Macro-chip reinforced alloy
Described herein are methods of forming a neutron shielding material. Such material may comprise a powder blend comprising a first component comprising a blend of a first metal particle and a first ceramic particle; and a second component comprising a reinforcing chip, the reinforcing chip comprising a second ceramic particle dispersed within a chip metal matrix.
1 . A powder blend comprising:
a first component comprising a blend of a first metal particle and a first ceramic particle; and
a second component comprising a reinforcing chip, the reinforcing chip comprising a second ceramic particle dispersed within a chip metal matrix;
wherein the first ceramic particle and the first metal particle are present in a weight ratio ranging from about 1:15 to about 1:7.
2 . The powder blend according to claim 1 , wherein the first component and the second component are present in a weight ratio ranging from about 100:1 to about 2:1.
3 . The powder blend according to claim 1 , wherein the first ceramic particle and the second ceramic particle are formed from the same material.
4 . The powder blend according to claim 1 , wherein the first ceramic particle and the second ceramic particle are formed from different materials.
5 . The powder blend according to claim 1 , wherein the first ceramic particle and the second ceramic particle are each independently selected from the group consisting of alumina, titanium carbide, silicon carbide, tungsten carbide, boron carbide, and mixtures thereof.
6 . The powder blend according to claim 1 , wherein the first metal particle and the chip metal matrix are formed from the same material.
7 . The powder blend according to claim 1 , wherein the first metal particle and the chip metal matrix are formed from different materials.
8 . The powder blend according to claim 1 , wherein the first metal particle and the chip metal matrix are each independently selected from the group consisting of pure aluminum, an aluminum alloy, steel, a nickel alloy, a titanium alloy, and combinations thereof.
9 . The powder blend according to claim 1 , wherein the reinforcing chip has a height to width aspect ratio ranging from about 1:3 to about 1:1.25.
10 . The powder blend according to claim 1 , wherein the reinforcing chip has a height to thickness aspect ratio ranging from about 2:1 to about 10:1.
11 . The powder blend according to claim 1 , wherein the alloy chips have a width ranging from about 2.0 mm to about 10.0 mm.
12 . The powder blend according to claim 1 , wherein the alloy chips have a thickness ranging from about 0.1 mm to about 1.0 mm.
13 . The powder blend according to claim 1 , wherein the first ceramic particle and the second ceramic particle each have a particle distribution of 100% less than about 250 μm.
14 . The powder blend according to claim 1 , wherein the first metal particle has a d50 ranging from about 1 μm to about 20 μm.
15 . The powder blend according to claim 1 , wherein the first metal particle is an aluminum particle and has a natural oxide formation layer having a thickness ranging from about 3 nm to about 7 nm.
16 . A powder blend comprising:
a first component comprising a blend of a first metal particle and a first ceramic particle; and
a second component comprising a reinforcing chip, the reinforcing chip comprising a second ceramic particle dispersed within a chip metal matrix;
wherein the first metal particle is an aluminum particle and has a natural oxide formation layer having a thickness ranging from about 3 nm to about 7 nm.
17 . The powder blend according to claim 16 , wherein the chip metal matrix is selected from the group consisting of pure aluminum, an aluminum alloy, steel, a nickel alloy, a titanium alloy, and combinations thereof.
18 . The powder blend according to claim 16 , wherein the first component and the second component are present in a weight ratio ranging from about 100:1 to about 2:1.
19 . The powder blend according to claim 16 , wherein the first ceramic particle and the second ceramic particle are each independently selected from the group consisting of alumina, titanium carbide, silicon carbide, tungsten carbide, boron carbide, and mixtures thereof.
20 . The powder blend according to claim 16 , wherein the first metal particle has a d50 ranging from about 1 μm to about 20 μm.