Granted Patent B2

US 12,503,557 · App. 17/680,806 · Granted Dec 23, 2025

Inventor: Tadashi Mizuno (Tokyo, JP)

Assignee: MCPP Innovation LLC

C08G81/022C08J3/24C08G2190/00C08J2353/02

Abstract

Claims (34)

1 . A joint member comprising a thermoplastic elastomer composition including components (A), (B), and (C) below, wherein an amount of the component (B) is 100 to 140 parts by mass and an amount of the component (C) is 60 to 140 parts by mass relative to 100 parts by mass of the component (A),

wherein the thermoplastic elastomer composition is formed by performing crosslinking with a component (D), and

wherein a compression set of the thermoplastic elastomer composition, the compression set being measured under conditions of 70° C., 22 hours, and 25% compression in accordance with JIS K 6262, is 60% or less,

Component (A): a hydrogenated product of a block copolymer including at least two polymer blocks composed primarily of a vinyl aromatic compound and at least one polymer block including butadiene, wherein the hydrogenated product of the block copolymer comprises a hydrogenated product (A1) of a block copolymer having a weight-average molecular weight of 300,000 or more and a hydrogenated product (A2) of a block copolymer having a weight-average molecular weight of 220,000 to 290,000,

Component (B): a hydrocarbon rubber softener,

Component (C): a polypropylene resin,

Component (D): a crosslinking agent

wherein a melt flow rate of the thermoplastic elastomer composition measured at a temperature of 230° C. and a load of 21.2 N in accordance with JIS K 7210 is 10 to 80 g/10 min.

2 . The joint member according to claim 1 , wherein the component (C) includes a propylene random copolymer having a melting peak temperature of 100° C. or more and less than 157° C.

3 . The joint member according to claim 1 , wherein a content of the component (D) in the thermoplastic elastomer composition is 0.5 parts by mass or more and 10.0 parts by mass or less relative to 100 parts by mass of the component (A).

4 . An automotive composite molded body comprising the joint member claim 1 .

5 . A method for producing a joint member, the method comprising melt-kneading a thermoplastic elastomer composition including components (A), (B), (C), and (D) below, wherein an amount of the component (B) is 100 to 140 parts by mass and an amount of the component (C) is 60 to 140 parts by mass relative to 100 parts by mass of the component (A), and injection-molding the kneaded thermoplastic elastomer composition,

Component (A): a hydrogenated product of a block copolymer including at least two polymer blocks composed primarily of a vinyl aromatic compound and at least one polymer block including butadiene, wherein the hydrogenated product of the block copolymer comprises a hydrogenated product (A1) of a block copolymer having a weight-average molecular weight of 300,000 or more and a hydrogenated product (A2) of a block copolymer having a weight-average molecular weight of 220,000 to 290,000,

Component (B): a hydrocarbon rubber softener,

Component (C): a polypropylene resin,

Component (D): a crosslinking agent,

wherein a melt flow rate of the thermoplastic elastomer composition measured at a temperature of 230° C. and a load of 21.2 N in accordance with JIS K 7210 is 10 to 80 g/10 min.

6 . A thermoplastic elastomer composition comprising components (A), (B), and (C) below, wherein an amount of the component (B) is 100 to 140 parts by mass and an amount of the component (C) is 60 to 140 parts by mass relative to 100 parts by mass of the component (A),

wherein the thermoplastic elastomer composition is formed by performing crosslinking with a component (D), and

wherein a compression set of the thermoplastic elastomer composition, the compression set being measured under conditions of 70° C., 22 hours, and 25% compression in accordance with JIS K 6262, is 60% or less,

Component (A): a hydrogenated product of a block copolymer including at least two polymer blocks composed primarily of a vinyl aromatic compound and at least one polymer block including butadiene, wherein the hydrogenated product of the block copolymer comprises a hydrogenated product (A1) of a block copolymer having a weight-average molecular weight of 300,000 or more and a hydrogenated product (A2) of a block copolymer having a weight-average molecular weight of 220,000 to 290,000,

Component (B): a hydrocarbon rubber softener,

Component (C): a polypropylene resin,

Component (D): a crosslinking agent,

wherein a melt flow rate of the thermoplastic elastomer composition measured at a temperature of 230° C. and a load of 21.2 N in accordance with JIS K 7210 is 10 to 80 g/10 min.

7 . The thermoplastic elastomer composition according to claim 6 , the thermoplastic elastomer composition having a density of 0.90 to 0.95 g/cm 3 .

8 . The joint member according to claim 1 , wherein the hydrogenated product (A2) of the block copolymer has a weight-average molecular weight of 230,000 to 280,000.

9 . The joint member according to claim 1 , wherein the polypropylene resin comprises a propylene random copolymer including a propylene unit and a unit other than the polypropylene unit.

10 . The joint member according to claim 9 , wherein a content of the propylene unit in the propylene random copolymer is 60 to 99 wt %.

11 . The joint member according to claim 9 , wherein a content of the propylene unit in the propylene random copolymer is 80 to 98 wt %.

12 . The joint member according to claim 1 , wherein the crosslinking agent comprises an organic peroxide.

13 . The joint member according to claim 1 , wherein the crosslinking agent comprises a phenolic resin.

14 . The joint member according to claim 1 , wherein the crosslinking agent comprises 2,5-dimethyl-2,5-di(t-butylperoxy)hexane.

15 . The joint member according to claim 1 , wherein the crosslinking agent comprises divinylbenzene.