Method for recovering active metal of lithium secondary battery
In a method for recovering an active metal of a lithium secondary battery, a preliminary cathode active material mixture is prepared from a cathode of a waste lithium secondary battery, the preliminary cathode active material mixture is fluidized through oxygen-containing gas within a fluidized bed reactor to form a cathode active material mixture, reductive gas is injected into the fluidized bed reactor to form a preliminary precursor mixture from the cathode active material mixture, and a lithium precursor is recovered from the preliminary precursor mixture.
1 . A method for recovering an active metal of a lithium secondary battery, the method comprising:
preparing a preliminary cathode active material mixture from a cathode of a waste lithium secondary battery;
fluidizing the preliminary cathode active material mixture by an oxygen-containing gas in a fluidized bed reactor to form a cathode active material mixture;
forming a preliminary precursor mixture from the cathode active material mixture by injecting a reductive gas into the fluidized bed reactor; and
recovering a lithium precursor from the preliminary precursor mixture.
2 . The method of claim 1 , wherein the cathode comprises a cathode current collector, and a cathode active material layer formed on the cathode current collector, and the cathode active material layer comprises a binder, a conductive material and a cathode active material,
wherein the preparing of the preliminary cathode active material mixture comprises removing the cathode current collector from the cathode; and
the preliminary cathode active material mixture comprises the binder, the conductive material and the cathode active material.
3 . The method of claim 2 , wherein the fluidizing of the preliminary cathode active material mixture by the oxygen-containing gas comprises decomposing and/or combusting the binder and the conductive material in the fluidized bed reactor.
4 . The method of claim 1 , wherein the oxygen-containing gas includes oxygen (O 2 ) and a non-reactive gas selected from the group consisting of helium (He), nitrogen (N 2 ), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe), and a combination thereof.
5 . The method of claim 4 , wherein a volume ratio of the oxygen is in a range from 10 to 30 vol %, and a volume ratio of the non-reactive gas is in a range from 70 to 90 vol % based on a total volume of the oxygen-containing gas.
6 . The method of claim 1 , wherein the fluidizing of the preliminary cathode active material mixture by the oxygen-containing gas is performed at a temperature from 100 to 600° C.
7 . The method of claim 6 , wherein the fluidizing of the preliminary cathode active material mixture by the oxygen-containing gas comprises heating an inside of the fluidized bed reactor from a temperature less than 50° C. for 1 to 2 hours so that a temperature of the inside of the fluidized bed reactor reaches a target temperature in a range from 400 to 600° C.
8 . The method of claim 7 , wherein the fluidizing of the preliminary cathode active material mixture by the oxygen-containing gas further comprises, subsequent to reaching the target temperature, performing a heat treatment at the target temperature for 2 to 5 hours.
9 . The method of claim 1 , wherein the reductive gas comprises hydrogen.
10 . The method of claim 9 , wherein the forming of the preliminary precursor mixture is performed at a temperature in a range from 400 to 500° C.
11 . The method of claim 9 , wherein the fluidizing of the preliminary cathode active material mixture by the oxygen-containing gas and the forming of the preliminary precursor mixture are continuously performed in-situ in the fluidized bed reactor.
12 . The method of claim 9 , wherein the preliminary precursor mixture includes preliminary lithium precursor particles and transition metal-containing particles including Ni, Co, NiO, CoO and MnO.
13 . The method of claim 12 , wherein the preliminary lithium precursor particles include at least one of lithium hydroxide, lithium oxide and lithium carbonate.
14 . The method of claim 13 , wherein the recovering of the lithium precursor comprises collecting the lithium hydroxide by washing the preliminary lithium precursor particles with water.
15 . The method of claim 1 , wherein the fluidizing of the preliminary cathode active material mixture and the forming of the preliminary precursor mixture are performed in different fluidized bed reactors.
16 . The method of claim 1 , further comprising, after forming of the preliminary precursor mixture:
forming the preliminary precursor mixture in a slurry state by injecting water and a non-reactive gas.
17 . The method of claim 1 , wherein the recovering of the lithium precursor from the preliminary precursor mixture comprises reacting the preliminary precursor mixture with a leaching solution comprising water.
18 . The method of claim 17 , wherein the leaching solution further comprises at least one of dimethyl carbonate and diethyl carbonate.