Method and device for regenerating granular activated carbon by arc initiation and discharge

1 . A method for regenerating granular activated carbon by arc initiation and discharge, the method comprising steps of:

the granular activated carbon continuously flowing through a heating passage; and

applying a DC (direct current) to two electrode plates in the heating passage, wherein a voltage of the DC is expressed by a voltage formula of

U

=

ηρ

⁢

cq

m

⁢

Δ

⁢

T

⁡

(

1

+

2

⁢

q

m

α

+

q

m

+

β

⁢

d

p

)

⁢

l

S

,

here, ρ is resistivity of the granular activated carbon, c is specific heat capacity of the granular activated carbon, q m is mass flow of the granular activated carbon in the heating passage, ΔT is target temperature rise value of regenerated activated carbon, d p is equivalent particle size of the granular activated carbon, l is distance between the two electrode plates, S is area of each of the two electrode plates, η is a dimensionless coefficient in a range of 1 to 5, α is an empirical parameter which is expressed by a formula of α=xwlρ m and has a unit of kg/s, here, x is an adjustment parameter with dimension m/s and is in range of 0.002 m/s to 0.01 m/s, w is facing width of the two electrode plates, ρ m is bulk density of the granular activated carbon, β is an empirical parameter in a range of 200 m −1 to 800 m −1 , wherein:

the granular activated carbon tumbles, collides and separates with each other in the heating passage during transportation, electrons are excited to pass through a potential barrier to form field emission and impact ionization, resulting in arc initiation;

the arc initiation is conducive to current conduction and heat release, and reduces the resistance of an activated carbon access circuit, so that under a combined action of conductive Joule heating and arc heat release, the activated carbon heats up and an adsorbate is pyrolyzed, thereby achieving regeneration.

2 . The method according to claim 1 , wherein a measurement process of the bulk density ρ m of the granular activated carbon comprises steps of (a) placing the granular activated carbon into a 100 mL of graduated cylinder several times, tapping a bottom of the graduated cylinder with a rubber hammer after each placement until a volume of the granular activated carbon reaches 100 mL and no longer decreases; (b) and then weighing out a net weight of the granular activated carbon in the graduated cylinder with an electronic scale; and (c) finally dividing the net weight of the granular activated carbon by the volume of 100 mL to obtain the bulk density of the granular activated carbon.

3 . The method according to claim 1 , wherein when the voltage of the DC, which is calculated according to the target temperature rise value, is higher than a preset value, or when an input power, which is calculated according to the voltage of the DC, exceeds a rated power of a DC power supply, the voltage of the DC and the input power are reduced by reducing the mass flow q m of the granular activated carbon in the heating passage; on the contrary, when the voltage of the DC, which is calculated according to the target temperature rise value, is lower than a preset low value, an efficiency and a capacity of the granular activated carbon are increased by increasing the mass flow q m , wherein q m =vwlρ m , here, v is flow rate of the granular activated carbon in a range of 0.0005 m/s to 0.02 m/s, and therefore, the mass flow q m is able to be adjusted by controlling the flow rate v of the granular activated carbon, changing the distance/between the two electrode plates and the facing width w of the two electrode plates.

4 . The method according to claim 1 , wherein the equivalent particle size of the granular activated carbon is in a range of 0.5 mm to 10 mm.

5 . The method according to claim 1 , wherein a moisture content of the granular activated carbon is less than 5%.