High voltage electrolyte for 5V solid state lithium-ion battery cell
View Patent ↗High voltage, high-ionic-conductivity, fire resistant solid-state polymer electrolytes include poly(vinylidene fluoride-co-hexafluoropropylene) P(VDF-HFP), sulfolane plasticizer, lithium salt, and ceramic nanoparticles with the basic formula Li 7 La 3 Zr 2 O 12 (LLZO) and derivatives thereof. During the curing process, the presence of the LLZO nanoparticles prevent the P(VDF-HFP) from developing into a crystalline phase. In the electrolyte formed, the P(VDF-HFP) is in an amorphous phase with LLZO nanoparticles, lithium salt and sulfolane distributed in the polymer matrix. The solid-state electrolyte with the amorphous polymer phase exhibit higher ionic conductivities than those having a crystalline polymer phase. The LLZO contributes to mechanical properties of the electrolyte and also function as tough ceramic fillers that inhibit lithium dendrite growth during operation of lithium-ion cells and batteries. 5V all-solid-state lithium-ion batteries incorporated the electrolytes exhibit high energy densities (250-350 Whr/kg), high power densities (high discharge rate up to 5 C) and long service lives (500-1500 cycles, <2% irreversible loss/month).
1 . A solid-state electrolyte that comprises (i) a polymer matrix that comprises poly (vinylidene fluoride-co-hexafluoropropylene) P (VDF-HFP), (ii) a plasticizer that comprises sulfolane (SL), (iii) a lithium salt, and (iv) ceramic nanoparticles with diameters that range from 10 to 2000 nm that are distributed in the polymer matrix, wherein the ceramic nanoparticles are selected from the group consisting of ceramic materials having the basic formula Li 7 La 3 Zr 2 O 12 (LLZO) and derivatives thereof wherein at least one of Al, Ta or Nb is substituted in Zr sites of the Li 7 La 3 Zr 2 O 12
wherein the P (VDF-HFP) polymer matrix, the sulfolane plasticizer and the lithium salt form a ternary complex with the P (VDF-HFP) polymer matrix having an amorphous polymer microstructure.
2 . The solid-state electrolyte of claim 1 comprising 10 to 50 wt % P(VDF-HFP) based polymer, 10 to 45 wt % SL based plasticizer, 10 to 50 wt % lithium salt, and 5 to 40 wt % LLZO based ceramic nanoparticles.
3 . The solid-state electrolyte of claim 1 forms a membrane that has an ionic conductivity of higher than 1×10-3 S/cm when measured at a temperature 20° C., or higher.
4 . The solid-state electrolyte of claim 1 forms a membrane that has a compressive strength of 1 to 100 MPa.
5 . The solid-state electrolyte of claim 1 forms a film which is fire-resistant and non-flammable.
6 . The solid-state electrolyte of claim 1 forms a film that is free standing and has a thickness that ranges from 10 to 200 μm.
7 . The solid-state electrolyte of claim 1 wherein the solid-state electrolyte is a film that is coated onto a separator layer comprising a polymer mesh or membrane.
8 . The solid-state electrolyte of claim 1 comprising a separator layer comprising a polymer mesh or membrane wherein the solid-state electrolyte is impregnated in the separator layer.
9 . The solid-state electrolyte of claim 1 wherein the polymer matrix consists of P(VDF-HFP) and the plasticizer consists of sulfolane.
10 . The solid-state electrolyte of claim 1 wherein the lithium salt is selected from the group consisting of LiTFSI, LiClO 4 , LiPF 6 , LiAsF 6 , LiBOB, and mixtures thereof.
11 . The solid-state electrolyte of claim 1 wherein the ceramic nanoparticles comprise Li 7 La 3 Zr 2 O 12.
12 . An all-solid-state lithium-ion electrochemical cell which comprises:
an anode, a cathode, and interposed between therebetween a solid-electrolyte that comprises: (i) a polymer matrix that comprises poly (vinylidene fluoride-co-hexafluoropropylene) P(VDF-HFP), (ii) ceramic nanoparticles with diameters that range from 10 to 2000 nm that are distributed in the polymer matrix, (iii) a plasticizer that comprises sulfolane and (iv) a lithium salt, wherein the ceramic nanoparticles are selected from the group consisting of ceramic materials having the basic formula Li 7 La 3 Zr 2 O 12 (LLZO) and derivatives thereof wherein at least one of Al, Ta or Nb is substituted in Zr sites of the Li 7 La 3 Zr 2 O 12,
wherein the polymer matrix is an amorphous polymer matrix, and the ceramic materials are distributed within the amorphous polymer matrix.
13 . The electrochemical cell of claim 12 which has an energy density of at least about 250 Wh/kg.
14 . The electrochemical cell of claim 12 which is capable of outputting a voltage of 4.1 volts to 5.1 volts.
15 . The electrochemical cell of claim 12 which has a power density of at least about 750 W/kg.
16 . The electrochemical cell of claim 12 wherein the anode comprises lithium, silicon or graphite and mixtures thereof.
17 . The electrochemical cell of claim 12 wherein the cathode comprises a material that is selected from the group consisting of LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NCM811), LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM 622), LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523), LiNiCoAlO 2 (NCA), LiMn 1.5 Ni 0.2 O 2 (LMNO), and LiMPO 4 wherein M is Ni, Co, Mn, or Fe, and mixtures thereof.
18 . A process for preparing an ASSB cell which comprises: (a) providing an anode; (b) providing a cathode; and (c) positioning a solid-state electrolyte between the cathode and anode, wherein the solid-state electrolyte comprises (i) a polymer matrix that comprises poly (vinylidene fluoride-co-hexafluoropropylene) P (VDF-HFP), (ii) a plasticizer that comprises sulfolane, (iii) a lithium salt, and (iv) ceramic nanoparticles with diameters that range from 10 to 2000 nm that are distributed in the polymer matrix, wherein the ceramic nanoparticles are selected from the group consisting of ceramic materials having the basic formula Li 7 La 3 Zr 2 O 12 (LLZO) and derivatives thereof wherein at least one of Al, Ta or Nb is substituted in Zr sites of the Li 7 La 3 Zr 2 O 12,
wherein the polymer matrix is an amorphous polymer matrix, and the nanoparticles of the ceramic materials are distributed within the amorphous polymer matrix.