Method for producing poly(3-hydroxyalkanoate) foam particles and method for producing poly(3-hydroxyalkanoate) foam molded article
Poly(3-hydroxyalkanoate) foam particles are obtained by: introducing a blowing agent into an aqueous dispersion in a pressure-resistant vessel, the aqueous dispersion containing a crosslinking agent and resin particles containing a poly(3-hydroxyalkanoate); heating the contents of the pressure-resistant vessel to a given temperature in a range of 130 to 150° C.; holding the contents of the pressure-resistant vessel at the given temperature for 5 to 55 minutes; and opening one end of the pressure-resistant vessel to discharge the contents of the pressure-resistant vessel into a low-pressure atmosphere and foam the resin particles. The poly(3-hydroxyalkanoate) is a mixture containing a poly(3-hydroxyalkanoate) copolymer and a poly(3-hydroxybutyrate) homopolymer at a weight ratio of 99:1 to 80:20, and the crosslinking agent is an organic peroxide which is a percarbonate.
1 . A method for producing poly(3-hydroxyalkanoate) foam particles, the method comprising:
introducing a blowing agent into an aqueous dispersion in a pressure-resistant vessel, wherein the aqueous dispersion comprises a crosslinking agent and resin particles comprising a poly(3-hydroxyalkanoate);
heating a content of the pressure-resistant vessel after the introducing to a temperature of from 130 to 150° C. and holding the temperature for 5 to 55 minutes; and
opening one end of the pressure-resistant vessel to discharge the content of the pressure-resistant vessel into a low-pressure atmosphere and foaming the resin particles, wherein
the poly(3-hydroxyalkanoate) is a mixture containing a poly(3-hydroxyalkanoate) copolymer and a poly(3-hydroxybutyrate) homopolymer at a weight ratio of from 99:1 to 80:20, and
the crosslinking agent is a percarbonate.
2 . The method according to claim 1 , wherein the blowing agent is carbon dioxide.
3 . The method according to claim 1 , wherein
the poly(3-hydroxyalkanoate) copolymer is a copolymer of 3-hydroxybutyrate and a comonomer, and
a 3-hydroxybutyrate/comonomer ratio in the copolymer is from 99/1 to 89/11 mol %/mol %.
4 . The method according to claim 1 , wherein the percarbonate has a 1 minute half-life temperature of from 150 to 170° C. and is liquid at room temperature.
5 . The method according to claim 4 , wherein the percarbonate is a compound having one carbonate group.
6 . The method according to claim 1 , further comprising, after the foaming of the resin particles, impregnating resulting foam particles with an inorganic gas to increase a pressure inside the foam particles and subsequently heating the foam particles to expand the foam particles.
7 . A method for producing a poly(3-hydroxyalkanoate) foam molded article, the method comprising:
producing poly(3-hydroxyalkanoate) foam particles by the method according to claim 1 ; and
heating and molding the foam particles in a mold.
8 . The method according to claim 1 , wherein the weight ratio of the poly(3-hydroxyalkanoate) copolymer and the poly(3-hydroxybutyrate) homopolymer is from 98:2 to 84:16.
9 . The method according to claim 1 , wherein the weight ratio of the poly(3-hydroxyalkanoate) copolymer and the poly(3-hydroxybutyrate) homopolymer is from 97:3 to 88:12.
10 . The method according to claim 1 , wherein the aqueous dispersion comprises a dispersant and an amount of the dispersant is from 0.1 to 3.0 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
11 . The method according to claim 10 , wherein the dispersant is at least one selected from the group consisting of tricalcium phosphate, trimagnesium phosphate, basic magnesium carbonate, calcium carbonate, barium sulfate, kaolin, talc, clay, aluminum oxide, titanium oxide, and aluminum hydroxide.
12 . The method according to claim 1 , wherein the aqueous dispersion comprises a dispersion aid, wherein an amount of the dispersant aid is from 0.001 to 0.5 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
13 . The method according to claim 1 , wherein an amount of the crosslinking agent is from 1.2 to 5 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
14 . The method according to claim 1 , wherein an amount of the crosslinking agent is from 1.3 to 4 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
15 . The method according to claim 4 , wherein an amount of the crosslinking agent is from 1.2 to 5 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
16 . The method according to claim 4 , wherein an amount of the crosslinking agent is from 1.3 to 4 parts by weight per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).
17 . The method according to claim 1 , wherein the percarbonate is at least one selected from the group consisting of t-butylperoxy-2-ethylhexyl monocarbonate, t-butylperoxyisopropyl monocarbonate, t-amylperoxy-2-ethylhexyl monocarbonate, and t-amylperoxyisopropyl monocarbonate.
18 . The method according to claim 3 , wherein the 3-hydroxybutyrate/comonomer ratio in the copolymer is from 97/3 to 91/9 mol %/mol %.
19 . The method according to claim 1 , wherein the blowing agent is at least one selected from the group consisting of carbon dioxide, nitrogen, air, a saturated hydrocarbon having 3 to 5 carbon atoms, a dimethyl ether, diethyl ether, methyl ethyl ether, monochloromethane, dichloromethane, dichlorodifluoroethane, and water.
20 . The method according to claim 19 , wherein an amount of the blowing agent is from 2 to 10000 parts by weigh per 100 parts by weight of the resin particles comprising the poly(3-hydroxyalkanoate).