Wood composites and processes to modify same using stable, low pH aqueous silicate suspensions
A stable, low pH aqueous silicate suspension is disclosed for modifying wood article(s). The suspension includes: a metal silicate having a solution concentration of from 1.5 wt % to 52 wt % and characterized by a modulus of from about 1.8 to about 4.0; at least one of a protic acid solution and a buffering acid solution in an amount effective to acidify the metal silicate to a pH of 3.0 or less, preferably to a pH between 1.0 and 3.0; and a multivalent metal salt having a solution concentration from 5 wt % to 25 wt %. The suspension has a pH of 3.0 or less. Wood articles impregnated with the suspension and processes for modifying wood articles with the suspension are also disclosed. The stable, low pH aqueous silicate suspensions provide for an increased depth of impregnation into wood articles as compared with conventional silicate treatments.
1 . A stable, low pH aqueous silicate suspension for impregnating a wood article, the suspension comprising:
a metal silicate having a solution concentration of from about 1.5 wt % to about 52 wt % and characterized by a modulus of from about 1.8 to about 4.0 and at least one of a protic acid solution and a buffering acid solution in an amount effective to acidify the metal silicate to a pH of about 3.0 or less; and
a multivalent metal salt having a solution concentration from about 5 wt % to about 30 wt %;
wherein the metal silicate includes a metal counterion selected from sodium, potassium, lithium, and combinations thereof;
wherein the suspension has a pH of about 3.0 or less; and
wherein the wood article has a depth of impregnation greater than that of a comparative wood article impregnated with the metal silicate alone, the depth of impregnation determined by X-ray fluorescence measurement of silicon based on a Forstner bit method, American Wood Protection Association Method A-51-1.
2 . The suspension of claim 1 , wherein the metal silicate has a solution concentration of from about 12 wt % to about 40 wt %.
3 . The suspension of claim 1 , wherein the multivalent metal salt has a solution concentration from about 15 wt % to about 30 wt %.
4 . A modified wood composite comprising:
a wood article having a plurality of interconnected pores and an outer surface; and
an interconnected solid extending radially inward from the outer surface to a first distance, wherein the interconnected solid comprises a plurality of precipitated silicate particles at least partially impregnated within the plurality of interconnected pores;
wherein the interconnected solid is formed by impregnating the wood article with the stable, low pH aqueous silicate suspension of claim 1 , and wherein the first distance is greater than that of a comparative wood article impregnated with the metal silicate alone.
5 . The modified wood composite of claim 4 further comprising the
interconnected solid enveloping the outer surface.
6 . The suspension of claim 1 , wherein the metal silicate has a modulus, SiO 2 /R 2 O, wherein R is a+1 metal selected from sodium, potassium, lithium, and combinations thereof.
7 . The suspension of claim 1 , wherein the metal silicate is sodium silicate and the modulus is
SiO
2
Na
2
O
.
8 . A stable, low pH aqueous silicate suspension for impregnating a wood article, the suspension comprising:
a sodium silicate having a solution concentration of from about 1.5 wt % to about 52 wt % and characterized by a modulus,
SiO
2
Na
2
O
,
of about 1.8 to about 4.0 and at least one of a protic acid solution and a buffering acid solution in an amount effective to acidify the metal silicate to a pH of about 3.0 or less; and
a multivalent metal salt having a solution concentration from about 5 wt % to about 30 wt %;
wherein the suspension has a pH of about 3.0 or less; and
wherein the wood article has a depth of impregnation greater than that of a comparative wood article impregnated with the sodium silicate alone, the depth of impregnation determined by X-ray fluorescence measurement of silicon based on a Forstner bit method, American Wood Protection Association Method A-51-1.
9 . A process for modifying a wood article, the process comprising:
applying a vacuum to a wood article within a reactor to obtain a vacuum of about 1000 Pa to about 4000 Pa followed by removing the vacuum;
feeding the reactor with the stable, low pH aqueous silicate suspension of claim 1 maintained at a temperature from about 20° C. to about 90° C.;
applying a first pressure from about 276 kPa (40 psi) to about 1379 kPa (200 psi) for about 15 minutes to 300 minutes to form a low pH modified wood article penetrated to a first depth with the stable, low pH aqueous silicate suspension to form an impregnate to a first depth of impregnation from an outer surface of the wood article, wherein the impregnate is solid.
10 . The process of claim 9 further comprising draining the reactor and/or drying the modified wood article at a temperature from about 30° C. to about 90° C. to form a dried low pH modified wood article.
11 . The process of claim 9 further comprising draining the reactor followed by introducing a mild base to raise the pH of the impregnate to a pH between about 6.0 and about 8.0.
12 . The process of claim 9 further comprising a second feeding step to form a second impregnate, wherein the second impregnate is formed from a high pH metal silicate suspension comprising a metal silicate having a solution concentration of about 5 wt % to about 40 wt % and a modulus of from about 2 to about 4.
13 . The process of claim 12 , wherein the high pH metal silicate suspension has a pH of from about pH 10 to about pH 11.
14 . The process of claim 9 further comprising exposing the low pH modified wood article to a protic acid, a Lewis acid, a multivalent metal salt, solutions thereof, and/or combinations thereof, wherein exposing includes at least one of:
the protic acid or solution thereof, wherein the protic acid is selected from sulfuric acid, acetic acid, phosphoric acid, hydrochloric acid, and combinations thereof;
the Lewis acid or solution thereof, wherein the Lewis acid is selected from zinc chloride, magnesium sulfate, calcium chloride, and combinations thereof; and
the multivalent metal salt or solution thereof, wherein the multivalent metal salt is aluminum sulfate.