190° C., in a parallel-plate (or so-called plate-plate) rheometer under dynamic oscillatory shear mode with an applied angular frequency of 0 . 02 rad/s;

a ratio (η 0.02 /1000)/LCBI, which is between η 0.02 divided by 1000 and LCBI, from 85 to 150;

a HMWcopo index from 0.5 to 5;

wherein the HMWcopo index is determined according to the following formula:

HMWcopo=(η 0.02 ×t maxDSC )/(10{circumflex over ( )}5)

whereinh t maxDSC is the time, in minutes, required to reach the maximum value of heat flow (in mW) of crystallization (time at which the maximum crystallization rate is achieved, equivalent to the t½ crystallization half-time) at a temperature of 124° C. under quiescent conditions, measured in isothermal mode in a differential scanning calorimetry apparatus, DSC.

9. A manufactured article comprising the polyethylene composition of claim 1 .

10. The manufactured article of claim 9 , wherein the manufactured article is a blow molded article and is handleware.

Assignments (3)

Continuity (1)

References Cited (43)