Moisture/oil-resistant fiber/starch composite materials
The invention relates to uncoated, fiber/starch composite materials manufactured without the use of fluorochemicals or additional binders that offer superior oil and grease resistance properties. Addition of an internal sizing agent in the preparation of the fiber/starch composite materials results in superior hot water and cold water resistance properties. The fiber/starch composite materials may be used for the manufacture of food service containers. The invention also relates to methods of preparation of the fiber/starch composite materials.
1. An oil, grease, and water-resistant composition comprising a matrix of starch, cellulosic fiber, and an internal sizing agent; wherein the composition is prepared by:
blending cellulosic fiber in water to create a fiber/water mixture;
blending the fiber/water mixture with starch granules and a sizing agent;
forming the fiber/starch/sizing agent blend into a sheet;
compressing and heating the sheet until nearly dry but still pliable;
forming the nearly dry sheet into an article; and
drying the article;
wherein the starch is about 30 to about 50 wt % of the composition;
wherein no fluorocarbons or auxiliary binders are in the composition;
wherein the composition is not covered by oil resistant, hot-water resistant, or cold-water resistant coatings;
wherein the composition optionally comprises a filler material; and
wherein the composition is oil, grease, and water-resistant.
2. An article of manufacture comprising the composition of claim 1 .
3. The article of manufacture of claim 2 , wherein the article of manufacture is a food container.
4. The article of manufacture of claim 3 , wherein the food container is a box, a cup, a clamshell, a plate, a bowl, a tray, a carton, an envelope, a sack, a bag, a baggie, a liner, a partition, a wrapper, a film, or a cushioning material.
5. The composition of claim 1 , wherein the internal sizing agent is an alkyl, alkenyl, aryl, alkaryl ketene dimer, alkenyl succinic anhydride, rosin, wax, stearic anhydride, or other fatty acid anhydride.
6. The composition of claim 5 , wherein the internal sizing agent is an alkene ketene dimer.
7. The composition of claim 1 , wherein the internal sizing agent is present from at least about 0.03% to less than about 90% by weight of the composition.