Hexagonal boron nitride powder and method for producing the same
The present invention provides a hexagonal boron nitride powder that has a highly reduced content of magnetic foreign bodies and is excellent in electrical insulation, and a production method capable of producing the hexagonal boron nitride powder at low cost. The hexagonal boron nitride powder includes single particles and/or aggregated particles of hexagonal boron nitride and has a total content of Co, Cr, Cu, Fe, Mg, Mn, Ni, Ti, Zn, and Al of not more than 20 ppm. The method for producing the hexagonal boron nitride powder with a reduced content of magnetic foreign bodies includes a plurality of specific steps.
1. A hexagonal boron nitride powder comprising single particles and/or aggregated particles of hexagonal boron nitride and having a total elemental content of Co, Cr, Cu, Fe, Mg, Mn, Ni, Ti, Zn, and Al of not more than 20 ppm, of which not more than 3.6 ppm is the Fe.
2. The hexagonal boron nitride powder according to claim 1 , having an average particle diameter of 2 to 90 μm.
3. The hexagonal boron nitride powder according to claim 1 , wherein amounts of eluted boron, eluted calcium, eluted sodium, and eluted silicon after immersion in a sulfuric acid aqueous solution at a concentration of 0.02 mol/L at 25° C. for 120 minutes are not more than 200 ppm in terms of B 2 O 3 , not more than 50 ppm, not more than 20 ppm, and not more than 20 ppm, respectively, and an amount of eluted chlorine after immersion in water at 25° C. for 120 minutes is not more than 10 ppm.